Effect of the amount of 3-methacyloxypropyltrimethoxysilane coupling agent on physical properties of dental resin nanocomposites

Dental Materials

Volumn 25, Issue 11, 2009, Pages 1315-1324

  Sideridou, Irini D ^a   Karabela, Maria M ^a  

^a ARISTOTLE UNIVERSITY OF THESSALONIKI   (Greece)

Author keywords

MPS; 3 Point bending; Degree of conversion; Dental nanocomposites; DMA; Silane coupling agents; Sorption; Thermogravimetric analysis

Indexed keywords

3-POINT BENDING; DEGREE OF CONVERSION; DENTAL NANOCOMPOSITES; DMA; SILANE COUPLING AGENTS;

BENDING STRENGTH; COUPLING AGENTS; DENTAL COMPOSITES; DYNAMICS; ELASTIC MODULI; FILLERS; MAGNETOPLASMA; MECHANICAL PROPERTIES; MOLECULES; NANOCOMPOSITES; NANOPARTICLES; RESINS; SILANES; SILICA; SORPTION;

THERMOGRAVIMETRIC ANALYSIS;

3 METHACRYLOXYPROPYLTRIMETHOXYSILANE; 3-METHACRYLOXYPROPYLTRIMETHOXYSILANE; ALCOHOL; BIOMEDICAL AND DENTAL MATERIALS; BISPHENOL A BIS(2 HYDROXYPROPYL) ETHER DIMETHACRYLATE; MACROGOL DERIVATIVE; METHACRYLIC ACID DERIVATIVE; NANOCOMPOSITE; POLYMETHACRYLIC ACID DERIVATIVE; RESIN; SILANE DERIVATIVE; SILICON DIOXIDE; SOLVENT; TRIETHYLENE GLYCOL DIMETHACRYLATE; WATER;

ABSORPTION; ADHESION; ADSORPTION; ARTICLE; CHEMISTRY; HUMAN; INFRARED SPECTROSCOPY; MATERIALS TESTING; MECHANICAL STRESS; MECHANICS; PHYSICAL CHEMISTRY; PLIABILITY; SOLUBILITY; SURFACE PROPERTY; TEMPERATURE; THERMOGRAVIMETRY; YOUNG MODULUS;

ABSORPTION; ADHESIVENESS; ADSORPTION; BISPHENOL A-GLYCIDYL METHACRYLATE; COMPOSITE RESINS; DENTAL MATERIALS; ELASTIC MODULUS; ETHANOL; HUMANS; MATERIALS TESTING; MECHANICAL PHENOMENA; METHACRYLATES; NANOCOMPOSITES; PHYSICOCHEMICAL PHENOMENA; PLIABILITY; POLYETHYLENE GLYCOLS; POLYMETHACRYLIC ACIDS; SILANES; SILICON DIOXIDE; SOLUBILITY; SOLVENTS; SPECTROSCOPY, FOURIER TRANSFORM INFRARED; STRESS, MECHANICAL; SURFACE PROPERTIES; TEMPERATURE; THERMOGRAVIMETRY; WATER;

EID: 70349416437     PISSN: 01095641     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.dental.2009.03.016     Document Type: Article

References (38)

1. Kim J.W., Kim L.U., Kim C.K., Cho B.H., and Kim O.Y. Characteristics of novel dental composites containing 2,2-bis[4-(2-methoxy-3-methacryloyloxy propoxy) phenyl] propane as a base resin. Biomacromolecules 7 (2006) 154-160
2. Wilson K.S., Zhang K., and Antonucci J.M. Systematic variation of interfacial phase reactivity in dental nanocomposites. Biomaterials 26 (2005) 5095-5103
3. Wilson K.S., and Antonucci J.M. Interphase structure-property relationships in thermoset dimethacrylate nanocomposites. Dent Mater 22 (2006) 995-1001
4. Wilson K.S., Allen A.J., Washburn N.R., and Antonucci J.M. Interphase effects in dental nanocomposites investigated by small-angle neutron scattering. J Biomed Mater Res 81A (2007) 113-123
5. Brown S.K. Mechanics of fracture in filled thermosetting resins. Br Polymer J 12 (1980) 24-30
6. Mohsen N.M., and Craig R.G. Effect of silanation of fillers on their dispersability by monomers systems. J Oral Rehabil 22 (1995) 183-189
7. Calais J.G., and Söderholm K.-J.M. Influence of filler type and water exposure on flexural strength of experimental composite resins. J Dent Res 67 (1988) 836-840
8. Nishiyama N., Ishizaki T., Horie K., Tomari M., and Someya M. Novel polyfunctional silanes for improved hydrolytic stability at the polymer-silica interface. J Biomed Mater Res 25 (1991) 213-221
9. Nishiyama N., Katsuki H., Horie K., and Asakura T. Adsorbed behavior of spin-labeled silane coupling agent on colloidal silica studied by electron spin resonance. J Biomed Mater Res A 21 (1987) 1029-1038
10. Ishida H., and Koenig J.L. The reinforcement mechanism of fiber-glass reinforced plastics under wet conditions: a review. Polym Eng Sci 18 (1978) 128
11. Karmaker A., Prasad A., and Sarkar N.K. Characterization of adsorbed silane on fillers used in dental composite restoratives and its effect on composite properties. J Mater Sci: Mater Med 18 (2007) 1157-1162
12. Chen T.M., and Brauer G.M. Solvent effects on bonding organo-silane to silica surfaces. J Dent Res 61 (1982) 1439-1443
13. Halvorson R.H., Erickson R.L., and Davidson C.L. The effect of filler and silane content on conversion of resin-based composite. Dent Mater 19 (2003) 327-333
14. Pflug K, Weber Ch. Dental materials having a nanoscale filler. US. Patent 6,399,037 (2002).
15. Rueggerberg F.A., Hashinger D.T., and Fairhurst C.W. Calibration of FTIR conversion analysis of contemporary dental resin composites. Dent Mater 6 (1990) 241-249
16. Sideridou I.D., Karabela M.M., and Vouvoudi E.Ch. Volumetric dimensional changes of dental light-cured dimethacrylate resins after sorption of water or ethanol. Dent Mater 24 (2008) 1131-1136
17. Pluedemann E.P. Silane coupling agents (1982), Plenum Press, New York
18. Kurata S., and Yamazaki N. Effect of silane coupling agent with various organofunctional and hydrolysable group on silicon and its water-resistance. Jpn J Dent Mater 11 (1992) 916-921
19. Antonucci J.M., Dickens S.H., Fowler B.O., Xu H.H.K., and McDonough W.G. Chemistry of silanes: interfaces in dental polymers and composites. J Res Natl Inst Stand Technol 110 (2005) 541-558
20. Kaas R.L., and Kardos J.L. The interaction of alkoxy silane coupling agents with silica surfaces. Polym Eng Sci 11 (1971) 11-18
21. Miller J.D., and Ishida H. Quantitative monomolecular coverage of inorganic particulates by methacryl-functional silanes. Surf Sci 148 (1984) 601-622
22. Söderholm K-JM, and Shang S.-W. Molecular orientation of silane at the surface of colloidal silica. J Dent Res 72 6 (1993) 1050-1054
23. Jang J., and Kim S. Factors affecting diametral tensile strength of microfilled dental composites. Polym J 28 4 (1996) 293-298
24. Bauer F., Ernst H., Decker U., Findeisen M., Glasel H.-J., Langguth H., et al. Preparation of scratch and abrasion resistant polymeric nanocomposites by monomer grafting onto nanoparticles. 1. FTIR and multi-nuclear NMR spectroscopy to the characterization of methacryl grafting. Macromol Chem Phys 201 (2000) 2654-2659
25. a. Characterization of radiation-cured polymeric nanocomposites. Macromol Chem Phys 201 (2000) 2765-2770
26. Mathias J., and Wannemacher G. Basic characteristics and applications of aerosol. 30. The chemistry and physics of the aerosol surface. J Colloid Interface Sci 125 (1988) 61-68
27. Liu Q., Ding J., Chambers D.E., Debnath S., Wunder S.L., and Baran G.R. Filler-coupling agent-matrix interactions in silica/polymethylmethacrylate composites. J Biomed Mater Res 57 (2001) 384-393
28. Ruyter I.E., and Øysæd H. Composites for use in posterior teeth: composition and conversion. J Biomed Mater Res 21 (1987) 11-23
29. Arkosornnukit M., Takahashi H., and Nishiyama N. Dent Mater J 23 (2004) 31-36
30. Vaidyanathan J., and Vaidyanathan T.K. Flexural creep deformation and recovery in dental composites. J Dent 29 (2001) 545-551
31. Wang J.-Y., and Ploehn H. Dynamic mechanical analysis of the effect of water on glass bead-epoxy composites. J Appl Polym Sci 59 (1996) 345-357
32. Lewis T.B., and Nielsen L.E. Dynamic mechanical properties of particulate-filled composites. J Appl Polym Sci 14 (1970) 1449
33. Amdouni N., Sautereau H., and Gerard J.F. Epoxy composites based on glass beads. I. Viscoelastic properties. J Appl Polym Sci 45 (1992) 1799
34. Hilborn J., Bidaux J.E., and Manson J.A.E. Toughening of glass filled epoxy by in-situ interface control. Polym Prepr 34 (1993) 639
35. Chua P.S. Dynamic mechanical analysis studies of the interface. Polym Comp 8 (1987) 308
36. Dow Corning Corporation, Silane Coupling Agents, Technical Brochure, 1981.
37. Chua P.S., Dai S.R., and Piggott M.R. Mechanical properties of the glass fibre-polyester interphase. J Mater Sci 27 (1992) 919-924
38. Teshima W., Nomura Y., Ikeda A., Kawahara T., Okazaki M., and Nahara Y. Thermal degradation of photo-polymerized BisGMA/TEGDMA-based dental resins. Polym Degradation Stability 84 (2004) 167-172