Delamination effect on bending behaviour in carbon-epoxy composites

Strain

Volumn 47, Issue 2, 2011, Pages 203-208

  Amaro, A M ^a   Reis, P N B ^b   De Moura, M F S F ^c  

^a UNIVERSITY OF COIMBRA   (Portugal)

^b UNIVERSITY OF BEIRA INTERIOR   (Portugal)

^c UNIVERSITY OF PORTO   (Portugal)

Author keywords

bending behaviour; composites; damage; interface elements; polymer matrix

Indexed keywords

ABAQUS SOFTWARE; BENDING BEHAVIOUR; CARBON FIBRES; CARBON-EPOXY COMPOSITE; COMPOSITES; DAMAGE; DELAMINATION PROPAGATION; EXPERIMENTAL TEST; INTERFACE ELEMENTS; LAMINATE THICKNESS; MAXIMUM LOAD; MIXED-MODE DAMAGE MODEL; NUMERICAL MODELS; NUMERICAL SIMULATION; NUMERICAL STUDIES; SOLID ELEMENTS; STRESS PROFILE; THREE POINT BENDING;

ABAQUS; BENDING TESTS; CARBON FIBERS; LAMINATES; POLYMER MATRIX COMPOSITES; STEEL SHEET;

DELAMINATION;

EID: 79952584848     PISSN: 00392103     EISSN: 14751305     Source Type: Journal    
DOI: 10.1111/j.1475-1305.2008.00520.x     Document Type: Article

References (18)

1. de Moura, M. F. S. F., and, Marques, A. T., (2002) Prediction of low velocity impact damage in carbon-epoxy laminates. Compos. Part A-Appl. S. 33, 361-368. (Pubitemid 34069945)
2. Collombet, F., Bonini, J., and, Lataillade, J. L., (1996) A three-dimensional modelling of low velocity impact damage in composite laminates. Int. J. Numer. Methods Eng. 39, 1491-1516. (Pubitemid 126648125)
3. Richardson, W. O. W., and, Wisheart, M. J., (1996) Review of low velocity impact properties of composite materials. Compos. Part A-Appl. S. 27, 1123-1131.
4. Cantwell, W. J., Curtis, P. T., and, Morton, J., (1984) Impact and subsequent fatigue damage growth in carbon-fibre laminates. Int. J. Fatigue 6, 113-118. (Pubitemid 14544404)
5. Soutis, C., and, Curtis, P. T., (1996) Prediction of the post-impact compressive strength of CFRP laminated composites. Compos. Sci. Technol. 56, 677-684. (Pubitemid 126376630)
6. Jeon, B. S., Lee, J. J., Kim, J. K., and, Huh, J. S., (1999) Low velocity impact and delamination buckling behaviour of composite laminates with embedded optical fibers. Smart Mater. Struct. 8, 41-48.
7. Adams, R. D., and, Cawley, P. D., (1998) A review of defects types and non-destructive testing techniques for composites and bonded joints. NDT&E Int. 21, 208-222.
8. Capriotti, R., Dati, E., Silvestri, P., and, Trivisonno, G., (2000) NDT Techniques for the Evaluation of Impact Damage on Aeronautical Structures. Proc. of 15th World conf. on Non-destr. Test. October 15-21, Rome, Italy.
9. Zheng, S., and, Sun, C., (1998) Delamination interaction in laminated structures. Eng. Fract. Mech. 59, 225-240. (Pubitemid 128647741)
10. de Moura, M. F. S. F., and, Gonçalves, J. P. M., (2004) Modelling the interaction between matrix cracking and delamination in carbon-epoxy laminates under low velocity impact. Compos. Sci. Technol. 64, 1021-1027.
11. American Society for Testing and Materials. (1983) Standard guide for testing inplane shear properties of composites laminates. Annual Book of ASTM Standards D, 4255-4283.
12. American Society for Testing and Materials (1999) Standard test method for apparent interlaminar shear strength of parallel fiber composites by short-beam method. Annual Book of ASTM Standards D, 2344-2376.
13. American Society for Testing and Materials (1999) Standard test method for tensile properties of fiber-resin composites. Annual Book of ASTM Standards D, 3039-3076.
14. Lammerant, L., and, Verpoest, I., (1996) Modelling the interaction between matrix cracks and delamination during impact of composite plates. Compos. Sci. Technol. 56, 1171-1178.
15. Brewer, J. C., and, Lagace, P. A., (1988) Quadratic stress criterion for initiation of delamination. J. Compos. Mater. 22, 1141-1153.
16. de Moura, M. F. S. F., Pereira, A. B., and, de Morais, A. B., (2004) Influence of intralaminar cracking on the apparent interlaminar mode I fracture toughness of cross-ply laminates. Fatigue Fract. Eng. M. 27, 759-766.
17. de Moura, M. F. S. F., Silva, M. A. L., de Morais, A. B., and, Morais, J. J. L., (2006) Equivalent crack based mode II fracture characterization of wood. Eng. Fract. Mech. 73, 978-993. (Pubitemid 43240106)
18. Reis, P. N. B., Ferreira, J. A. M., Antunes, F. V., and, Costa, J. D. M., (2007) Flexural behaviour of hybrid laminated composites. Compos. Part A-Appl. Sci. Manuf. 38, 1612-1620. (Pubitemid 46561390)