Increased Tcin electrolyte-gated cuprates

Advanced Materials

Volumn 22, Issue 23, 2010, Pages 2529-2533

  Dhoot, Anoop Singh ^a   Wimbush, Stuart C ^b   Benseman, Tim ^a   MacManus Driscoll, Judith L ^b   Cooper, J R ^a   Friend, Richard Henry ^a  

^a UNIVERSITY OF CAMBRIDGE   (United Kingdom)

^b UNIVERSITY OF CAMBRIDGE   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

ACTIVE CONDUCTORS; CUPRATES; HIGH-T;

COPPER COMPOUNDS; ELECTROLYTES; GATE DIELECTRICS; GATES (TRANSISTOR); SUPERCONDUCTING TRANSITION TEMPERATURE; SUPERCONDUCTIVITY;

FIELD EFFECT TRANSISTORS;

COPPER; LITHIUM DERIVATIVE; LITHIUM PERCHLORATE; MACROGOL DERIVATIVE; PERCHLORIC ACID;

ARTICLE; CHEMISTRY; IMPEDANCE; SEMICONDUCTOR; TRANSITION TEMPERATURE;

COPPER; ELECTRIC IMPEDANCE; LITHIUM COMPOUNDS; PERCHLORIC ACID; POLYETHYLENE GLYCOLS; TRANSISTORS, ELECTRONIC; TRANSITION TEMPERATURE;

EID: 77954263485     PISSN: 09359648     EISSN: 15214095     Source Type: Journal    
DOI: 10.1002/adma.200904024     Document Type: Article

References (27)

1. J. G. Bednorz, K. A. Müller, Z. Phys. B 1986, 64, 189.
2. A. T. Fiory, A. F. Hebard, R. H. Eick, P. M. Mankiewich, R. E. Howard, M. L. O'Malley, Phys. Rev. Lett. 1990, 65, 3441.
3. J. Mannhart, Supercond. Sci. Technol. 1996, 9, 49, and references contained therein.
4. R. E. Glover, M. D. Sherrill, Phys. Rev. Lett. 1960, 5, 248.
5. X. X. Xi, C. Doughty, A. Walkenhorst, C. Kwon, Q. Li, T. Venkatesan, Phys. Rev. Lett. 1992, 68, 1240.
6. C. H. Ahn, S. Gariglio, P. Paruch, T. Tybell, L. Antognazza, J.-M. Triscone, Science 1999, 284, 1152.
7. H. Shimotani, H. Asanuma, A. Tsukazaki, A. Ohtomo, M. Kawasaki, Y. Iwasa, Appl. Phys. Lett. 2007, 97, 082106.
8. K. Ueno, S. Nakamura, H. Shimotani, A. Ohtomo, N. Kimura, T. Nojima, H. Aoki, Y. Iwasa, M. Kawasaki, Nat. Mater. 2008, 7, 855.
9. A. S. Dhoot, C. Israel, X. Moya, N. D. Mathur, R. H. Friend, Phys. Rev. Lett. 2009, 102, 136402.
10. N.F. Mott, A Life In Science, Taylor & Francis, London and Philadelphia 1986, p. 134.
11. A. Pinkowski, K. Jüttner, W. J. Lorenz, G. Saemann-Ischenko, M. W. Breiter, J. Electroanal. Chem. 1990, 286, 253.
12. M. Schwartz, D. Cahen, M. Rappaport, G. Hodes, Solid State Ionics 1989, 32, 1137.
13. M. Schwartz, Y. Scolnik, M. Rappaport, G. Hodes, D. Cahen, J. Mater. Chem. 1991, 1, 339.
14. H. Tada, T. Nojima, S. Nakamura, H. Shimotani, Y. Iwasa, N. Kobayashi, J. Phys.: Conf. Ser. 2009, 150, 052255.
15. On values obtained for single crystals; Y. Ando, S. Komiya, K. Segawa, S. Ono, Y. Kurita, Phys. Rev. Lett. 2004, 93, 267001.
16. F. K. Shokoohi, L. M. Schiavone, C. T. Rogers, A. Inam, X. D. Wu, L. Nazar, T. Venkatesan, Appl. Phys. Lett. 1989, 55, 2661.
17. J. Mannhart, J. Ströbel, J. G. Bednorz, C. Gerber, Appl. Phys. Lett. 1993, 62, 630.
18. For this device, a 100-nm-thick epitaxial YBCO film was etched and used as the superconducting layer. In addition, gold was deposited on one half of the YBCO layer and used as the gate electrode.
19. c over time as found for the polymer electrolyte (Fig. 2c).
20. C. I. H. Ashby, J. Martens, T. A. Plut, D. S. Ginley, J. M. Phillips, Appl. Phys. Lett. 1992, 60, 2147.
21. T. Frey, J. Mannhart, J. G. Bednorz, E. J. Williams, Phys. Rev. B 1995, 51, 3257.
22. V. Talyansky, S. B. Ogale, I. Takeuchi, C. Doughty, T. Venkatesan, Phys. Rev. B 1996, 53, 14575.
23. A. V. Mitin, N. E. Alekseevskii, E. P. Khlybov, Phys. C (Amsterdam, Neth.) 1992, 199, 351.
24. g=-3V. Superconductivity was restored to the sample. In this way, the transition was confirmed to be reversible and not to depend on any irrevocable change to the superconducting layer.
25. N. Chandrasekhar, O. T. Valls, A. M. Goldman, Phys. Rev. Lett. 1993, 71, 1079.
26. B. W. Veal, A. P. Paulikas, H. You, H. Shi, Y. Fang, J. W. Downey, Phys. Rev. B 1990, 42, 6305.
27. H. Shaked, J. D. Jorgensen, B. A. Hunter, R. L. Hitterman, A. P. Paulikas, B. W. Veal, Phys. Rev. B 1995, 57, 547.