Volumn 24, Issue 12, 2009, Pages 1431-1435

Improvement of fatigue strength of maraging steel by shot peening

Author keywords

Fatigue; Fracture mechanism; Maraging steel; Reversion austenite; Shot peening

Indexed keywords

FATIGUE; FATIGUE FRACTURE MECHANISMS; FATIGUE LIFE; FATIGUE STRENGTH; FINE PARTICLES; FRACTURE MECHANISM; FRACTURE MECHANISMS; FRACTURE ORIGINS; INTERGRANULAR CRACKING; INTERNAL FRACTURE; LONG LIFE; ROTATING BENDING FATIGUE; S-N CURVE; S-N PROPERTY; SPECIMEN SURFACES; SUPERHARD; SURFACE FRACTURE;

EID: 77949544167     PISSN: 10426914     EISSN: 15322475     Source Type: Journal    
DOI: 10.1080/10426910903386055     Document Type: Article
Times cited : (33)

References (8)
  • 2
    • 85009578756 scopus 로고
    • Effects of nonmetallic inclusions, small defects and small cracks on fatigue strength of metals
    • Murakami, Y.; Shimizu, M. Effects of nonmetallic inclusions, small defects and small cracks on fatigue strength of metals. Trans. Jpn. Soc. Mech. Eng. A 1983, 54, 413.
    • (1983) Trans. Jpn. Soc. Mech. Eng. A , vol.54 , pp. 413
    • Murakami, Y.1    Shimizu, M.2
  • 3
    • 34547203032 scopus 로고
    • Fatigue crack growth under stress corrosion conditions of a high strength steel
    • Endo, K.; Komai, K.; Fujimoto, T.; Matsuda, Y. Fatigue crack growth under stress corrosion conditions of a high strength steel. Trans. Jpn. Soc. Mech. Eng. A 1979, 45, 1152.
    • (1979) Trans. Jpn. Soc. Mech. Eng. A , vol.45 , pp. 1152
    • Endo, K.1    Komai, K.2    Fujimoto, T.3    Matsuda, Y.4
  • 4
    • 0003106712 scopus 로고
    • Relation between shotpeening residual stress distribution and fatigue crack propagation life in spring steel
    • Tange, A.; Akutsu, T.; Takamura, N. Relation between shotpeening residual stress distribution and fatigue crack propagation life in spring steel. Bane Ronbunshu 1991, 36, 47.
    • (1991) Bane Ronbunshu , vol.36 , pp. 47
    • Tange, A.1    Akutsu, T.2    Takamura, N.3
  • 5
    • 0023999231 scopus 로고
    • Quantitative evaluation of effects of nonmetallic inclusions on fatigue strength of high strength steel
    • Murakami, Y.; Kodama, S.; Konuma, S. Quantitative evaluation of effects of nonmetallic inclusions on fatigue strength of high strength steel. Trans. Jpn. Soc. Mech. Eng. A 1988, 54, 688.
    • (1988) Trans. Jpn. Soc. Mech. Eng. A , vol.54 , pp. 688
    • Murakami, Y.1    Kodama, S.2    Konuma, S.3
  • 6
    • 0023114116 scopus 로고
    • Effects of small defects and inclusions on fatigue strength of maraging steel
    • Murakami, Y.; Abe, M.; Kiyota, T. Effects of small defects and inclusions on fatigue strength of maraging steel. Trans. Jpn. Soc. Mech. Eng. A 1987, 53, 688.
    • (1987) Trans. Jpn. Soc. Mech. Eng. A , vol.53 , pp. 688
    • Murakami, Y.1    Abe, M.2    Kiyota, T.3
  • 8
    • 0037941523 scopus 로고    scopus 로고
    • Influence of reversion austenite on initiation and propagation of fatigue crack of maraging steel
    • Nagano, T.; Kawagoishi, N.; Moriyama, M. Influence of reversion austenite on initiation and propagation of fatigue crack of maraging steel. Trans. Jpn. Soc. Mech. Eng. A 2003, 69, 633.
    • (2003) Trans. Jpn. Soc. Mech. Eng. A , vol.69 , pp. 633
    • Nagano, T.1    Kawagoishi, N.2    Moriyama, M.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.