A voronoi fe fatigue damage model for life scatter in rolling contacts

Journal of Tribology

Volumn 132, Issue 2, 2010, Pages 1-14

  Jalalahmadi, Behrooz ^a   Sadeghi, Farshid ^a  

^a Purdue University   (United States)

Author keywords

Damage mechanics; Material microstructure; Numerical simulation; Rolling contact fatigue; Voronoi nite element method

Indexed keywords

FATIGUE DAMAGE; FINITE ELEMENT METHOD; FRICTION; MICROSTRUCTURE; NUMERICAL METHODS; TOPOLOGY;

BEARINGS MATERIAL; DAMAGE-MECHANICS; ELEMENT METHOD; FATIGUE DAMAGE MODELS; INHOMOGENEOUS MATERIALS; MATERIAL MICROSTRUCTURES; ROLLING CONTACT FATIGUE; ROLLING CONTACT FATIGUE LIFE; VORONOI; VORONOI NITE ELEMENT METHOD;

NORMAL DISTRIBUTION;

EID: 77955297723     PISSN: 07424787     EISSN: 15288897     Source Type: Journal    
DOI: 10.1115/1.4001012     Document Type: Article

References (58)

1. Littmann, W. E., and Widner, R. L., 1966, " Propagation of Contact Fatigue From Surface and Sub-Surface Origins," ASME J. Basic Eng., 88, pp. 624-636.
2. Littmann, W. E., 1969, "The Mechanism of Contact Fatigue," NASA Special Report No. SP-237.
3. Voskamp, A. P., Osterlund, R., Becker, P. C., and Vingsbo, O., 1980, "Gradual Changes in Residual Stress and Microstructure During Contact Fatigue in Ball Bearings," Met. Technol. (London), 7, pp. 14-21.
4. Österlund, R., and Vingsbo, O., 1980, "Phase Changes in Fatigued Ball Bearings," Metall. Trans. A, 11, pp. 701-707.
5. Voskamp, A. P., 1985, "Material Response to Rolling Contact Loading," ASME J. Tribol., 107, pp. 359-366.
6. Voskamp, A. P., 1998, "Fatigue and Material Response in Rolling Contact," Bearing Steels: Into the 20th Century," ASTM, Philadelphia, PA, Vol. 1328, pp. 152-166.
7. Voskamp, A. P., and Mittemeijer, E. J., 1997, "The Effect of the Changing Microstructure on the Fatigue Behavior During Cyclic Rolling Contact Loading," Z. Metallkd., 88, pp. 310-319.
8. Lou, B., Han, L., Lu, Z., Liu, S., and Shen, F., 1990, "The Rolling Contact Fatigue Behaviors in Carburized and Hardened Steel," Fatigue 90: Proceedings of the Fourth International Conference on Fatigue and Fatigue Thresholds, H. Kitagawa and T. Tanaka, eds., Honolulu, HI, pp. 627-632.
9. Furuma, K., Shirota, S., and Hirakawa, K., 1975, "The Subsurface-Initiated and the Surface-Initiated Rolling Fatigue Life of Bearing Steels," Proceedings of the JSLE-ASLE International Conference on Lubrication, Tokyo, Japan, pp. 475-483.
10. Bower, A. F., 1988, "The Inuence of Crack Face Friction and Trapped Fluid on Surface Initiated Rolling Contact Fatigue Cracks," ASME J. Tribol., 110, pp. 704-711.
11. Nélias, D., Dumont, M. L., Champiot, F., Vincent, A., Girodin, D., Fougeres, R., and Flamand, L., 1999, "Role of Inclusions, Surface Roughness and Operating Conditions on Rolling Contact Fatigue," ASME J. Tribol., 121(2), pp. 240-251.
12. Miller, K. J., 1999, "A Historical Perspective of the Important Parameters of Metal Fatigue; and Problems for the Next Century," Fatigue '99: Proceedings of the Seventh International Fatigue Congress, Beijing, China, pp. 15-39.
13. Ito, O., and Fuller, E. R., 1993, "Computer Modeling of Anisotropic Grain Microstructure in Two Dimensions," Acta Metall. Mater., 41, pp. 191-198.
14. Zavattieri, P. D., 2000, "Computational Modeling for Bridging Size Scales in the Failure of Solids," Ph.D. thesis, Purdue University, West Lafayette, IN.
15. Zavattieri, P. D., and Espinosa, H. D., 2001, "Grain Level Analysis of Crack Initiation and Propagation in Brittle Materials," Acta Mater., 49, pp. 4291-4311.
16. Jalalahmadi, B., and Sadeghi, F., 2009, "A Voronoi Finite Element Study of Fatigue Life Scatter in Rolling Contacts," ASME J. Trib., 131(2), p. 022203.
17. Lundberg, G., and Palmgren, A., 1947, "Dynamic Capacity of Rolling Bearings," Acta Polytech. Scand., Mech. Eng. Ser., 1(3), pp. 7-53.
18. Chiu, Y. P., Tallian, T. E., and McCool, J. I., 1971, "An Engineering Model of Spalling Fatigue Failure in Rolling Contact-The Subsurface Model," Wear, 17, pp. 433-446.
19. Ioannides, E., and Harris, T. A., 1985, "A New Fatigue Life Model for Rolling Bearings," ASME J. Tribol., 107(3), pp. 367-378.
20. Schlicht, H., Schreiber, E., and Zwirlein, O., 1986, "Fatigue and Failure Mechanism of Bearings," Proceedings of International Conference on Fatigue of Engineering Materials and Structures, Institution of Mechanical Engineering, Publications Limited, London, pp. 85-91.
21. Tallian, T. E., 1992, "Simplied Contact Fatigue Life Prediction Model-Part I: Review of Published Models," ASME J. Tribol., 114, pp. 207-213.
22. Tallian, T. E., 1992, "Simplied Contact Fatigue Life Prediction Model-Part II: New Model," ASME J. Tribol., 114, pp. 214-222.
23. Zaretsky, E. V., 1994, "Design for Life, Plan for Death," Mach. Des., 66(15), pp. 55-59.
24. Keer, L. M., and Bryant, M. D., 1983, "A Pitting Model for Rolling Contact Fatigue," ASME J. Lubr. Technol., 105, pp. 198-205.
25. Bhargava, V., Hahn, G. T., and Rubin, C. A., 1990, "Rolling Contact Deformation, Etching Effects and Failure of High Strength Steels," Metall. Trans. A, 21, pp. 1921-1931.
26. Zhou, R. S., 1993, "Surface Topography and Fatigue Life of Rolling Contact Bearings," Tribol. Trans., 36, pp. 329-340.
27. Cheng, W., and Cheng, H. S., 1995, " Semi-Analytical Modeling of Crack Initiation Dominant Contact Fatigue for Roller Bearings," Proceedings of the 1995 Joint ASME/STLE Tribology Conference, Orlando, FL.
28. Lormand, G., Meynaud, G., Vincent, A., Baudry, G., Girodin, D., and Dudragne, G., 1998, "From Cleanliness to Rolling Fatigue Life of Bearings-A New Approach," Bearing Steels: Into the 21st Century,J.Hoo and W. Green, eds., ASTM, Philadelphia, PA, Vol. 1327, pp. 55-69.
29. Jiang, Y., and Sehitoglu, H., 1999, "A Model for Rolling Contact Failure," Wear, 224, pp. 38-49.
30. Raje, N. N., Sadeghi, F., and Rateick, R. G., Jr., 2008, "A Statistical Damage Mechanics Model for Subsurface Initiated Spalling in Rolling Contacts," ASME J. Tribol., 130(4), p. 042201.
31. Kachanov, L. M., 1958, "Time of the Rupture Process Under Creep Conditions," Izv. Akad. Nauk SSSR, Otd. Tekh. Nauk., 8, pp. 26-31.
32. Robotnov, Y. N., 1969, Creep Problems in Structural Mechanics, North-Holland, Amsterdam.
33. Chaboche, J. L., 1988, "Continuum Damage Mechanics: Part I-General Concepts," ASME J. Appl. Mech., 55, pp. 59-64.
34. Memon, I. R., Zhang, X., and Cui, D., 2002, "Fatigue Life Prediction of 3-D Problems by Damage Mechanics With Two-Block Loading," Int. J. Fatigue, 24, pp. 29-37.
35. Chen, L., Chen, Q., and Shao, E., 1989, "Study on Initiation and Propagation Angles of Sub-Surface Cracks in GCr15 Bearing Steel Under Rolling Contact," Wear, 133, pp. 205-218.
36. Okabe, A., and Boots, B., 1992, Spatial Tessellations: Concepts and Applications of Voronoi Diagrams, Wiley, New York.
37. Moller, J., 1994, Lectures Notes on Random Voronoi Tessellations, Springer, Berlin.
38. Lemaitre, J., 1992, A Course on Damage Mechanics, Springer-Verlag, Berlin.
39. Chaboche, J. L., and Lesne, P. M., 1988, "A Non-Linear Continuous Fatigue Damage Model," Fatigue Fract. Eng. Mater. Struct., 11, pp. 1-17.
40. Xiao, Y. C., Li, S., and Gao, Z., 1998, "A Continuum Damage Mechanics Model for High Cycle Fatigue," Int. J. Fatigue, 20, pp. 503-508.
41. Memon, I. R., Cui, D., and Zhang, X., 1999, "Fatigue Life Prediction of 3-D Problems by Damage Mechanics-Finite Element Additional Load Method," Proceedings of the Seventh International Fatigue Conference, Beijing, China, pp. 827-832.
42. Bolotin, V. V., 1999, Mechanics of Fatigue, CRC, Boca Raton, FL.
43. Otsuka, A., Sugawara, H., and Shomura, M., 1996, "A Test Method for Mode II Fatigue Crack Growth Relating to a Model for Rolling Contact Fatigue," Fatigue Fract. Eng. Mater. Struct., 19(10), pp. 1265-1275.
44. Lemaitre, J., Sermage, J. P., and Desmorat, R., 1999, "A Two Scale Damage Concept Applied to Fatigue," Int. J. Fract., 97, pp. 67-81.
45. Styri, H., 1951, "Fatigue Strength of Ball Bearing Races and Heat-Treated 52100 Steel Specimens," Proceedings of the ASTM 1951, Vol. 51, pp. 682-700.
46. Ashby, M. F., and Hallam, S. D., 1986, "The Fracture of Brittle Solids Containing Small Cracks Under Compressive Stress States," Acta Mater., 34, pp. 497-510.
47. Wang, Y., and Hadeld, M., 2004, "Failure Modes of Ceramic Rolling Elements With Surface Crack Defects," Wear, 256, pp. 208-219.
48. Melander, A., 1998, "Simulation of the Behavior of Short Cracks at Inclusions Under Rolling Contact Fatigue Loading-Specially the Effect of Plasticity," Bearing Steels: Into the 21st Century, J. Hoo and W. Green, eds., ASTM, Philadelphia, PA, Vol. 1327, pp. 70-86.
49. Raje, N., Slack, T., and Sadeghi, F., 2009, "A Discrete Damage Mechanics Model for High Cycle Fatigue in Polycrystalline Materials Subject to Rolling Contact," Int. J. Fatigue, 31, pp. 346-360.
50. Shao, E., Huang, X., Wang, C., Zhu, Y., and Chen, Q., 1987, "A Method of Detecting Rolling Contact Crack Initiation and the Establishment of Crack Propagation Curves," STLE Tribol. Trans., 31(1), pp. 6-11.
51. Leng, X., Chen, Q., and Shao, E., 1988, "Initiation and Propagation of Case Crushing Cracks in Rolling Contact Fatigue," Wear, 122, pp. 33-43.
52. Miyashita, Y., Yoshimura, Y., Xu, J.-Q., Horikoshi, M., and Mutoh, Y., 2003, "Subsurface Crack Propagation in Rolling Contact Fatigue of Sintered Alloy," JSME Int. J., Ser. A, 46(3), pp. 341-347.
53. Fajdiga, G., Glodez, S., and Kramar, J., 2007, "Pitting Formation Due to Surface and Sub-Surface Initiated Fatigue Crack Growth in Contacting Mechanical Elements," Wear, 262, pp. 1217-1224
54. Chen, Q., Shao, E., Zhao, D., Gue, J., and Fan, Z., 1991, "Measurement of the Critical Size of Inclusions Initiating Contact Fatigue Cracks and Its Application in Bearing Steels," Wear, 147, pp. 285-294.
55. Harris, T. A., 2001, Rolling Bearing Analysis, Wiley, New York..
56. Harris, T. A., and Barnsby, R. M., 2001, "Life Ratings for Ball and Roller Bearings," Proc. Inst. Mech. Eng., Part J: J. Eng. Tribol., 215, pp. 577-595
57. Jalalahmadi, B., Sadeghi, F., and Peroulis, D., 2009, "A Numerical Fatigue Damage Model for Life Scatter of MEMS Devices," J. Microelectromech. Syst., 18(5), pp. 1016-1031.
58. Poplawski, J. V., Peters, S. M., and Zaretsky, E. V., 2001, "Effect of Roller Pro?le on Cylindrical Roller Bearing Life Predication-Part I: Comparison of Bearing Life Theories," Tribol. Trans., 44(3), pp. 339-350.