Crack initiation behavior from internal defect in high carbon-chromium bearing steel under rolling contact fatigue

Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

Volumn 94, Issue 1, 2008, Pages 13-20

  Fujimatsu, Takeshi ^a   Hiraoka, Kazuhiko ^a   Yamamoto, Atsushi ^b  

^a Nakashima   (Japan)

^b UNIVERSITY OF HYOGO   (Japan)

Author keywords

Bearing steel; Fracture observation; Initial crack; Internal defect; Nonmetallic inclusion; Pore; Rolling contact fatigue life; Stress

Indexed keywords

BEARING STEEL; BEARING STEELS; INTERNAL DEFECTS; NON-METALLIC INCLUSIONS; NONMETALLIC INCLUSION; ROLLING CONTACT FATIGUE LIFE;

BEARINGS (MACHINE PARTS); BEARINGS (STRUCTURAL); CHROMIUM; FATIGUE OF MATERIALS; FRACTURE; FRICTION; INCLUSIONS; STEEL METALLURGY;

CRACKS;

EID: 77949813528     PISSN: 00211575     EISSN: None     Source Type: Journal    
DOI: 10.2355/tetsutohagane.94.13     Document Type: Article

References (12)

1. T. Uesugi: Tetsu-to-Hagané, 74 (1988), 1889.
2. H. Narai, T. Abe, K. Furumura, H. Nishimori, K. Kobayashi and K. Tsubota: CAMP-ISIJ, 5 (1992), 1959.
3. T. Fujimatsu, M. Nagao, M. Nakasaki and K. Hiraoka: CAMP-ISIJ, 19 (2006), 485.
4. M. Nagao, K. Hiraoka and Y. Unigame: Sanyo Tech. Rep., 12 (2005), 38.
5. T. Fujimatsu, M. Nagao, M. Nakasaki and K. Hiraoka: Sanyo Tech. Rep., 13 (2006), 62.
6. Y. Murakami: Sanyo Techn. Rep., 1 (1994), 3.
7. D. Nelias, M. L. Dumont, F. Champiot, A. Vincent, D. Girodin, R. Fougeres and L. Flamand: ASME. J. Tribology, 121 (1999), 240.
8. H. Takemura and Y. Murakami: International Symposium, Finland, (1995), 345.
9. L. T. Lu and K. Shiozawa: Irans. Jpn. Soc. Mech. Eng. A, 67 (2001), 1630.
10. T. Sakai, M. Takeda, K. Shiozawa, Y. Ochi, M. Nakajima, T. Nakamura and N. Oguma: J Soc. Mater. Sci., Jpn., 49 (2000), 779.
11. Y. Murakami, T. Nomoto, T. Ueda, Y. Murakami and M. Ohori: J. Soc. Mater. Sci., Jpn., 48 (1999), 1112.
12. Y. Murakami, S. Hamada, K. Sugino and K. Takao: J. Soc. Mater. Sci., Jpn., 43 (1994), 1264.