Preparation of pseudoboehmite with a large pore volume and a large pore size by using a membrane-dispersion microstructured reactor through the reaction of CO2 and a NaAlO2 solution

Industrial and Engineering Chemistry Research

Volumn 50, Issue 7, 2011, Pages 3889-3894

  Wang, Yujun ^a   Xu, Dengqing ^b   Sun, Haitao ^b   Luo, Guangsheng ^a  

^a TSINGHUA UNIVERSITY   (China)

^b QUFU NORMAL UNIVERSITY   (China)

Author keywords

[No Author keywords available]

Indexed keywords

ALUMINA; ALUMINUM OXIDE; CARBON DIOXIDE; DISPERSIONS; GASES; MASS TRANSFER; MICROSTRUCTURE; PORE SIZE; SODIUM ALUMINATE; SOLUTIONS;

LARGE PORE SIZE; LARGE PORE VOLUME; MASS TRANSFER RATE; MEMBRANE DISPERSION; MICROSTRUCTURED REACTORS; OPTIMAL CONDITIONS; PORE DIAMETERS; PSEUDO-BOEHMITE;

SODIUM COMPOUNDS;

EID: 79953317247     PISSN: 08885885     EISSN: 15205045     Source Type: Journal    
DOI: 10.1021/ie101629g     Document Type: Article

References (20)

1. Liu, Q.; Wang, A.; Wang, X.; Gao, P.; Wang, X.; Zhang, T. Synthesis, characterization and catalytic applications of mesoporous Î-alumina from boehmite sol Microporous Mesoporous Mater. 2008, 111, 323
2. Kim, P.; Kim, Y.; Kim, H.; Song, I. K.; Yi, J. Synthesis and characterization of mesoporous alumina for use as a catalyst support in the hydrodechlorination of 1,2-dichloropropane: Effect of preparation condition of mesoporous alumina J. Mol. Catal. A: Chem. 2004, 219, 87
3. 3 with a lathlike framework morphology J. Am. Chem. Soc. 2002, 124, 12294
4. 3 catalyst for deep hydrodesulfurization via the hydrogenation reaction pathway J. Catal. 2010, 272, 28
5. 3-supported NiMo catalysts Catal. Today 2010, 149, 62
6. Kresge, C. T.; Leonowicz, M. E.; Roth, W. J.; Vartuli, J. C.; Beck, J. S. Ordered mesoporous molecular sieves synthesized by a liquid-crystal template mechanism Nature 1992, 359, 710
7. Ma, M. G.; Zhu, Y. J.; Xu, Z. L. A new route to synthesis of Î-alumina nanorods Mater. Lett. 2007, 61, 1812
8. Wang, S. Y.; Li, X. A.; Wang, S. F.; Li, Y.; Zhai, Y. C. Synthesis of Î3-alumina via precipitation in ethanol Mater. Lett. 2008, 62, 3552
9. Gan, Z. H.; Ning, G. L.; Lin, Y.; Cong, Y. Morphological control of mesoporous alumina nanostructures via template-free solvent thermal synthesis Mater. Lett. 2007, 61, 3758
10. Yamauchi, N. One-step synthesis of hierarchical porous Î3-alumina J. Sol-Gel Sci. Technol. 2010, 53, 428
11. 2 China Petroleum Process. Petrochem. Technol. 2003, 1, 47
12. Armbrust, B. F.; Carithers, V. G.; Hrishikesan, K. G.; Drown, H. L. Alumina hydrate and its method of preparation. US Patent USP3 268 295, 1966.
13. Du, J. W.; Liu, J.; Meng, W.; Gong, H.; Liang, Z. Y. A method to prepare pseudoboehmite. China Patent CN186152A. 200510068393.0, 2005.
14. Zeng, S. Q.; Yang, Q. H.; Liu, B.; Hu, D. W.; Nie, H.; Li, D. D. A Pseudo-boehmite and its preparation method. China Patent CN 1000999328A. 200610000703.X, 2006.
15. Wang, K.; Wang, Y. J.; Chen, G. G.; Luo, G. S.; Wang, J. D. Enhancement of mixing and mass transfer performance with a microstructure minireactor for controllable preparation of CaCO3 nanoparticles Ind. Eng. Chem. Res. 2007, 46, 6092
16. Chen, G. G.; Luo, G. S.; Xu, J. H.; Wang, J. D. Membrane dispersion precipitation method to prepare nanoparticles Powder Technol. 2004, 139, 180
17. Li, S. W.; Xu, J. H.; Luo, G. S. Control of crystal morphology through supersaturation ratio and mixing conditions J. Cryst. Growth 2007, 304, 219
18. 2 Chin. J. Catal. 1997, 18 (6) 478
19. Okada, K.; Nagashima, T.; Kameshima, Y.; Yasumori, A.; Tsukada, T. Relationship between formation conditions, properties, and crystallite size of boehmite J. Colloid Interface Sci. 2002, 253, 308
20. 2 China Petroleum Process. Petrochem. 1999, 30 (4) 59