Influence of ZrC content on the elevated temperature tensile properties of ZrCp/W composites

Materials Science and Engineering: A

Volumn 528, Issue 3, 2011, Pages 1805-1811

  Wang, Yujin ^a,b   Peng, Hua Xin ^b   Zhou, Yu ^a   Song, Gui Ming ^a,c  

^a HARBIN INSTITUTE OF TECHNOLOGY   (China)

^b UNIVERSITY OF BRISTOL   (United Kingdom)

^c DELFT UNIVERSITY OF TECHNOLOGY   (Netherlands)

Author keywords

Deformation behavior; High temperature; Ultimate tensile strength; ZrC content

Indexed keywords

FRACTURE TOUGHNESS; STRESS-STRAIN CURVES; TENSILE STRENGTH; TUNGSTEN; ZIRCONIUM COMPOUNDS;

DEFORMATION BEHAVIOR; ELEVATED TEMPERATURE TENSILE PROPERTIES; HIGHEST TEMPERATURE; MATRIX; NONLINEAR FEATURES; STRESS/STRAIN CURVES; TEMPERATURE RANGE; TENSILE DEFORMATION; ULTIMATE TENSILE STRENGTH; ZRC CONTENT;

DEFORMATION;

EID: 78650180087     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2010.11.029     Document Type: Article

References (32)

1. Song G.M., Wang Y.J., Zhou Y. Mater. Sci. Eng. 2002, A334:223-332.
2. Wang Y.J., Zhou Y., Song G.M., Lei T.C. J. Mater. Sci. Technol. 2003, 19:167-169.
3. T.Q. Zhang, High temperature compressive deformation behavior and strength mechanisms of ZrCp/W composites, Harbin Institute of Technology, PhD Thesis, 2008.
4. Zhang S.C., Hilmas G.E., Fahrenholtz W.G. J. Am. Ceram. Soc. 2007, 90:1930-1933.
5. Dickerson M.B., Snyder R.L., Sandhage K.H. J. Am. Ceram. Soc. 2002, 85:730-732.
6. Dickerson M.B., Snyder R.L., Sandhage K.H. Ceram. Eng. Sci. Proc. 2001, 22:97-107.
7. Dickerson M.B., Wurm P.J., Schorr J.R., Hoffman W.P., Wapner P.G., Sandhage K.H. J. Mater. Sci. 2004, 39:6005-6015.
8. Lipke D.W., Zhang Y., Liu Y., Church B.C., Sandhage K.H. J. Eur. Ceram. Soc. 2010, 30:2265-2277.
9. Roosta M., Baharvandi H. Int. J. Refract. Met. Hard Mater. 2010, 28:587-592.
10. Song G.M., Zhou Y., Wang Y.J., Lei T.C. J. Mater. Sci. Lett. 1998, 17:1739-1741.
11. Song G.M., Wang Y.J., Zhou Y. J. Mater. Sci. 2001, 36:4625-4631.
12. Song G.M., Zhou Y., Wang Y.J. Mater. Charact. 2003, 50:293-303.
13. Upadhya K. High Performance High Temperature Materials for Rocket Engines and Space Environment 1993, ASM, Materials Park, OH, p. 1. K. Upadhya (Ed.).
14. Zhang T.Q., Wang Y.J., Zhou Y., Song G.M. Int. J. Refract. Met. Hard Mater. 2009, 27:126-129.
15. Zhang T.Q., Wang Y.J., Zhou Y., Song G.M. Int. J. Refract. Met. Hard Mater. 2009, 27:14-19.
16. Zhou Y., Wang Y.J., Song G.M., Lei T.Q., Huang Z.H. J. Adv. Mater. 2003, 35(2):41-45.
17. Wang Y.J., Zhang T.Q., Zhou Y., Song G.M. J. Comp. Theor. Nanosci. 2008, 5:1730-1734.
18. Zhang T.Q., Wang Y.J., Zhou Y., Lei T.C., Song.G.M. Mater. Sci. Eng. A 2008, 474:382-389.
19. Song G.M., Wang Y.J., Zhou Y. Int. J. Refract. Met. Hard Mater. 2003, 21:1-12.
20. ASTM C 1359-05: Standard Test Method for Monotonic Tensile Strength Testing of Continuous Fiber-reinforced Advanced Ceramics with Solid Rectangular Cross-section Test Specimens at Elevated Temperatures 2005, ASTM International, Philadelphia.
21. ASTM B328-96: Standard Test Method for Density, Oil Content and Interconnected Porosity of Sintered Metal Parts and Oil-impregnated Bearings 2003, ASTM International, Philadelphia.
22. Yih S.W., Wang.C.T. Tungsten-Sources 1979, Plenum Press, New York.
23. T.Y. Kosolapova, Hemisphere Publication Corporation, New York, 1990.
24. Luo A.H., Shin K.S., Jacobson D.L. Scripta Metall. Mater. 1991, 25:2411-2414.
25. Zhang T.Q., Wang Y.J., Zhou Y., Song G.M. Mater. Sci. Eng. A 2009, 512:19-25.
26. Luo A.H., Shin K.S., Jacobson D.L. Mater. Sci. Eng. 1991, A148:219-229.
27. Luo A.H., Jacobson D.L., Shin K.S. Scripta Metall. Mater. 1991, 25:1811-1814.
28. Rice R.W. Porosity of Ceramics 1998, Marcel Dekker Inc., New York.
29. Neshpor V.S., Fridlender B.A., Komozynskii P.A. Powder Metall. Met. Ceram. 1990, 29:330.
30. Zhang T.Q., Wang Y.J., Lei T.Q., Song G.M. Int. J. Refract. Met. Hard Mater. 2007, 25:445-450.
31. Davidge R.W. Mechanical Behavior of Cermics 1979, Cambridge University Press, New York.
32. Lanin A.G., Turchin V.N., Erin O.N. Int. J. Refract. Met. Hard Mater. 1990, 9(3):139-142.