Investigation on corrosion of titanium/steel brazed joint

Materialwissenschaft und Werkstofftechnik

Volumn 41, Issue 11, 2010, Pages 908-913

  Elrefaey, A ^a   Wojarski, L ^a   Tillmann, W ^a  

^a TU DORTMUND UNIVERSITY   (Germany)

Author keywords

brazing; Corrosion; mass loss; potentiodynamic polarization

Indexed keywords

BRAZED JOINT; BRAZING TEMPERATURE; COMMERCIALLY PURE TITANIUMS; CORROSION ATTACK; CORROSION BEHAVIOR; CORROSION CURRENT DENSITIES; CORROSION POTENTIALS; ELECTROCHEMICAL TEST; HOLDING TIME; INTERFACIAL AREAS; MASS LOSS; POLARIZATION RESISTANCES; POTENTIODYNAMICS; SEVERE CORROSION; SILVER-BASED FILLER METAL; WEIGHT LOSS; WEIGHT LOSS MEASUREMENTS;

CORROSION RESISTANCE; CORROSIVE EFFECTS; ELECTROCHEMICAL CORROSION; FILLER METALS; LOW CARBON STEEL; POLARIZATION; POTENTIODYNAMIC POLARIZATION; SILVER ALLOYS; SOLDERING; SULFURIC ACID; TITANIUM; TITANIUM ALLOYS; VACUUM BRAZING; VACUUM FURNACES;

CORROSION RATE;

EID: 78649870766     PISSN: 09335137     EISSN: 15214052     Source Type: Journal    
DOI: 10.1002/mawe.201000684     Document Type: Article

References (14)

1. B. Block, H. Haferkamp, A. Ostendorf, O. Meier, J. Huang, T. Hassel, C. Bruns, presented at the 3rd international WLT-conference on laser in manufacturing, Munich, Germany, 13.-16. Juni, 2005, pp. 209-218.
2. H. Fujii, K. Takahashi, Y. Yamashita, Nippon Steel Technical Report No. 88, 2003, pp. 70-75.
3. S. Kundu, M. Ghosh, S. Chatterjee, Mater. Sci. Eng. A 2006, 428, 18.
4. J. G. Banker, J. P. Winsky, Presented at ALTA Autoclave Design & Operation Symposium, Australia, May, 1999.
5. A. Elrefaey, W. Tillmann, Metall. Mater. Trans. A 2007, 38, 2956.
6. R. K. Shiue, S. K. Wu, S. Y. Chen, Acta Mater. 2003, 51, 1991.
7. P. He, J.C. Feng, W. Xu, Mater. Sci. Eng. A 2006, 418, 53.
8. J. A. van Beek, A. A. Kodentsov, F. J. J. van Loo, J. Alloys Compd. 1995, 217, 97.
9. L. S. Castleman, S.M. Motzkin, Biocompatibility of Clinical Implant Materials, CRC Press Boca Raton, Florida 1981.
10. O. C. Pavia, M. A. Barbosa, J. Mater. Sci. 2000, 1165.
11. P. C. Wingert, C. H. Leung, presented at the Thirty Fifth meeting of the IEEE Holm Conference, Chicago, Sept. 18-20, 1989, pp. 87-91.
12. H. Matsuoka, Y. Matsunaga, S. Mitsumoto, H. Seki, Corros. Eng. 1987, 36, 625.
13. E. Ariza, L. A. Rocha, O. C. presented at the European Corrosion Conference, Nice, 2004.
14. O. C. Paiva, M. A. Barbosa, Mater. Sci. Eng. A 2008, 480, 306.