Study on the SCC growth of alloy 182 under constant displacement condition in high temperature oxygenated water

American Society of Mechanical Engineers, Pressure Vessels and Piping Division (Publication) PVP

Volumn 479, Issue , 2004, Pages 209-215

  Suzuki, Shunichi ^a   Kumagai, Katsuhiko ^a   Namatame, Satoshi ^a   Kikuchi, Masaaki ^b   Itow, Mikiro ^b   Futami, Tsuneo ^c  

^a TOKYO ELECTRIC POWER COMPANY   (Japan)

^b TOSHIBA CORPORATION   (Japan)

^c CENTRAL RESEARCH INSTITUTE OF ELECTRIC POWER INDUSTRY   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

CONSTANT DISPLACEMENT; GROWTH RATES; OXYGENATED WATER; WELD METALS;

BOILING WATER REACTORS; GROWTH (MATERIALS); MATHEMATICAL MODELS; RESIDUAL STRESSES; TEMPERATURE MEASUREMENT; TENSILE STRESS; WATER;

STRESS CORROSION CRACKING;

EID: 7744235357     PISSN: 0277027X     EISSN: None     Source Type: Conference Proceeding    
DOI: 10.1115/PVP2004-2665     Document Type: Conference Paper

References (11)

1. th International Symposium on Environmental Degradation of Materials in Nuclear Power Systems- Water Reactor, pp.712-719.
2. Itow, M., et al., 2000, "SCC Crack Growth Rates of Type 304 Stainless Steel at High K Region in Simulated BWR Environments", CORROSION 2000, NACE, No.221.
3. Katayama, Y., et al., 2002, "Long term SCC growth behavior of austenitic stainless steel in high temperature water" Proc. 49th Zairyo to Kankyo Touronkai, pp.303-304.
4. Kikuchi, E., et al., 1997, "Intergranular Stress Corrosion Crack Growth of Sensitized Type 304 Stainless Steel in a Simulated Boiling-Water Reactor Environment", CORROSION, NACE, Vol.53, No.4, pp. 306-311.
5. Lefort, P., and Mowbray, d. F., 1978, "Calibration of the Side-Grooved Modified Wedge-opening load Specimen", Journal of Testing and Evaluation, vol.6, N0.2, pp.114-119.
6. Namatame, S., et al., 2001, "SCC growth behavior in Alloy 182 under constant displacement conditions" Proc. 48th Zairyo to Kankyo Touronkai, pp. 135-138.
7. Saito, N., et al., 1997, "Susceptibility of Sensitized Type 304 Stainless Steel to Intergranular Stress Corrosion Cracking in Simulated Boiling-Water Reactor Environments", CORROSION, NACE, Vol.51, No.7, pp. 537-545.
8. Shoji, T., et al., 1995, "Theoretical Prediction of SCC Growth Behavior", Proceedings of the Seventh International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, NACE, pp. 881-889.
9. Suzuki, S., 1999, "Effect of Stress Biaxiality on SCC Growth Rate", Proceedings of the Ninth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, TMS, pp. 361-371.
10. Suzuki, S., et al., 1995, "Theoretical SCC Crack Growth Prediction Under Various Loading Modes in High Temperature Water", Proceedings of the Eighth International Symposium on Environmental Degradation of Materials in Nuclear Power Systems, ANS, pp. 695-703.
11. Suzuki, S., 2001, Ph.D thesis.