Glass-forming ability and competitive crystalline phases for lightweight Ti-Be-based alloys

Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

Volumn 41, Issue 7, 2010, Pages 1670-1676

  Zhang, Y ^a   Zhang, W G ^a,b   Lin, J P ^a   Hao, G J ^a   Chen, G L ^a   Liaw, P K ^c  

^a UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

^b CHINA ACADEMY OF SPACE TECHNOLOGY   (China)

^c University of Tennessee Knoxville   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

CRYSTALLINE PHASIS; CRYSTALLIZATION TEMPERATURE; CU-MOLD CASTING; GLASS TRANSITION TEMPERATURE; GLASS-FORMING ABILITY; SEM; SUPERCOOLED LIQUID REGION; TERNARY ALLOY SYSTEMS; X-RAY DIFFRACTOMETRY;

BERYLLIUM ALLOYS; CERIUM ALLOYS; CRYSTALLINE MATERIALS; GLASS; GLASS TRANSITION; METALLIC GLASS; SCANNING ELECTRON MICROSCOPY; SUPERCOOLING; TERNARY ALLOYS; TERNARY SYSTEMS; X RAY DIFFRACTION ANALYSIS; ZIRCONIUM;

TITANIUM ALLOYS;

EID: 77955768429     PISSN: 10735623     EISSN: None     Source Type: Journal    
DOI: 10.1007/s11661-009-0122-9     Document Type: Article

References (36)

1. A. Peker and W. L. Johnson: Appl. Phys. Lett., 1993, vol. 63, pp. 2342-44.
2. F. Q. Guo, H. J. Wang, S. J. Poon, and G. J. Shiflet: Appl. Phys. Lett., 2005, vol. 86, p. 091907 (1-3).
3. H. Tan, Y. Zhang, D. Ma, Y. P. Feng, and Y. Li: Acta Mater., 2003, vol. 51, pp. 4551-61.
4. Y. Zhang, W. Xu, H. Tan, and Y. Li: Acta Mater., 2005, vol. 53, pp. 2607-16.
5. G. J. Hao, Y. Zhang, J. P. Lin, Y. L. Wang, Z. Lin, and G. L. Chen: Mater. Lett., 2006, vol. 60, pp. 1256-60.
6. Y. Zhang, Y. Li, H. Tan, G. L. Chen, and H. A. Davies: J. Non-Cryst. Solids, 2006, vol. 352, pp. 5482-86.
7. C. L. Ma, S. Ishihara, H. Soejima, N. Nishiyama, and A. Inoue: Mater. Trans., 2004, vol. 45, pp. 1802-06.
8. H. Men, S. J. Pang, A. Inoue, and T. Zhang: Mater. Trans., 2005, vol. 46, pp. 2218-20.
9. J. J. Oak, D. V. Louzguine-Luzgin, and A. Inoue: J. Mater. Res., 2007, vol. 22, pp. 1346-53.
10. W. H. Peter, P. K. Liaw, R. A. Buchanan, C. T. Liu, C. R. Brooks, I. A. Horton, C. A. Carmichael, and I. L. Wright: Intermetallics, 2002, vol. 10 (11-12), pp. 1125-29.
11. G. Y. Wang, P. K. Liaw, W. H. Peter, B. Yang, Y. Yokoyama, M. L. Benson, B. A. Green, M. J. Kirkham, S. A. White, T. A. Saleh, R. L. McDaniels, R. V. Steward, C. T. Liu, and C. R. Brooks: Intermetallics, 2004, vol. 12 (7-9), pp. 885-92.
12. W. H. Peter, R. A. Buchanan, C. T. Liu, P. K. Liaw, M. L. Morrison, I. A. Horton, C. A. Carmichael, and J. L. Wright: Intermetallics, 2002, vol. 10 (11-12), pp. 1157-62.
13. B. Yang, P. K. Liaw, G. Wang, M. Morrison, C. T. Liu, R. A. Buchanan, and Y. Yokoyama: Intermetallics, 2004, vol. 12 (10-11), pp. 1265-74.
14. H. Q. Li, C. Fan, K. X. Tao, H. Choo, and P. K. Liaw: Adv. Mater, 2006, vol. 18 (6), pp. 752-54.
15. W. H. Jiang, G. J. Fan, F. X. Liu, G. Y. Wang, H. Choo, and P. K. Liaw: J. Mater. Res, 2006, vol. 21 (9), pp. 2164-67.
16. C. Fan, H. Q. Li, L. I. Kecskes, K. X. Tao, H. Choo, P. K. Liaw, and C. T. Liu: Phys. Rev. Lett, 2006, vol. 96 (14), pp. 145506-09.
17. B. Yang, C. T. Liu, T. G. Nieh, M. L. Morrison, P. K. Liaw, and R. A. Buchanan: J. Mater. Res, 2006, vol. 21 (4), pp. 915-22.
18. G. Chen, H. Bei, Y. Cao, A. Gali, C. T. Liu, and E. P. George: Appl. Phys. Lett., 2009, vol. 95, p. 081908 (1-3).
19. G. Y. Sun, G. Chen, and G. L. Chen: Intermetallics, 2007, vol. 15 (5-6), pp. 632-34.
20. L. E. Tanner and R. Ray: Scripta Metall., 1977, vol. 11, pp. 783-89.
21. R. Hasegawa and L. E. Tanner: Phys. Rev. B, 1977, vol. 16, pp. 3925-28.
22. L. E. Tanner and R. Ray: Acta Metall., 1979, vol. 27, pp. 1727-47.
23. L. E. Tanner and R. Ray: Scripta Metall., 1977, vol. 11 (9), pp. 783-89.
24. A. Wiest, G. Duan, M. D. Demetriou, L. A. Wiest, A. Peck, G. Kaltenboeck, B. Wiest, and W. L. Johnson: Acta Mater., 2008, vol. 56, pp. 2625-30.
25. G. Duan, A. Wiest, M. L. Lind, A. Kahl, and W. L. Johnson: Scripta Mater., 2008, vol. 58, pp. 465-68.
26. D. C. Hoffmann, J. Suh, A. Wiest, M. Lind, M. D. Demetriou, and W. L. Johnson: PNAS, 2008, vol. 105 (51), pp. 20136-40.
27. Z. P. Lu, J. Shen, D. W. Xing, J. F. Sun, and C. T. Liu: Appl. Phys. Lett., 2006, vol. 89, p. 071910 (1-3).
28. Y. Zhang, Y. F. Ji, D. Q. Zhao, Y. X. Zhuang, R. J. Wang, M. X. Pan, Y. D. Dong, and W. H. Wang: Scripta Mater., 2001, vol. 44, pp. 1107-12.
29. Y. Zhang, Y. J. Zhou, J. P. Lin, G. L. Chen, and P. K. Liaw: Adv. Eng. Mater, 2008, vol. 10 (6), pp. 534-38.
30. A. Inoue and A. Takeuchi: Mater. Trans., 2002, vol. 43, pp. 1892-1906.
31. Y. Zhang, Y. J. Zhou, X. D. Hui, M. L. Wang, and G. L. Chen: Sci. China, Ser. G, 2008, vol. 51 (4), pp. 427-37.
32. Y. Zhang, J. Chen, G. L. Chen, and X. J. Liu: Appl. Phys. Lett., 2006, vol. 89, p. 131904 (1-3).
33. Y. Zhang, M. X. Pan, D. Q. Zhao, R. J. Wang, and W. H. Wang: Mater. Trans. JIM, 2000, vol. 41 (11), pp. 1410-14.
34. W. Z. Liang, J. Shen, and J. F. Sun: J. Alloys Compd., 2006, vol. 420 (1-2), pp. 94-97.
35. X. D. Hui, W. Dong, G. L. Chen, and K. F. Yao: Acta Mater., 2007, vol. 55, pp. 907-20.
36. Y. K. Xu, H. Ma, J. Xu, and E. Ma: Acta Mater., 2005, vol. 53, pp. 1857-66.