Volumn 32, Issue 1, 2010, Pages 29-36

High-cycle fatigue characteristics of quasi-isotropic CFRP laminates over 108 cycles (Initiation and propagation of delamination considering interaction with transverse cracks)

Author keywords

Composites; Delamination; Energy release rate; High cycle fatigue; Transverse crack

Indexed keywords

APPLIED STRESS; CFRP LAMINATE; COMPOSITES; EDGE DELAMINATION; FATIGUE DAMAGE GROWTH; HIGH-CYCLE FATIGUE; HIGH-CYCLE FATIGUES; HIGH-CYCLE LOADING; INITIATION AND PROPAGATION; ISOTROPIC CARBON; STACKING SEQUENCE; TRANSVERSE CRACK;

EID: 70349993421     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2009.02.028     Document Type: Article
Times cited : (95)

References (19)
  • 1
    • 85129342846 scopus 로고
    • The dependence of transverse cracking and delamination on ply thickness in graphite/epoxy laminates
    • Crossman F.W., and Wang A.S.D. The dependence of transverse cracking and delamination on ply thickness in graphite/epoxy laminates. ASTM STP 775 (1982) 118-139
    • (1982) ASTM STP , vol.775 , pp. 118-139
    • Crossman, F.W.1    Wang, A.S.D.2
  • 2
    • 0022198987 scopus 로고
    • Analysis of local delamination and their influence on composite laminate behavior
    • O'Brien T.K. Analysis of local delamination and their influence on composite laminate behavior. ASTM STP 876 (1985) 282-297
    • (1985) ASTM STP , vol.876 , pp. 282-297
    • O'Brien, T.K.1
  • 3
    • 0025842907 scopus 로고
    • Combined effect of matrix cracking and free edge on delamination
    • Salpekar S.A., and O'Brien T.K. Combined effect of matrix cracking and free edge on delamination. ASTM STP 1110 (1991) 287-311
    • (1991) ASTM STP , vol.1110 , pp. 287-311
    • Salpekar, S.A.1    O'Brien, T.K.2
  • 4
    • 0002256402 scopus 로고
    • The initiation and growth of delamination induced by matrix microcracks in laminated composites
    • Nairn J.A., and Hu S. The initiation and growth of delamination induced by matrix microcracks in laminated composites. Int J Fatigue 57 (1992) 1-24
    • (1992) Int J Fatigue , vol.57 , pp. 1-24
    • Nairn, J.A.1    Hu, S.2
  • 5
    • 0028699132 scopus 로고
    • Initiation and growth of delamination from the tips of transverse cracks in CFRP cross-ply laminates
    • Takeda N., and Ogihara S. Initiation and growth of delamination from the tips of transverse cracks in CFRP cross-ply laminates. Compos Sci Technol 52 (1994) 309-318
    • (1994) Compos Sci Technol , vol.52 , pp. 309-318
    • Takeda, N.1    Ogihara, S.2
  • 6
    • 0000621169 scopus 로고
    • Microscopic fatigue damage progress in CFRP cross-ply laminates
    • Takeda N., Ogihara S., and Kobayashi A. Microscopic fatigue damage progress in CFRP cross-ply laminates. Composites 26 (1995) 859-867
    • (1995) Composites , vol.26 , pp. 859-867
    • Takeda, N.1    Ogihara, S.2    Kobayashi, A.3
  • 7
    • 0034464708 scopus 로고    scopus 로고
    • The effect of delamination induced by transverse cracks and splits on stiffness properties of composite laminates
    • Kashtalyan M., and Soutis C. The effect of delamination induced by transverse cracks and splits on stiffness properties of composite laminates. Compos Part A-Appl S 31 (2000) 107-119
    • (2000) Compos Part A-Appl S , vol.31 , pp. 107-119
    • Kashtalyan, M.1    Soutis, C.2
  • 8
    • 0037066162 scopus 로고    scopus 로고
    • Analysis of local delaminations in composite laminates with angle-ply matrix cracks
    • Kashtalyan M., and Soutis C. Analysis of local delaminations in composite laminates with angle-ply matrix cracks. Int J Solids Struct 39 (2002) 1515-1537
    • (2002) Int J Solids Struct , vol.39 , pp. 1515-1537
    • Kashtalyan, M.1    Soutis, C.2
  • 9
    • 38149143131 scopus 로고
    • Effects of matrix cracking and hygrothermal stresses on the strain energy release rate for edge delamination in composite laminates
    • Zhang J., Soutis C., and Fan J. Effects of matrix cracking and hygrothermal stresses on the strain energy release rate for edge delamination in composite laminates. Composites 25 (1994) 27-35
    • (1994) Composites , vol.25 , pp. 27-35
    • Zhang, J.1    Soutis, C.2    Fan, J.3
  • 10
    • 0028257264 scopus 로고
    • Interaction between matrix cracking and edge delamination in composite laminates
    • Xu L.Y. Interaction between matrix cracking and edge delamination in composite laminates. Compos Sci Technol 50 (1994) 469-478
    • (1994) Compos Sci Technol , vol.50 , pp. 469-478
    • Xu, L.Y.1
  • 12
    • 0000382348 scopus 로고    scopus 로고
    • Fracture mechanics of composite with residual thermal stresses
    • Nairn J.A. Fracture mechanics of composite with residual thermal stresses. J Appl Mech 64 (1997) 804-810
    • (1997) J Appl Mech , vol.64 , pp. 804-810
    • Nairn, J.A.1
  • 13
    • 34547935758 scopus 로고    scopus 로고
    • High-cycle fatigue characteristics of quasi-isotropic CFRP laminates
    • Hosoi A., Arao Y., Karasawa H., and Kawada H. High-cycle fatigue characteristics of quasi-isotropic CFRP laminates. Adv Compos Mater 16 (2007) 151-166
    • (2007) Adv Compos Mater , vol.16 , pp. 151-166
    • Hosoi, A.1    Arao, Y.2    Karasawa, H.3    Kawada, H.4
  • 14
    • 33745953929 scopus 로고    scopus 로고
    • Fatigue characteristic of quasi-isotropic CFRP laminates subjected to variable amplitude cyclic loading of two-stage
    • Hosoi A., Kawada H., and Yoshino H. Fatigue characteristic of quasi-isotropic CFRP laminates subjected to variable amplitude cyclic loading of two-stage. Int J Fatigue 28 (2006) 1284-1289
    • (2006) Int J Fatigue , vol.28 , pp. 1284-1289
    • Hosoi, A.1    Kawada, H.2    Yoshino, H.3
  • 15
    • 0027205776 scopus 로고
    • In-situ damage evolution and micro/macro transition for laminated composites
    • Fan J., and Zhang J. In-situ damage evolution and micro/macro transition for laminated composites. Composi Sci Technol 47 (1993) 107-118
    • (1993) Composi Sci Technol , vol.47 , pp. 107-118
    • Fan, J.1    Zhang, J.2
  • 16
    • 84958508474 scopus 로고
    • Characterization of delamination onset and growth in composite laminate
    • O'Brien T.K. Characterization of delamination onset and growth in composite laminate. ASTM STP 775 (1982) 140-167
    • (1982) ASTM STP , vol.775 , pp. 140-167
    • O'Brien, T.K.1
  • 17
    • 0032655842 scopus 로고    scopus 로고
    • Analytical modeling of stiffness reduction in symmetric and balanced laminates due to cracks in 90° layers
    • Joffe R., and Varna J. Analytical modeling of stiffness reduction in symmetric and balanced laminates due to cracks in 90° layers. Compos Sci Technol 59 (1999) 1641-1652
    • (1999) Compos Sci Technol , vol.59 , pp. 1641-1652
    • Joffe, R.1    Varna, J.2
  • 18
    • 0022740013 scopus 로고
    • Residual thermal and moisture influence on the strain energy release rate analysis of edge delamination
    • O'Brien T.K., Raju I.S., and Garber D.P. Residual thermal and moisture influence on the strain energy release rate analysis of edge delamination. J Compos Technol Res 8 (1986) 37-47
    • (1986) J Compos Technol Res , vol.8 , pp. 37-47
    • O'Brien, T.K.1    Raju, I.S.2    Garber, D.P.3
  • 19
    • 0022231438 scopus 로고
    • Delamination crack growth in composite laminates
    • Wang A.S.D., Slomiana M., and Bucinell R.B. Delamination crack growth in composite laminates. ASTM STP 876 (1985) 135-167
    • (1985) ASTM STP , vol.876 , pp. 135-167
    • Wang, A.S.D.1    Slomiana, M.2    Bucinell, R.B.3


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.