Improved dehydrogenation of TiF3-doped NaAIH4 using ordered mesoporous SIO2 as a codopant

Journal of Materials Research

Volumn 25, Issue 10, 2010, Pages 2047-2053

  Zheng, Shiyou ^a,b   Li, Yongtao ^a   Fang, Fang ^a   Zhou, Guangyou ^a   Yu, Xuebin ^a   Chen, Guorong ^a   Sun, Dalin ^a   Ouyang, Liuzhang ^c   Zhu, Min ^c  

^a FUDAN UNIVERSITY   (China)

^b SHANGHAI INSTITUTE OF CERAMICS   (China)

^c SOUTH CHINA UNIVERSITY OF TECHNOLOGY   (China)

Author keywords

[No Author keywords available]

Indexed keywords

CATALYTIC MECHANISMS; CO-DOPANTS; HIGH SPECIFIC SURFACE AREA; MESOPOROUS; NANOSIZED PORES; ORDERED MESOPOROUS; SYNERGISTIC EFFECT; TEMPERATURE RANGE;

DEHYDROGENATION;

SILICON COMPOUNDS;

EID: 77958106409     PISSN: 08842914     EISSN: None     Source Type: Journal    
DOI: 10.1557/jmr.2010.0260     Document Type: Article

References (35)

1. L. Schlapbach and A. Züttel: Hydrogen-storage materials for mobile applications. Nature 414, 353 (2001).
2. W. Grochala and P.P. Edwards: Thermal decomposition of non-interstitial hydrides for storage and production of hydrogen. Chem. Rev. 104, 1283 (2004).
3. S. Orimo, Y. Nakamori, J.R. Eliseo, A. Züttel, and CM. Jensen: Complex hydrides for hydrogen storage. Chem. Rev. 107, 4111 (2007).
4. N. Eigen, C. Keller, M. Dornheim, T. Klassen, and R. Bormann: Industrial production of light metal hydrides for hydrogen storage. Scr. Mater. 56, 847 (2007).
5. B. Bogdanović and M. Schwickardi: Ti-doped alkali metal aluminum hydrides as potential novel reversible hydrogen storage material. J. Alloys Comped. 1, 253 (1997).
6. 4. J. Alloys Comped. 356-357, 400 (2003).
7. 4. J. Alloys Comped. 297, 270 (2000).
8. S. Chaudhuri, J. Graetz, A. Ignatov, J.J. Reilly, and J.T. Muckerman: Understanding the role of Ti in reversible hydrogen storage as sodium alanate: A combined experimental and density functional theoretical approach. J. Am. Chem. Soc. 128,11404 (2006).
9. B. Bogdanović, M. Fclderhoff, S. Kaskel, A. Pommcrin, K. Schlichte, and F Schüth: Improvement hydrogen storage properties of Ti-doped sodium alanate using titanium nanoparticles as doping agents. Adv. Meiter. 15, 1012 (2003).
10. B. Bogdanović, R.A. Brand, A. Marjanovic, M. .Schwickardi, and J. Tolle: Metal-doped sodium aluminium hydrides as potential new hydrogen-storage materials. J. Alloys Comped. 302, 36 (2000).
11. 4. J. Alloys Compel. 373,265 (2004).
12. 4. Adv. Mater. 18, 1 198 (2006).
13. 4, for hydrogen storage induces grain refinement and impacts on hydrogen vacancy formation. Acta Mater. 55, 5549 (2007).
14. 4. J. Alloys Compd. 330-332, 702 (2002).
15. 4 J. Phys. Chem. B 109, 6952 (2005).'
16. F. Fang, J. Zhang, J. Zhu, G. Chen, D. Sun, B. He, Z. Wei, and S. Wei: Nature and role of Ti species in the hydrogenation of a NaH/AI mixture..J. Wm. Chem. C 111, 3476 (2007).
17. A. Gutowska, L. Li, Y. Shin, CM. Wang, X.S. Li, J.C Linehan, R.S. Smith, B.D. Kay, B. Schmid, W. Shaw, M. Gutowski, and T. Autrey: Nanoscaffold mediates hydrogen release and the reactivity of ammonia borane. Angew. Chem. Int. Ed. 44, 3578 (2005).
18. 4 in nanoporous carbon scaffolds. J. Phys. Chem. C 112, 5651 (2008).
19. 4 a new hydrogen storage material.J. Power Sources 118, 1 (2008).
20. 4/silica-gel mixtures and the effect of additives. J. Phys. Chem. C 111, 14026 (2007).
21. 4 nanoparticles in ordered mesoporous silica. Chem. Mater. 20,3954 (2008).
22. 4. J. Am. Chem. Soc. 131, 13198 (2009).
23. 4 at low temperature and pressure. J. Phys. Chem. B 107, 10176 (2003).
24. H. Zhang. J. Sun, D. Ma, X. Bao, A. Klein-Hoffmann, G. Weinberg, D. Su, and R. Schlögl: Unusual mesoporous SBA-15 with parallel channels running along the short axis. J. Am. Chem. Soc. 126, 7440 (2004).
25. F. Schüth: Non-siliceous mesostructured and mesoporous materials. Chem. Mater. 13, 3184 (2001).
26. E. Kochrick, P. Krawiec, W. Schnelle, D. Geiger, F.M. Schappacher, R. Pöttgen, and S. Kaskel: Space-confined formation of FePt nanoparticles in ordered mesoporous silica SBA-15. Adv. Mater. 19, 3021 (2007).
27. H. Hsueh, C. Yang, J.I. Zink, and M.H. Huang: Formation of titanium nitride nanoparticles within mesoporous silica SBA-15, J. Phys. Chem. 8 109,4404 (2005).
28. 4: Elucidation of doping induced structural changes and their relationship to enhanced hydrogen storage properties, J. Alloys Compel. 337, L8 (2002).
29. P. Claudy, B. Bonnetot, G. Cliahme, and J.M. Letoffe: Study of the thermal behavior of sodium tetrahydroaluminate and sodium hexahydroaluminate. Thermochim. Acta 38, 75 (1980).
30. J.A. Dills and E.G. Ashby: A study of the thermal decomposition of complex metal hydrides. Inorg. Chem. 11, 1230 (1972).
31. F Schüth, B. Bogdanović, and M. Felderhoff: Light metal hydrides and complex hydrides for hydrogen storage. Chem. Commun. (Comb.) 20, 2249 (2004).
32. H.E. Kissinger: Reaction kinetics in differential thermal analysis. Anal Chem. 29, 1702 (1957).
33. E.E. Santiso, A.M.. George, C.H. Turner, M.K. Kpstov, K.E. Gubbins, M. Buongiorno-Nardelli, and M. Sliwinska-Bartkowiak: Adsorption and catalysis: The effect of confinement on chemical reactions. Appl. Surf. Sci. 252, 766 (2005).
34. 4. J. Alloys Compd. 437, 360 (2007).
35. Z. Dehouche, L. Lafi, N. Grimard, J. Goyette, and R. Chahine: The catalytic effect of single-wall carbon nanotubes on the hydrogen sorption properties of sodium alanates, Nanotechnology 16, 402 (2005).