Effects of LOI of ground bagasse ash on the compressive strength and sulfate resistance of mortars

Construction and Building Materials

Volumn 23, Issue 12, 2009, Pages 3523-3531

  Chusilp, Nuntachai ^a   Jaturapitakkul, Chai ^a   Kiattikomol, Kraiwood ^a  

^a KING MONGKUT'S UNIVERSITY OF TECHNOLOGY THONBURI   (Thailand)

Author keywords

Bagasse ash; Compressive strength; LOI; Mortar; Sulfate resistance

Indexed keywords

LOI; LOSS ON IGNITION; MORTAR BARS; RAW BAGASSE; REPLACEMENT LEVEL; SULFATE ATTACK; SULFATE RESISTANCE;

BAGASSE; BINDERS; CEMENT MANUFACTURE; MORTAR; PLASTER; PORTLAND CEMENT; SUGAR (SUCROSE); SUGAR INDUSTRY; SUGARS;

COMPRESSIVE STRENGTH;

EID: 70349298356     PISSN: 09500618     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.conbuildmat.2009.06.046     Document Type: Article

References (29)

1. ACI Committee 116, ACI 116R-00. Cement and concrete terminology. American Concrete Institute; 2000. 73p.
2. ASTM C 618. Standard specification for coal fly ash and raw or calcined natural pozzolan for use as a mineral admixture in concrete. ASTM C 618-2001. In: Annual book of ASTM standards, vol. 04.02; 2001.
3. Atis C.D. Strength properties of high-volume fly ash roller compacted and workable concrete, and influence of curing condition. Cem Concr Res 35 (2005) 1112-1121
4. Berry EE, Hemmings RT, Langley WS, Carrette GG. Beneficated fly ash: hydration, microstructure, and strength development in Portland cement. In: Proceedings of the first international conference on fly ash, silica fume, slag, and natural pozzolans in concretes, SP-114, Detroit, USA; 1989. p. 241-73.
5. Martirena J.F., Middendorf B., Gehrke M., and Budelmann H. Use of waste of sugar industry as pozzolana in lime-pozzolana binders: study of reaction. Cem Concr Res 28 (1998) 1525-1536
6. Singh N.B., Singh V.D., and Rai S. Hydration of bagasse ash-blended Portland cement. Cem Concr Res 30 (2000) 1485-1488
7. Villar-Cociña E., Valencia-Morales E., González-Rodríguez R., and Hernández-Ruíz J. Kinetics of the pozzolanic reaction between lime and sugar cane straw ash by electrical conductivity measurement: a kinetic-diffusive model. Cem Concr Res 33 (2003) 517-524
8. Villar-Cocina E., Frias Rojas M., and Valencia Morales E. Sugar cane wastes as pozzolanic materials: application of mathematical model. ACI Mater J 105 (2008) 258-264
9. Kantiranis N. Re-cycling of sugar-ash: a raw feed material for rotary kilns. Waste Manage 24 (2004) 999-1004
10. Batra V.S., Urbonaite S., and Svensson G. Characterization of unburned carbon in bagasse fly ash. Fuel 87 (2008) 2972-2976
11. Umamaheswaran K, Batra VS, Bhagavanulu DVS. Development of biomass ash filters for high temperature applications. In: International symposium of research students on materials science and engineering, Chennai, India; 20-22 Decemberm 2004.
12. Frías M., Villar-Cociña E., and Valencia-Morales E. Characterisation of sugar cane straw waste as pozzolanic material for construction: calcining temperature and kinetic parameters. Waste Manage 27 (2007) 533-538
13. Chindaprasirt P., Kanchanda P., Sathonsaowaphak A., and Cao H.T. Sulfate resistance of blended cements containing fly ash and rice husk ash. Construct Build Mater 21 (2007) 1356-1361
14. Ghrici M., Kenai S., and Said-Mansour M. Mechanical properties and durability of mortar and concrete containing natural pozzolana and limestone blended cements. Cem Concr Compos 29 (2007) 542-549
15. Tangchirapat W., Saeting T., Jaturapitakkul C., Kiattikomol K., and Siripanichgorn A. Use of waste ash from palm oil industry in concrete. Waste Manage 27 (2007) 81-88
16. ASTM C 311-00. Standard test method for sampling and testing fly ash or natural pozzolans for use as a mineral admixture in Portland-cement concrete. In: Annual book of ASTM standards, vol. 04.02; 2001. p. 191-9.
17. ASTM C 109-99. Standard test method for compressive strength of hydraulic cement mortars (using 2-in. or [50 mm] cube specimens). In: Annual book of ASTM standards, vol. 04.01; 2001. p. 83-8.
18. ASTM C 230-98. Specification for flow table for use in tests of hydraulic cement. In: Annual book of ASTM standards, vol. 04.01; 2001. p. 203-9.
19. ASTM C 1012-95a. Standard test method for length change of hydraulic-cement mortars exposed to a sulfate solution. In: Annual book of ASTM standards, vol. 04.01; 2001. p. 503-7.
20. Chindaprasirt P., Homwuttiwong S., and Jaturapitakkul C. Strength and water permeability of concrete containing palm oil fuel ash and rice husk-bark ash. Construct Build Mater 21 (2007) 1492-1499
21. Chindaprasirt P., Jaturapitakkul C., and Sinsiri T. Effect of fly ash fineness on microstructure of blended cement paste. Construct Build Mater 21 (2007) 1534-1541
22. Ganesan K., Rajagopal K., and Thangavel K. Evaluation of bagasse ash as supplementary cementitious material. Cem Concr Compos 29 (2007) 515-524
23. Cordeiro G.C., Toledo Filho R.D., and Fairbairn E.M.R. Use of ultra-fine sugar cane bagasse ash as mineral admixture for concrete. ACI Mater J 105 (2008) 487-493
24. Cordeiro G.C., Toledo Filho R.D., Tavares L.M., and Fairbairn E.M.R. Pozzolanic activity and filler effect of sugar cane bagasse ash in Portland cement and lime mortars. Cem Concr Compos 30 (2008) 410-418
25. Moon H.Y., Lee S.T., and Kim S.S. Sulphate resistance of silica fume blended mortars exposed to various sulphate solutions. Canadian J Civ Eng 30 (2003) 625-636
26. Odler I., and Jawed J. Expansion reaction in concrete. In: Skalny J., and Mindess S. (Eds). Materials science of concrete (1989), American Ceramic Society, Westerville (OH)
27. Kalousek G.L., Porter L.C., and Benton E.J. Cement for long-term service in sulfate environment. Cem Concr Res 2 (1972) 79-89
28. Tikalaky P.J., Roy D., Scheetz B., and Krize T. Redefining cement characteristics for sulfate-resistant Portland cement. Cem Concr Res 32 (2002) 1239-1246
29. Jaturapitakkul C., Kiattikomol K., Tangchirapat W., and Saeting T. Evaluation of the sulfate resistance of concrete containing palm oil fuel ash. Contruct Build Mater 21 (2007) 1399-1405