A comparison of progressive-failure criteria in the prediction of the dynamic bending failure of composite laminated beams

Composite Structures

Volumn 92, Issue 10, 2010, Pages 2406-2414

  Santiuste, C ^a   Sanchez Saez S ^a   Barbero, E ^a  

^a UNIVERSIDAD CARLOS III DE MADRID   (Spain)

Author keywords

Failure criteria; Finite element analysis; Impact behaviour; Laminates

Indexed keywords

COMPRESSIVE FAILURE; CROSS-PLY; DROP WEIGHT; DYNAMIC CONDITION; FAILURE CRITERIA; FAILURE MECHANISM; FINITE ELEMENT ANALYSIS; FINITE ELEMENT CODES; IMPACT BEHAVIOUR; LAMINATED BEAMS; LOW VELOCITY IMPACT; MATRIX; MATRIX CRACKING; NUMERICAL MODELS; POINT CONFIGURATIONS; PROGRESSIVE FAILURE; SPLIT HOPKINSON PRESSURE BARS; TENSILE FAILURES;

FINITE ELEMENT METHOD; LAMINATES; METALLIC GLASS; QUALITY ASSURANCE; TOWERS;

FAILURE ANALYSIS;

BEAM; COMPOSITE PROPERTY; COMPRESSIVE PROPERTY; FAILURE ANALYSIS; FIBER REINFORCED COMPOSITE; FINITE ELEMENT ANALYSIS; LAMINATE; MATHEMATICAL MODEL; TENSILE PROPERTY;

EID: 77952422500     PISSN: 02638223     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compstruct.2010.03.004     Document Type: Article

References (36)

1. Turon A., Costa J., Maimi P., Trias D., Mayugo J.A. A progressive damage model for unidirectional fibre-reinforced composites based on fibre fragmentation. Part I: formulation. Compos Sci Technol 2005, 65(13):2039-2048.
2. Davies G.A.O., Hitchings D., Wang J. Prediction of threshold impact energy for onset of delamination in quasi-isotropic carbon/epoxy composite laminates under low-velocity impact. Compos Sci Technol 2000, 60(1):1-7.
3. Sanchez-Saez S., Barbero E., Zaera R., Navarro C. Compression after impact of thin composite laminates. Compos Sci Technol 2005, 65(13):1911-1919.
4. Chan S., Fawaz Z., Behdinan K., Amid R. Ballistic limit prediction using a numerical model with progressive damage capability. Compos Struct 2007, 77(4):466-474.
5. Sanchez-Saez S., Barbero E., Navarro C. Compressive residual strength at low temperatures of composite laminates subjected to low-velocity impacts. Compos Struct 2007, 85(3):226-232.
6. Tita V., de Carvalho J., Vandepitte D. Failure analysis of low velocity impact on thin composite laminates: experimental and numerical approaches. Compos Struct 2008, 83(4):413-428.
7. Deka L.J., Bartus S.D., Vaidya U.K. Damage evolution and energy absorption of E-glass/polypropylene laminates subjected to ballistic impact. J Mater Sci 2008, 43(13):4399-4410.
8. Sheikh A.H., Bull P.H., Kepler J.A. Behaviour of multiple composite plates subjected to ballistic impact. Compos Sci Technol 2009, 69:704-710.
9. Hallett S.R. Three-point beam impact tests on T300/914 carbon-fibre composites. Compos Sci Technol 2000, 60:115-124.
10. Sánchez-Sáez S., Barbero E., Navarro C. Analysis of the dynamic flexural behaviour of composite beams at low temperature. Compos Sci Technol 2007, 67(11-12):2616-2632.
11. Sevkat E., Liaw B., Delale F., Raju B.B. A combined experimental and numerical approach to study ballistic impact response of S2-glass fiber/toughened epoxy composite beams. Compos Sci Technol 2009, 69(7-8):965-982.
12. Maimí P., Camanho P.P., Mayugo J.A., Dávila C.G. A continuum damage model for composite laminates. Part II - computational implementation and validation. Mech Mater 2007, 39(10):897-908.
13. Nahas N.M. Survey of failure and post-failure theories of laminated fiber-reinforced composites. J Compos Technol Res 1986, 8(4):138-153.
14. Paris F. A study of failure criteria of fibrous composite materials. Technical report: NASA-cr210661, 2001.
15. Kärger L., Baaran J., Tessmer J. Efficient simulation of low-velocity impacts on composite sandwich panels. Comput Struct 2008, 86:988-996.
16. Jadhav P., Mantena P.R., Gibson R.F. Energy absorption and damage evaluation of grid stiffened composite panels under transverse loading. Composites Part B 2006, 37(2-3):191-199.
17. Greve L., Pickett A.K. Delamination testing and modelling for composite crash simulation. Compos Sci Technol 2006, 66:816-826.
18. Hashin Z. Failure criteria for unidirectional fiber composites. J Appl Mech 1980, 47(2):329-334.
19. Hou J.P., Petrinic N., Ruiz C., Hallett S.R. Prediction of impact damage in composite plates. Compos Sci Technol 2000, 60(2):228-273.
20. Chang F., Chang K. A progressive damage model for laminated composites containing stress concentrations. J Compos Mater 1987, 21:834-855.
21. Foo C.C., Chai G.B., Seah L.K. A model to predict low-velocity impact response and damage in sandwich composites. Compos Sci Technol 2008, 68:1348-1356.
22. Minak G., Abrate S., Ghellia D., Pancirolia R., Zucchellia A. Low-velocity impact on carbon/epoxy tubes subjected to torque - experimental results, analytical models and fem analysis. Compos Struct 2010, 92:623-632.
23. Sriram R., Vaidya U.K., Kim J.E. Blast impact response of aluminum foam sandwich composites. J Mater Sci 2006, 41(13):4023-4039.
24. Gómez-del Rio T., Zaera R., Barbero E., Navarro C. Damage in CFRPs due to low velocity impact at low temperature. Composites Part B 2005, 36(1):41-50.
25. Ghasemnejad H., Hadavinia H., Aboutorabi A. Effect of delamination failure in crashworthiness analysis of hybrid composite box structures. Mater Des 2010, 31:1105-1116.
26. García-Castillo S.K., Sánchez-Sáez S., López-Puente J., Barbero E., Navarro C. Impact behaviour of preloaded glass/polyester woven plates. Compos Sci Technol 2009, 69(6):711-717.
27. Meo M., Morris A.J., Vignjevic R., Marengo G. Numerical simulations of low-velocity impact on an aircraft sandwich panel. Compos Struct 2003, 62(3-4):353-360.
28. Nguyen M.Q., Jacombs S.S., Thomson R.S., Hachenberg D., Scott M.L. Simulation of impact on sandwich structures. Compos Struct 2005, 67:217-227.
29. Zangani D., Robinson M., Gibson A.G. Energy absorption characteristics of web-core sandwich composite panels subjected to drop-weight impact. Appl Compos Mater 2008, 15:139-156.
30. Heimbs S., Cichosz J., Klaus M., Kilchert S., Johnson A.F. Sandwich structures with textile-reinforced composite foldcores under impact loads. Compos Struct 2010, 92:1485-1497.
31. Ivañez I., Santiuste C., Sanchez-Saez S. FEM analysis of dynamic flexural behaviour of composite sandwich beams with foam core. Compos Struct 2009, 10.1016/j.compstruct.2009.07.01.
32. Hashin Z., Rotem A. A fatigue failure criterion for fiber reinforced materials. Compos Mater 1973, 7:448-464.
33. Kim RY, Soni SR. Failure of composite laminates due to combined interlaminar normal and shear stresses. In: Kawata K, Umekawa S, Kobayashi A, editors. Composites'86: recent advances in Japan and the United States. Proceedings of Japan-U.S. CCM-III, 1986. p. 341-50.
34. Brewer J.C., Lagace P.A. Quadratic stress criterion for initiation of delamination. J Compos Mater 1988, 22(12):1141-1155.
35. Mahanta B.B., Chakraborty D., Dutta A. Accurate prediction of delamination in FRP composite laminates resulting from transverse impact. Compos Sci Technol 2004, 64:2341-2351.
36. Lopez-Puente J., Zaera R., Navarro C. Experimental and numerical analysis of normal and oblique ballistic impacts on thin carbon/epoxy woven laminates. Composites: Part A 2008, 39:374-387.