An isolated cohesive crack in tension

Continuum Mechanics and Thermodynamics

Volumn 22, Issue 6, 2010, Pages 617-634

  Dempsey, John P ^a   Tan, Li ^b   Wang, Shen ^c  

^a Clarkson University   (United States)

^b BEIHANG UNIVERSITY   (China)

^c BECHTEL CORPORATION   (United States)

Author keywords

Cohesive crack model; Cohesive zone model; Fictitious crack model; Linear softening; Prescribed cohesive shape; Prescribed cohesive stress; Sea ice

Indexed keywords

COHESIVE CRACK MODELS; COHESIVE STRESS; COHESIVE ZONE MODEL; FICTITIOUS CRACK MODEL; LINEAR SOFTENING; PRESCRIBED COHESIVE SHAPE;

FRACTURE; NUCLEATION; OCEANOGRAPHY; SEA ICE;

CRACKS;

EID: 78650174169     PISSN: 09351175     EISSN: None     Source Type: Journal    
DOI: 10.1007/s00161-010-0144-y     Document Type: Article

References (33)

1. Dempsey, J.P., Adamson, R.M., Mulmule, S.V.: Scale effects on the in-situ tensile strength and fracture of ice. Part II: First-year sea ice at Resolute. N.W.T. Int. J. Fract. 95, 347-366 (1999)
2. Wang, S., Dempsey, J.P., Cole, D.M.: In-situ fracture of first-year sea ice in McMurdo Sound: Test A2-SP8. In: Dempsey, J.P. (ed.) Proc. 18th Int. POAC Conf., vol. 3, pp. 1071-1082. Clarkson University, Potsdam (2006)
3. Mulmule, S.V., Dempsey, J.P.: A viscoelastic fictitious crack model for the fracture of sea ice. Mech. Time-Depend. Mater. 1, 331-356 (1998)
4. Irwin, G.R.: Analysis of stresses and strains near the end of a crack traversing a plate. J. Appl. Mech. 24, 91-94 (1957)
5. Westergaard, H.M.: Bearing pressures and cracks. J. Appl. Mech. 6, A49-A53 (1939)
6. England, A.H., Green, A.E.: Some two-dimensional punch and crack problems in classical elasticity. Proc. Camb. Phil. Soc. 59, 489-500 (1963)
7. Rice, J.R.: Path independent integral and approximate analysis of strain concentration by notches and cracks. J. Appl. Mech. 35, 379-386 (1968)
8. Keer, L.M.: Stress distribution at the base of an equilibrium edge crack. J. Mech. Phys. Solids 12, 149-163 (1964)
9. Wang, W.V., Kramer, E.J.: A distributed dislocation stress analysis for crazes and plastic zones at crack tips. J. Mater. Sci. 17, 2013-2026 (1982)
10. Bilby, B.A., Eshelby, J.D.: Dislocations and the theory of fracture. In: Liebowitz, H. (ed.) Fracture, vol. I. Academic Press, New York (1968)
11. Slepyan, L.I.: Mechanics of Cracks (in Russian). Sudostroenie, Leningrad (1981)
12. Hillerborg, A., Modéer, M., Petersson, P.E.: Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements. Cem. Concr. Res. 6, 773-782 (1976)
13. Barenblatt, G.I.: The mathematical theory of equilibrium cracks in brittle fracture. Adv. Appl. Mech. 7, 55-129 (1962)
14. Dugdale, D.S.: Yielding of steel sheets containing slits. J. Mech. Phys. Solids 8, 100-104 (1960)
15. Planas, J., Elices, M.: Asymptotic analysis of a cohesive crack: 2. Influence of the softening curve. Int. J. Fract. 64, 221-237 (1993)
16. Bilby, B.A., Cottrell, A.H., Swinden, K.H.: The spread of plastic yield from a notch. Proc. R. Soc. Lond. A 272, 304-314 (1963)
17. Goodier, J.N., Field, F.A.: Plastic energy dissipation in crack propagation. In: Drucker, D.C., Gilman, J.J. (eds.) Fracture of Solids, pp. 103-118. Wiley (Interscience), New York (1963)
18. Rice, J.R.: Plastic yielding at a crack tip. In: Yokobori, T., Kawasaki, T., Swedlow, J.L. (eds.) Proc. 1st Int. Conf. Fracture, Sendai, Japan, 1965, Vol. I, pp. 283-308 (1966)
19. Weertman, J.: Dislocation Based Fracture Mechanics. World Scientific, Singapore (1996)
20. Ungsuwarungsri, T., Knauss,W.G.: A nonlinear analysis of an equilibrium craze: Part I-problem formulation and solution; part II-simulations of craze and crack growth. J. Appl. Mech. 55, 44-58 (1988)
21. Li,Y.N., Hong, A.P.: Predictions of failure in notched infinite strips by the cohesive crack model. Int. J. Solids Struct. 29, 2815-2828 (1992)
22. Li,Y.N., Liang, R.Y.: The theory of the boundary eigenvalue problem in the cohesive crack model and its application. J. Mech. Phys. Solids 41, 331-350 (1993)
23. Baẑant, Z.P., Li, Y.-N.: Stability of cohesive crack model: Part I-energy principles; part II-eigenvalue analysis of size effect on strength and ductility of structures. J. Appl. Mech. 62, 959-969 (1995)
24. Uenishi, K., Rice, J.R.: Universal nucleation length for slip-weakening rupture instability under nonuniform fault loading. J. Geophys. Res. 108(B1), 2042 (2003)
25. Ståhle, P.: On the small crack fracture mechanics. Int. J. Fract. 22, 203-216 (1983)
26. Reinhardt, H.W.: Plain concrete as an elastic strain-softening material at fracture. Eng. Fract. Mech. 22, 787-796 (1985)
27. Clarin, P.G.: Fracture analysis of center cracked infinite plates of linearly softening materials. Eng. Fract. Mech. 27, 231-245 (1987)
28. Dascalu, C., Ionescu, I.R., Campillo, M.: Fault finiteness and initiation of dynamic shear instability. Earth. Planet. Sci. Lett. 177, 163-176 (2000)
29. Stakgold, I.: Boundary Value Problems of Mathematical Physics. SIAM, Philadelphia (2000)
30. Smith, E.: The structure in the vicinity of a crack tip: A general theory based on the cohesive zone model. Eng. Fract. Mech. 6, 213-222 (1974)
31. Palmer, A.C., Rice, J.R.: The growth of slip surfaces in the progressive failure of over-consolidated clay. Proc. R. Soc. Lond. A 332, 527-548 (1973)
32. Cottrell, A.H.: The structure of a crack. In: Argon, A.S. (ed.) Physics of Strength and Plasticity, pp. 257-261. The M.I.T. Press, Cambridge, MA (1969)
33. Cribb, J.L., Tomkins, B.: On the nature of the stress at the tip of a perfectly brittle crack. J. Mech. Phys. Solids 15, 135-140 (1967)