Facile synthesis of 3D flowerlike CeO2 microspheres under mild condition with high catalytic performance for CO oxidation

Journal of Colloid and Interface Science

Volumn 360, Issue 1, 2011, Pages 93-99

  Li, Junfeng ^a   Lu, Guanzhong ^a   Li, Hongfeng ^a   Wang, Yanqin ^a   Guo, Yun ^a   Guo, Yanglong ^a  

^a RESEARCH INSTITUTE OF INDUSTRIAL CATALYSIS   (China)

Author keywords

Catalytic CO oxidation; Co surfactant technology; Facile synthesis; Flowerlike CeO2 microspheres; Mild condition

Indexed keywords

CO OXIDATION; CO-SURFACTANTS; FACILE SYNTHESIS; FLOWERLIKE CEO2 MICROSPHERES; MILD CONDITION;

ADSORPTION; CATALYST ACTIVITY; CERIUM COMPOUNDS; MICROSPHERES; NANOWIRES; OXIDATION; SODIUM; SURFACE ACTIVE AGENTS; THREE DIMENSIONAL;

CATALYTIC OXIDATION;

CARBON MONOXIDE; CERIUM OXIDE; COSURFACTANT; DODECYL SULFATE SODIUM; MACROGOL; MICROSPHERE; NITROGEN; SURFACTANT;

ADSORPTION; ARTICLE; CATALYSIS; INFRARED SPECTROSCOPY; MORPHOLOGY; OXIDATION; PHOTOLUMINESCENCE; PRIORITY JOURNAL; QUANTUM MECHANICS; SCANNING ELECTRON MICROSCOPY; TEMPERATURE; ULTRAVIOLET SPECTROSCOPY;

EID: 79957833445     PISSN: 00219797     EISSN: 10957103     Source Type: Journal    
DOI: 10.1016/j.jcis.2011.04.052     Document Type: Article

References (51)

1. Shi R.J., Wang F., Tana T., Li Y., Huang X.M., Shen W.J. Green Chem. 2010, 12:108.
2. Yu M., Lin J., Wang Z., Fu J., Wang S., Zhang H.J., Han Y.C. Chem. Mater. 2002, 14:2224.
3. Tomota M., Murakami M. Nature 2003, 421:517.
4. Cavani F., Trifiro F. Catal. Today 1999, 51:561.
5. Zhang T.S., Ma J., Kong L.B., Chan S.H., Kilner J.A. Solid State Ionics 2004, 170:209.
6. Trovarelli A. Catal. Rev. Sci. Eng. 1996, 38:439.
7. Yabe S., Sato T.J. Solid State Chem 2003, 171:7.
8. Park S.D., Vohs J.M., Gorte R.J. Nature 2000, 404:265.
9. Weber W.H., Hass K.C., McBride J.R. Phys. Rev. B. 1993, 50:13297.
10. Tsunekawa S., Fukuda T., Kasuya A. J. Appl. Phys. 2000, 87:1318.
11. Srivastava R. J. Colloid Interface Sci. 2010, 348:600.
12. Corma A., Atienzar P., Garcia H., Chane-Ching J.Y. Nat. Mater. 2004, 3:394.
13. Lyons D.M., Ryan K.M., Morris M.A. J. Mater. Chem. 2002, 12:1207.
14. Tang C.C., Bando Y., Liu B.D., Golberg D. Adv. Mater. 2005, 17:3005.
15. Wu X.S., Kawi S. Cryst. Growth Des. 2010, 10:1833.
16. Zhang D.S., Fu H.X., Shi L.Y., Pan C.S., Li Q., Chu Y.L., Yu W.J. Inorg. Chem. 2007, 46:2446.
17. Zhou K.B., Wang X., Sun X.M., Peng Q., Li Y.D. J. Catal. 2005, 229:206.
18. Lin H.L., Wu C.Y., Chiang R.K. J. Colloid Interface Sci. 2010, 341:12.
19. Tang B., Zhuo L.H., Ge J.C., Wang G.L., Shi Z.Q., Niu J.Y. Chem. Commun. 2005, 28:3565.
20. Liao L., Mai H.X., Yuan Q., Lu H.B., Li J.C., Liu C., Yan C.H., Shen Z.X., Yu T. J. Phy. Chem. C 2008, 112:9061.
21. Wang X., Li Y.D. Chem. Eur. J. 2003, 9:5627.
22. Lu X.H., Zheng D.Z., Gan J.Y., Liu Z.Q., Liang C.L., Liu P. J. Mater. Chem. 2010, 20:7118.
23. Li G.R., Qu D.L., Tong Y.X. Electrochem. Commun. 2008, 10:80.
24. Yang S.W., Gao L. J. Am. Chem. Soc. 2006, 128:9330.
25. Qian L.W., Zhu J., Du W.M., Qian X.F. Mater. Chem. Phys. 2009, 2-3:835.
26. Si R., Zhang Y.W., You L.P., Yan C.H. Angew. Chem. Int. Ed. 2005, 44:3256.
27. Mai H.X., Sun L.D., Zhang Y.W., Si R., Feng W., Zhang H.P., Liu H.C., Yan C.H. J. Phy. Chem. B 2005, 109:24380.
28. Zhong L.S., Hu J.S., Cao A.M., Liu Q., Song W.G., Wan L. J. Chem. Mater. 2007, 19:1648.
29. Li Z.X., Li L.L., Yuan Q., Feng W., Xu J., Sun L.D., Song W.G., Yan C.H. J. Phys. Chem. C 2008, 112:18405.
30. Zhou F., Ni X.M., Zhang Y.F., Zheng H.G. J. Colloid Interface Sci. 2007, 307:135.
31. Cui R.R., Lu W.C., Zhang L.M., Yue B.H., Shen S.S. J. Phys. Chem. C 2009, 113:21520.
32. Laberty-Robert C., Long J.W., Lucas E.M., Pettigrew K.A., Stroud R.M., Doescher M.S., Rolison D.R. Chem. Mater. 2006, 18:50.
33. Pan C.S., Zhang D.S., Shi L.Y. J. Solid State Chem. 2008, 181:1298.
34. Wu N.C., Shi E.W., Zheng Y.Q., Li W.J. J. Am. Ceram. Chem. 2002, 85:2462.
35. Wang D.S., Xie T., Peng Q., Zhang S.Y., Chen J., Li Y.D. Chem. Eur. J. 2008, 14:2507.
36. Xia B., Lenggoro I.W., Okuyama K. J. Mater. Chem. 2001, 11:2925.
37. Yan L., Yu R.B., Chen J., Xing X.R. Cryst. Growth Des. 2008, 8:1474.
38. Liu B., Zeng H.C. J. Am. Chem. Soc. 2004, 126:16744.
39. Zhu H., Wang X.L., Wang Z.J., Yang C., Yang F., Yang X.R. J. Phys. Chem. C 2008, 112:15285.
40. Zhang L.S., Wang W.Z., Chen Z.G., Zhou L., Xua H.L., Zhu W. J. Mater. Chem. 2007, 17:2526.
41. Yan C.L., Xue D.F. J. Phys. Chem. B 2005, 109:12358.
42. Li H.F., Lu G.Z., Dai Q.G., Wang Y.Q., Guo Y., Guo Y.L. ACS Appl. Mater. Int. 2010, 2:838.
43. Wang G.F., Mu Q.Y., Chen T., Wang Y.D. J. Alloys Compd. 2010, 493:202.
44. Suzuki T., Kosacki I., Petrovsky V., Anderson H.U. J. Appl. Phys. 2002, 91:2308.
45. Yada M., Kitamura H., Machida M., Kijima T. Inorg. Chem. 1998, 37:6470.
46. Guo W., Sun Y.W., Luo G.S., Wang Y. Colloids Surf., A: Physicochem. Eng. Aspects 2005, 252:71.
47. Sayle D.C., Maicaneanu S.A., Watson G.W. J. Am. Chem. Soc. 2002, 124:11429.
48. Lundberg M., Skårman B., Wallenberg L.R. Microporous Mesoporous Mater. 2004, 69:187.
49. Liu X.H., Chen S.J., Wang X.D. J. Lumin. 2007, 127:650.
50. Li G.C., Chao K., Peng H.R., Chen K.Z., Zhang Z.K. J. Phys. Chem. C 2008, 112:16452.
51. Mochizuki S., Fujishiro F. Phys. Status Solidi B 2009, 246:2320.