Application of the indentation method for cracking resistance evaluation of hard coatings on tool steels;Tööriistateraste õhukeste kõvapinnete vastupanu hindamine pragunemisele indenteerimismeetodi abil

Estonian Journal of Engineering

Volumn 15, Issue 4, 2009, Pages 309-317

  Sivitski, Alina ^a   Gregor, Andre ^a   Saarna, Mart ^a   Kulu, Priit ^a   Sergejev, Fjodor ^a  

^a TALLINN UNIVERSITY OF TECHNOLOGY   (Estonia)

Author keywords

Cracking; Delamination; Hard coating; Indentation method; Multilayers; PVD

Indexed keywords

ADHESION TESTING; COATED SYSTEMS; CRACKING; CRACKING RESISTANCE; CYCLIC LOADINGS; DAMAGE EVOLUTION; FATIGUE PROPERTIES; FATIGUE RESISTANCE; INDENTATION METHOD; NUMBER OF CYCLES; ROCKWELL; VICKERS INDENTATION METHOD;

CRACKING (CHEMICAL); METAL FORMING; MULTILAYERS; STEEL SHEET; TITANIUM NITRIDE;

HARD COATINGS;

EID: 79955141258     PISSN: 17366038     EISSN: 17367522     Source Type: Journal    
DOI: 10.3176/eng.2009.4.08     Document Type: Article

References (11)

1. Richter, J. Application of Vickers indentation for assessment of PVD TiN coated new nonledeburitic high-speed steels. Surf. Coat. Tech., 2003, 162, 119-130.
2. Zoestbergen, E. and DeHosson, J. Th. M. Crack resistance of PVD coatings: Influence of surface treatment prior to deposition. Surf. Eng., 2002, 18, 283-288.
3. Tarrés, E., Ramirez, G., Gaillard, Y., Jiménez-Piqué, E. and Llanes, L. Contact fatigue behavior of PVD-coated hardmetals. Int. J. Refract. Met. Hard Mater., 2009, 27, 323-331.
4. Cook, R. F. and Pharr, G. M. Direct observation and analysis of indentation cracking in glasses and ceramics. J. Am. Ceram. Soc., 1990, 73, 787-817.
5. Kim, D. K., Jung, Y.-G., Peterson, I. M. and Lawn, B. R. Cyclic contact fatigue of intrinsically brittle ceramics in contact with spheres. Acta Mater., 1999, 47, 4711-4725.
6. Chiang, S. S., Marshall, D. B. and Evans, A. G. The response of solids to elastic/plastic indentation. II. Fracture initiation. J. Appl. Phys., 1982, 53, 312-317.
7. Holmberg, K., Ronkainen, H., Laukkanen, A., Wallin, K., Hogmark, S., Jacobson, S., Wiklund, U., Souza, R. M. and Ståhle, P. Residual stresses in TiN, DLC and MoS2 coated surfaces with regard to their tribological fracture behaviour. In Proc. 13th Nordic Symposium on Tribology NORDTRIB 2008. Tampere, Finland, 2008, 37 p.
8. Fouvry, S., Liskiewicz, T. and Paulin, C. A global-local wear approach to quantify the contact endurance under reciprocating-fretting sliding conditions. Wear, 2007, 263, 518-531.
9. Palmqvist, S. The work for the formation of a crack during Vickers indentation as a measure of the toughness of hard metals. Arch. Eisenhüttenwes., 1962, 33, 629-634.
10. VDI 3198:1992-08, Coating (CVD, PVD) of Cold Forging Tools. VDI-Verlag, Düsseldorf, 1991.
11. Bouzakis, K.-D., Siganos, A., Leyendecker, T. and Erkens, G. Thin hard coatings fracture propagation during the impact test. Thin Solid Films, 2004, 460, 181-189.