Effects of K and anion impurity concentration on crack growth kinetics near alloy 182/A533B weld overlay boundaries in BWRS

14th International Conference on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors 2009

Volumn 1, Issue , 2009, Pages 671-683

  Kumagai, Katsuhiko ^a   Morra, Martin ^b   Andresen, Peter ^b   Catlin, Gregory ^b   Nelson, Lawrence ^b   Suzuki, Shunichi ^a   Takagi, Yoshio ^a   Horn, Ronald ^c  

^a TOKYO ELECTRIC POWER COMPANY   (Japan)

^b GE GLOBAL RESEARCH   (United States)

^c GE HITACHI NUCLEAR ENERGY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK ADVANCE; CRACK KINETICS; DISSIMILAR WELD; IMPURITY CONCENTRATION; LOW ALLOY STEELS; STEADY OPERATING CONDITIONS; STRESS CORROSION CRACK; TEST RESULTS; THRESHOLD CONDITION; WELD OVERLAY;

ALLOYS; BOILING WATER REACTORS; CHLORINE COMPOUNDS; CRACK PROPAGATION; DEGRADATION; GROWTH KINETICS; NUCLEAR ENERGY; STRESS CORROSION CRACKING; UNLOADING; WELDING; WELDS;

CRACKS;

EID: 78649338495     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (10)

1. K. KUSSMAUL, D. BLIND and V. LAEPPLE, Nuclear Eng. and Design, 168 (1997), p. 53-75
2. S. RITTER and H.P. SEIFERT, NACE Corrosion 2002, Paper #02516
3. th Int. Conf. on Env. Deg. of Materials in Nuclear Power Systems-Water Reactor (2000), p.911
4. th Int. Conf. on Env. Deg. of Materials in Nuclear Power Systems-Water Reactor (2002)
5. th Int. Conf. on Nuclear Engineering, Paper ICONE 9-66, 8-12 (2001)
6. th Int. Conf. on Env. Deg. of Materials in Nuclear Power Systems-Water Reactor (2005),
7. H.P. SEIFERT, et al Journal of Nuclear Materials, 378 (2008), p. 197-210
8. th Int. Conf. on Env. Deg. of Materials in Nuclear Power Systems-Water Reactor (2000), p.411
9. H.P. SEIFERT and S. RITTER, Journal of Nuclear Materials, 372 (2008), p. 114-131
10. H.P.S EIFERT and S. RITTER, SKI Report 2005: 60, (2004).