Fabrication of excellent mechanical properties AZ31 magnesium alloy sheets by conventional rolling and subsequent annealing

Materials Science and Engineering: A

Volumn 528, Issue 22-23, 2011, Pages 6694-6701

  Miao, Qing ^a   Hu, Lianxi ^a   Wang, Guojun ^b   Wang, Erde ^a  

^a HARBIN INSTITUTE OF TECHNOLOGY   (China)

^b Northeast Light Alloy Co Ltd   (China)

Author keywords

Magnesium alloy sheets; Mechanical properties; Microstructure; Rolling and annealing

Indexed keywords

COST EFFECTIVENESS; CRYSTAL MICROSTRUCTURE; DYNAMIC RECRYSTALLIZATION; MAGNESIUM ALLOYS; MAGNESIUM PRINTING PLATES; ROLLING;

AVERAGE SIZE; AZ31 MAGNESIUM ALLOY SHEET; CONVENTIONAL ROLLING; DYNAMIC RECRYSTALLISATION; MAGNESIUM ALLOY SHEETS; PROCESSING ROUTE; RECRYSTALLIZED MICROSTRUCTURES; ROLLING AND ANNEALING; TEMPERATURE RANGE; TENSILE ELONGATION;

ANNEALING;

EID: 79960083012     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2011.05.023     Document Type: Article

References (27)

1. Brown R.E. Proceedings of 59th Annual World Magnesium Conference 2002, 25.
2. Kitazono K., Sato E., Kuribayashi K. Scripta Mater. 2001, 44:2695-2702.
3. Püschl W. Prog. Mater. Sci. 2002, 47:415-461.
4. Perez-Prado M.T., del Valle J.A., Ruano O.A. Scripta Mater. 2004, 51:1093-1097.
5. Armstrong R.W., Codd I., Douthwaite R.M., Petch N.J. Philos. Mag. 1962, 7:45-58.
6. Mabuchi M., Higashi K. Acta Mater. 1996, 44:4611-4618.
7. Chang T., Wang J.Y., Chia-Ming O., Lee S. J. Mater. Process. Technol. 2003, 140:588-591.
8. Mabuchi M., Asahina T., Iwasaki H., Higashi K. Mater. Sci. Technol. 1997, 13:825-831.
9. Valiev R.Z., Islamgaliev R.K., Alexandrov I.V. Prog. Mater. Sci. 2000, 45:103-189.
10. Jin L., Lin D., Mao D., Zeng X., Ding W. Mater. Lett. 2005, 59:2267-2270.
11. Chino Y., Mabuchi M. Adv. Eng. Mater. 2001, 3:981-983.
12. Mukai T., Yamanoi M., Watanabe H., Higashi K. Scripta Mater. 2001, 45:89-94.
13. Kim W.J., Lee J.B., Kim W.Y., Jeong H.T., Jeong H.G. Scripta Mater. 2007, 56:309-312.
14. Kim S.H., You B.S., Yim C.D., Seo Y.M. Mater. Lett. 2005, 59:3876-3880.
15. Kim W.J., Park J.D., Kim W.Y. J. Alloys Compd. 2008, 460:289-293.
16. Pérez-Prado M.T., del Valle J.A., Ruano O.A. Mater. Lett. 2005, 59:3299-3303.
17. Annual Book of ASTM Standards 1998, ASTM, Philadelphia, PA, p. 229.
18. Miao Q., Hu L.X., Wang E., Liang S.J., Chao H.Y. Int. J. Mod. Phys. B 2009, 23(6-7):984-989.
19. Yin D.L., Zhang K.F., Wang G.F., Han W.B. Mater. Sci. Eng. A 2005, 392:320-325.
20. Bohlen J., Chmelík F., Dobroň P., Kaiser F., Letzig D., Lukáč P., Kainer K.U. J. Alloys Compd. 2004, 378:207-213.
21. Wang Q.J., Zhang Y.B., Sun Y.F. Mater. Sci. Forum 2009, 610-613:742-745.
22. Iwanaga K., Tashiro H., Okamoto H., Shimizu K. J. Mater. Process. Technol. 2004, 155-156:1313-1316.
23. Koike J., Kobayashi T., Mukai T., Watanabe H., Suzuki M., Maruyama K., Higashi K. Acta Mater. 2003, 51:2055-2065.
24. Stanford N., Barnett M.R. J. Alloys Compd. 2008, 466:182-188.
25. Kim W.J., Hong S.I., Kim Y.S., Min S.H., Jeong H.T., Lee J.D. Acta Mater. 2003, 51:3293-3307.
26. Kim W.J., Jeong H.T. Mater. Trans. 2005, 46:251-258.
27. Chao H.Y., Yang Y., Wang X., Wang E.D. Mater. Sci. Eng. A 2011, 528:3428-3434.