Lifetime assessment for thermal barrier coatings: Tests for measuring mixed mode delamination toughness

Journal of the American Ceramic Society

Volumn 94, Issue SUPPL. 1, 2011, Pages s85-s95

  Hutchinson, Robert G ^a   Hutchinson, John W ^b  

^a PRATT AND WHITNEY   (United States)

^b HARVARD UNIVERSITY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CERAMIC MATERIALS; MATERIALS SCIENCE;

CRACKING CONDITION; DEGRADATION PROCESS; DELAMINATION TOUGHNESS; DIRECT MEASUREMENT; LIFETIME ASSESSMENT; MIXED MODE DELAMINATION; PREDICTIVE MODELS; THERMAL BARRIER COATING (TBC);

THERMAL BARRIER COATINGS;

EID: 79959928939     PISSN: 00027820     EISSN: 15512916     Source Type: Journal    
DOI: 10.1111/j.1551-2916.2011.04499.x     Document Type: Article

References (24)

1. N. P. Padture, M. Gell, and, E. H. Jordan, " Thermal-Barrier Coatings for Gas-Turbine Engine Applications," Science, 296, 280-4 (2002). (Pubitemid 34308457)
2. D. R. Clarke, and, C. G. Levi, " Materials Design for the Next Generation Thermal-Barrier Coatings," Annu. Rev. Mater. Res., 33, 383 -417 (2003).
3. A. G. Evans, D. R. Mumm, J. W. Hutchinson, G. H. Meier, and, F. S. Pettit, " Mechanisms Controlling the Durability of Thermal-Barrier Coatings," Prog. Mater. Sci., 46, 505 -53 (2001).
4. S. Kraemer, S. Faulhaber, M. Chambers, D. R. Clarke, C. G. Levi, J. W. Hutchinson, and, A. G. Evans, " Mechanisms of Cracking and Delaminations within Thick Thermal Barrier Systems in Aero-Engines Subject to Calcium-Magnesium-Alumino-Silicate (CMAS) Penetration," Mater. Sci. Eng. A, 490, 26-35 (2008).
5. I. Hofinger, M. Oechsner, H.-A. Bahr, and, M. V. Swain, " Modified Four-Point Bend Specimen for Determining the Interface Fracture Energy for Thin, Brittle Layers," Int. J. Fracture, 92, 213-20 (1998).
6. P.-Y. Thery, M. Poulain, M. Dupeux, and, M. Braccini, " Spallation of Two Thermal Barrier Coating Systems: Experimental Study of Adhesion and Energetic Approach to Lifetime During Cyclic Oxidation," J. Mater. Sci., 44, 1726-33 (2009).
7. H. H. Yu, M. Y. He, and, J. W. Hutchinson, " Edge Effects in Thin Film Delamination," Acta Mater., 49, 93-107 (2001). (Pubitemid 32093210)
8. D. Balint, and, J. W. Hutchinson, " Mode II Edge Delamination of Compressed Thin Films," J. Appl. Mech., 68, 725-30 (2001). (Pubitemid 33770336)
9. J. W. Hutchinson, and, Z. Suo, " Mixed Mode Cracking in Layered Materials," Adv. Appl. Mech., 29, 63-191 (1992).
10. A. Vastinonta, and, J. L. Beuth, " Measurement of Interfacial Toughness in Thermal Barrier Coating Systems by Indentation," Eng. Fract. Mech., 68, 843-60 (2001). (Pubitemid 32406549)
11. C. Eberl, D. S. Gianola, Xi Wang, M. Y. He, A. G. Evans, and, K. J. Hemker, "In Situ Measurement of the Toughness of the Interface Between a Thermal Barrier Coating and a Ni Alloy," J. Am. Ceram. Soc. (this issue).
12. S. Q. Guo, D. R. Mumm, A. M. Karlsson, and, Y. Kagawa, " Measurement of Interfacial Shear Mechanical Properties in Thermal Barrier Coating Systems by a Barb Pullout Method," Scr. Mater., 53, 1043-8 (2005). (Pubitemid 41162525)
13. M. Tanaka, Y. F. Liu, S. S. Kim, and, Y. Kagawa, " Delamination Toughness of Electron Beam Physical Vapor Deposition (EB-PVD) Y2O3-ZrO2 Thermal Barrier Coatings by the Pushout Method: Effect of Thermal Cycling Temperature," J. Mater. Res., 23, 2382-92 (2008).
14. Y. F. Liu, Y. Kagawa, and, A. G. Evans, " Analysis of a "Barb Test" for Measuring the Mixed-Mode Delamination Toughness of Coatings," Acta Mater., 56, 43-9 (2008). (Pubitemid 350123099)
15. P. G. Charalambides, J. Lund, A. G. Evans, and, R. M. McMeeking, " A Test Specimen for Determining the Fracture Resistance of Bimaterial Interfaces," J. Appl. Mech., 56, 77-82 (1989).
16. G. Bao, S. Ho, B. Fan, and, Z. Suo, " The Role of Material Orthotropy in Fracture Specimens for Composites," Int. J. Solids Struct., 29, 1105-16 (1992).
17. B. F. Sorensen, K. Jorgensen, T. Jacobsen, and, R. C. Ostergaard, " DCB-Specimen with Uneven Bending Moments," Int. J. Fracture, 141, 163-76 (2006).
18. J. S. Wang, and, Z. Suo, " Experimental Determination of Interfacial Toughness Curves Using Brazil-Nut-Sandwiches," Acta Metall., 38, 1279-90 (1990).
19. L. Bank-Sills, V. Boniface, and, R. Eliasi, " Development of a Methodology for Determination of Interface Fracture Toughness of Laminate Composites-the 0°/90° Pair," Int. J. Solids Struct., 42, 663-89 (2005).
20. A. Dorogoy, and, L. Banks-Sills, " Effective of Crack Face Contact and Friction on Brazilian Disk Specimens-A Finite Difference Solution," Eng. Fract. Mech., 72, 2758-73 (2005). (Pubitemid 41372545)
21. Z. Suo, and, J. W. Hutchinson, " Sandwich Test Specimens for Measuring Interface Crack Toughness," Mater. Sci. Eng., A107, 135-43 (1989).
22. K. M. Liechti, and, Y.-S. Chai, " Asymmetric Shielding in Interfacial Fracture Under Inplane Shear," J. Appl. Mech., 59, 295-304 (1992).
23. M. Y. He, A. Bartlett, A. G. Evans, and, J. W. Hutchinson, " Kinking of a Crack Out of an Interface: Role of In-Plane Stress," J. Am. Ceram. Soc., 74, 767-71 (1991).
24. J. R. Rice, " Elastic Fracture Concepts for Interfacial Cracks," J. Appl. Mech., 55, 98-103 (1988). (Pubitemid 18590050)