Correlations between intergranular stress corrosion cracking, grain-boundary microchemistry, and grain-boundary electrochemistry for Al-Zn-Mg-Cu alloys
|
Author keywords
A. Aluminium; C. Stress Corrosion
|
Indexed keywords
A. ALUMINIUM;
AL-ZN-MG-CU ALLOY;
BENEFICIAL EFFECTS;
C. STRESS CORROSION;
COPPER CONTENT;
GRAIN-BOUNDARY PRECIPITATES;
INTERGRANULAR FRACTURE;
INTERGRANULAR STRESS CORROSION CRACKING;
MATRIX;
OPEN-CIRCUIT POTENTIAL;
OVER-AGING;
ALUMINUM;
BRITTLE FRACTURE;
CERIUM ALLOYS;
COPPER;
RESIDUAL STRESSES;
TEXTURES;
STRESS CORROSION CRACKING;
|