Effect of densification on crack initiation under Vickers indentation test

Journal of Non-Crystalline Solids

Volumn 356, Issue 35-36, 2010, Pages 1768-1773

  Kato, Yoshinari ^a,b   Yamazaki, Hiroki ^a   Yoshida, Satoshi ^b   Matsuoka, Jun ^b  

^a NIPPON ELECTRIC GLASS CO LTD   (Japan)

^b UNIVERSITY OF SHIGA PREFECTURE   (Japan)

Author keywords

Crack growth C281; Fracture F200; Glasses G205; Oxydes O180

Indexed keywords

COMMERCIAL GLASS; CRACK GROWTH; CRACK RESISTANCE; OXYDES O180; VICKERS INDENTATION; VICKERS INDENTATION TEST;

CRACK INITIATION; DENSIFICATION; FRACTURE; FRACTURE TOUGHNESS; GLASS; HARDNESS; STRESS CORROSION CRACKING; VICKERS HARDNESS TESTING;

CRACKS;

EID: 77956341940     PISSN: 00223093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.jnoncrysol.2010.07.015     Document Type: Article

References (13)

1. M. Wada, H. Furukawa, and K. Fujita Proc. X Int. Congr. Glass 11 1974 39
2. B.R. Lawn, and D.B. Marshall J. Am. Ceram. Soc. 62 1979 347
3. J. Sehgal, Y. Nakao, H. Takahashi, and S. Ito J. Mat. Sci. Lett. 14 1995 167
4. J. Sehgal, and S. Ito J. Non-Cryst. Solids 253 1999 126
5. Japanese Industrial Standard, JIS R1607.
6. J.E. Neely, and J.D. Mackenzie J. Mater. Sci. 3 1968 603
7. S. Yoshida, S. Isono, J. Matsuoka, and N. Soga J. Am. Ceram. Soc. 84 2001 2141
8. S. Yoshida, J.-C. Sanglebouef, and T. Rouxel J. Mater. Res. 20 2005 3404
9. S. Yoshida, J.-C. Sanglebouef, and T. Rouxel Int. J. Mater. Res. 98 2007 360
10. J.D. Maceknzie J. Am. Ceram. Soc. 46 1963 470
11. R.F. Cook, and G.M. Pharr J. Am. Ceram. Soc. 73 1990 787
12. B.R. Lawn, A.G. Evans, and D.B. Marshall J. Am. Ceram. Soc. 63 1980 574
13. E.H. Yoffe Philos. Mag. A 46 1982 617