Aging of alkali-resistant glass and basalt fibers in alkaline solutions: Evaluation of the failure stress by Weibull distribution function

Author keywords

Chemical durability; Corrosion; Defects; Fracture; Nanoparticles; Oxide glasses; Scanning electron microscopy; Strength

Indexed keywords

ALKALI RESISTANT; ALKALINE SOLUTIONS; BASALT FIBER; CALCIUM IONS; CHEMICAL CONSTITUTION; CHEMICAL DURABILITY; CORROSION DEFECT; CORROSION MECHANISMS; FAILURE STRESS; GLASS NETWORK; HYDROXYL ION; INHIBITING EFFECT; LOCAL ATTACK; MECHANICAL BEHAVIOR; MIXED DISTRIBUTION; NAOH SOLUTIONS; ON TIME; OUTER LAYER; OXIDE GLASS; PH VALUE; STRENGTH DISTRIBUTION;

EID: 72149127173     PISSN: 00223093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.jnoncrysol.2009.09.018     Document Type: Article
Times cited : (209)

References (23)
  • 21
    • 72149108514 scopus 로고    scopus 로고
    • S. Hempel, M. Götze, R. Hempel, Korrosionsverhalten von AR-Glasfasern unter extremer exposition. Tagungsbericht 16. Internationale Baustofftagung 'ibausil', Bd. 2, S.223, Bauhaus-Universität Weimar, 2006-10-06.
    • S. Hempel, M. Götze, R. Hempel, Korrosionsverhalten von AR-Glasfasern unter extremer exposition. Tagungsbericht 16. Internationale Baustofftagung 'ibausil', Bd. 2, S.223, Bauhaus-Universität Weimar, 2006-10-06.


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.