Acoustic Emission based on sentry function to monitor the initiation of delamination in composite materials

Materials and Design

Volumn 32, Issue 5, 2011, Pages 3059-3065

  Bakhtiary Davijani, A A ^a   Hajikhani, M ^a   Ahmadi, M ^a  

^a AMIRKABIR UNIVERSITY OF TECHNOLOGY   (Iran)

Author keywords

[No Author keywords available]

Indexed keywords

APPROPRIATE TECHNIQUES; GLASS/EPOXY; IN-SITU MONITORING; INITIATION AND PROPAGATION; MICRO-EVENTS; SCANNING ELECTRON MICROSCOPES;

ACOUSTIC EMISSIONS; COMPOSITE MATERIALS; CRACK INITIATION; CRACKS; DELAMINATION; FAILURE ANALYSIS; NUMERICAL METHODS; SCANNING ELECTRON MICROSCOPY; STEEL SHEET; STRESS CORROSION CRACKING;

BEHAVIORAL RESEARCH;

EID: 79952185424     PISSN: 02641275     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.matdes.2011.01.010     Document Type: Article

References (39)

1. Loutas T.H., Kostopulos V., Ramirez-Jimenez C., Pharaoh M. Damage evolution in center-holed glass/polyester composites under quasi-static loading using time/frequency analysis of acoustic emission monitored waveforms. Compos Sci Technol 2006, 66:1366-1375.
2. Bourchak M., Farrow I.R., Bond I.P., Rowland C.W., Menan F. Acoustic emission energy as a fatigue damage parameter for CFRP composites. Int J Fatigue 2007, 29:458-470.
3. de Oliveira R., Marques A.T. Health monitoring of FRP using acoustic emission and artificial neural networks. Comput Struct 2008, 86:367-373.
4. Eitzen D.G., Wadley H.N.G. Acoustic emission: establishing the fundamentals. J Res Natl Bur Stand 1984, 89:75-100.
5. Ndiaye I, Maslouhi A, Denault J. Characterization of interfacial properties of composite materials by acoustic emission. Polym Compos 2000;21(4).
6. Philippidis T.P., Assimakopoulou T.T. Using acoustic emission to assess shear strength degradation in FRP composites due to constant and variable amplitude fatigue loading. Compos Sci Technol 2008, 68:840-847.
7. Oskouei A.R., Ahmadi M., Hajikhani M. Wavelet-based acoustic emission characterization of damage mechanism in composite materials under mode I delamination at different interfaces. Express Polym Lett 2009, 3(12):804-813.
8. Marec A., Thomas J.H., El Guerjoumaa R. Damage characterization of polymer-based composite materials: multivariable analysis and wavelet transform for clustering acoustic emission data. Mech Syst Signal Process 2008, 22:1441-1464.
9. Ativitavas N, Fowler T, Pothisiri T. Acoustic emission characteristics of pultruded fiber reinforced plastics under uniaxial tensile stress. In: Proceedings of European WG on AE, Berlin; 2004. p. 447-54.
10. Anastassopoulos A.A., Philippidis T.P. Clustering methodology for the evaluation of AE from composites. J Acoust Emission 1995, 13:11-22.
11. Huguet S., Godin N., Gaertner R., Salmon L., Villard D. Use of acoustic emission to identify damage modes in glass fibre reinforced polyester. Compos Sci Technol 2002, 62:1433-1444.
12. Kostopoulos V., Loutas T.H., Kontsos A., Sotiriadis G., Pappas Y.Z. On the identification of the failure mechanisms in oxide/oxide composites using acoustic emission. NDT&E Int 2003, 36:571-580.
13. Pappas Y.Z., Kontsos A., Loutas T.H., Kostopoulos V. On the characterization of continuous fibres fracture by quantifying acoustic emission and acousto-ultrasonics waveforms. NDT&E Int 2004, 37:389-401.
14. Kostopoulos V., Loutas T., Dassios K. Fracture behavior and damage mechanisms identification of SiC/glass ceramic composites using AE monitoring. Compos Sci Technol 2007, 67:1740-1746.
15. Godin N., Huguet S., Gaertner R. Integration of the Kohonen's self-organising map and k-means algorithm for the segmentation of the AE data collected during tensile tests on cross-ply composites. NDT&E Int 2005, 38:299-309.
16. Kalogiannakis G., Quintelier J., De Baets P., Degrieck J., Van Hemelrijck D. Identification of wear mechanisms of glass/polyester composites by means of acoustic emission. Wear 2008, 264:235-244.
17. Ziehl PH. Development of a damage based design criterion for fiber reinforced vessels, PhD dissertation, Austin, Texas: University of Texas at Austin; 2000.
18. Stevanovic D., Jar P.Y.B., Kalyanasundaram S., Lowe A. On crack-initiation conditions for mode I and mode II delamination testing of composite materials. Compos Sci Technol 2000, 60:1879-1887.
19. Lagunegrand L., Lorriot T., Harry R., Wargnier H., Quenisset J.M. Initiation of free-edge delamination in composite laminates. Compos Sci Technol 2006, 66:1315-1327.
20. Benmedakhene S., Kenane M., Benzeggagh M.L. Initiation and growth of delamination in glass/epoxy composites subjected to static and dynamic loading by acoustic emission monitoring. Compos Sci Technol 1999, 59:201-208.
21. Ramirez-Jimenez C.R., Papadakis N., Reynolds N., Gan T.H., Purnell P., Pharaoh M. Identification of failure modes in glass/polypropylene composites by means of the primary frequency content of the acoustic emission event. Compos Sci Technol 2004, 64:1819-1827.
22. Mäder E., Moos E., Karger-Kocsis J. Role of film formers in glass fibre reinforced polypropylene - new insights and relation to mechanical properties. Composites Part A 2001, 32:631-639.
23. Kim S.T., Lee Y.T. Characteristics of damage and fracture process of carbon fiber reinforced plastic under loading-unloading test by using AE method. Mater Sci Eng Part A 1997, 234-6:322-326.
24. Kotsikos G., Evans J.T., Gibson A.G., Hale J. Use of acoustic emission to characterize corrosion fatigue damage accumulation in glass fiber reinforced polyester laminates. Polym Compos 1999, 20:689-696.
25. Chandrashekhar B., Bhat M.R., Murthy C.R.L. Acoustic emission characterization of failure modes in composites with ANN. Compos Struct 2003, 61:213-220.
26. Minak G, Zucchelli A. Damage evaluation and residual strength prediction of CFRP laminates by means of acoustic emission techniques. In: Durand LP, editor. Composite Materials Research Progress, New York: Nova Science Publishers Inc.; 2008. p. 165-207.
27. ASTM Standard D5528. Standard test method for mode I interlaminar fracture toughness of unidirectional fiber-reinforced polymer matrix composites, West Conshohocken, PA: ASTM International; 2002.
28. Cesari F., Dal Re V., Minak G., Zucchelli A. Damage and residual strength of laminated graphite-epoxy composite circular plates loaded at the centre. Composites Part A 2007, 38:1163-1173.
29. Paris PC, Sih GC. Stress analysis of cracks, ASTM Special Publication, No. 381, ASTM; 1965.
30. Tada H., Paris P.C., Irwin G.R. The stress analysis of cracks handbook 2000, ASME, New York, NY. 3rd ed.
31. Sridharan Srinivasan, editor. Delamination behaviour of composites. Boca Raton, Boston, New York, Washington, DC: Woodhead Publishing and Maney Publishing on behalf of The Institute of Materials, Minerals & Mining. CRC Press; 2008.
32. Zucchelli A, Dal Re V. Experimental analysis of composite laminate progressive failure by AE monitoring. In: Proceedings ICEM12 - 12th international conference on experimental mechanics, Bari; 2004.
33. Zhuang X., Yan X. Investigation of damage mechanisms in self-reinforced polyethylene composites by acoustic emission. Compos Sci Technol 2006, 66:444-449.
34. Nechad H., Helmstetter A., Guerjouma R.E., Sornette D. Creep ruptures in heterogeneous materials. Phys Rev Lett 2005, 94.
35. Ducret D., Guerjouma R.E., Jayet Y., Baboux J.C. Anisotropic damage evaluation in polymer fiber composites under hygrothermal aging by means of ultrasonic techniques. Rev Prog Quant Nondestruct Eval 2000, 20B:1199-1206.
36. Marec A, Thomas JH, Guerjouma RE. Etude multivariable par émission acoustique de l'endommagement et de la rupture des matériaux composites sollicités en fluage. In: Proceedings of the CFA; 2006. p. 793-6.
37. Alifa N., Carlssona L.A., Booghb L. The effect of weave pattern and crack propagation direction on mode I delamination resistance of woven glass and carbon composites. Composites Part B 1998, 29B:603-611.
38. Pereira A.B., de Morais A.B., de Moura M.F.S.F., Magalhaes A.G. Mode I interlaminar fracture of woven glass/epoxy multidirectional laminates. Composites Part A 2005, 36:1119-1127.
39. Barre S., Benzeggagh M.L. On the use of acoustic emission to investigate damage mechanisms in glass-fiber-reinforced. Compos Sci Technol 1994, 52(3):369-376.