Fatigue of 7075-T651 aluminum alloy under constant and variable amplitude loadings

International Journal of Fatigue

Volumn 31, Issue 11-12, 2009, Pages 1858-1864

  Lee, E U ^a   Glinka, G ^b   Vasudevan, A K ^c   Iyyer, N ^d   Phan, N D ^a  

^a NAVAL AIR WARFARE CENTER AIRCRAFT DIVISION   (United States)

^b UNIVERSITY OF WATERLOO   (Canada)

^c OFFICE OF NAVAL RESEARCH   (United States)

^d Technical Data Analysis Inc   (United States)

Author keywords

Constant and variable amplitude loadings; Fatigue crack growth; Frequency; Load spectrum; Stress ratio

Indexed keywords

CONSTANT AND VARIABLE AMPLITUDE LOADINGS; FATIGUE CRACK GROWTH; FREQUENCY; LOAD SPECTRUM; STRESS RATIO;

ALUMINA; ALUMINUM; ALUMINUM ALLOYS; CRACK DETECTION; CRACKING (CHEMICAL); FATIGUE CRACK PROPAGATION; FATIGUE OF MATERIALS; LOADS (FORCES); SODIUM CHLORIDE; STRESS ANALYSIS;

LOADING;

EID: 68949094319     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2008.11.013     Document Type: Article

References (46)

1. Shen H., Podlaseck S.E., and Kramer I.R. Effect of vacuum on the fatigue life of aluminum. Acta Metall 14 March (1966) 341-346
2. Duquette D.J., and Gell M. The effect of environment on the mechanism of stage I: fatigue fracture. Metall Trans 2 May (1971) 1325-1331
3. Mendez J., and Demulsant X. Influence of environment on low cycle fatigue damage in Ti-6Al-4V and Ti 6246 titanium alloys. Mater Sci Eng A 219 1-2 (1996) 202-211
4. Mendez J. On the effects of temperature and environment on fatigue damage processes in Ti alloys and in stainless steel. Mater Sci Eng A 263 2 (1999) 187-192
5. Jaske C.E., Broek D., Slater J.E., and Anderson W.E. Corrosion fatigue of structural steels in seawater and for offshore applications. Corrosion fatigue technology, ASTM STP 642 (1978), American Society for Testing and Materials 19-47
6. Henaff G., Odemer G., and Tonneau-Morel A. Environmentally-assisted fatigue crack growth mechanisms in advanced materials for aerospace applications. Int J Fatigue 29 (2007) 1927-1940
7. Wei R.P., and Simmons G.W. Recent progress in understanding environment-assisted fatigue crack growth. Int J Fract 17 2 (1981) 235-247
8. Radon J.C., Branco C.M., and Culver L.E. Crack blunting and arrest in corrosion fatigue of mild steel. Int J Fract 12 (1976) 467-469
9. Tu L.K.L., and Seth B.B. Threshold corrosion fatigue crack growth in steels. J Test Eval 6 1 (1978) 66-74
10. Nordmark G.E., and Fricke W.G. Fatigue crack arrest at low stress intensities in a corrosive environment. J Test Eval 6 5 (1978) 301-303
11. Creager M., and Paris P.C. Elastic field equations for blunt cracks with reference to stress corrosion cracking. Int J Fract Mech 3 (1967) 247-252
12. Vitek V. Plane strain intensity factors for branched cracks. Int J Fract 13 (1977) 481-501
13. Vasudevan A.K., and Suresh S. Influence of corrosion deposits on near-threshold fatigue crack growth behavior in 2xxx and 7xxx series aluminum alloys. Metall Trans A 13A (1982) 2271-2280
14. Elber W. The significance of fatigue crack closure. Damage tolerance in aircraft structures ASTM STP 486 (1971), American Society for Testing and Materials 230-242
15. Wheeler O. Spectrum loading and crack growth. J Basic Eng 94 (1972) 181-186
16. Skorupa M. Load interaction effects during fatigue crack growth under variable amplitude loading - a literature review Part II: qualitative interpretation. Fatigue Fract Eng Mater Struct 22 10 (1999) 905-926
17. Pommier S. Cyclic plasticity and variable amplitude fatigue. Int J Fatigue 25 9-11 (2003) 983-997
18. Pommier S., and DeFreitas M. Effect on fatigue crack growth of interactions between overloads. Fatigue Fract Eng Mater Struct 25 (2002) 709
19. Willenborg J, Engle RM, Wood HA. A crack growth retardation model using an effective stress concept. AFFDL-TR71-1. Air Force Flight Dynamic Laboratory, Wright-Patterson Air Force Base; 1971.
20. Wheeler O.E. Spectrum loading and crack growth. J Basic Eng 94 (1972) 181-186
21. Elber W. Fatigue crack closure under cyclic tension. Eng Fract Mech 2 (1970) 37-45
22. Dougdale D.S. Yielding of steel sheets containing slits. J Mech Phys Solids 8 (1960) 100-108
23. Vasudevan A.K., Sadananda K., and Glinka G. Critical parameters for fatigue damage. Int J Fatigue 23 (2001) S39-53
24. Noroozi A.H., Glinka G., and Lambert S.A. A two parameter driving force for fatigue crack growth analysis. Int J Fatigue 27 (2005) 1277-1296
25. Coffin L.F. A study of the effects of cyclic thermal stresses on a ductile metal. Trans ASME 76 (1954) 931-950
26. Manson SS. Behavior of materials under conditions of thermal stress. NACA Report 1170, 1954.
27. Ramberg W, Osgood WR. Description of stress-strain curves by three parameters. NACA, Technical Note No. 902, July 1943.
28. Smith K.N., Watson P., and Topper T.H. A stress-strain function for the fatigue of metals. J Mater, JMLSA 5 4 (1970) 767-778
29. Kirby B.R., and Beever C.J. Slow fatigue crack growth and threshold behaviour in air and vacuum of commercial aluminum alloys. Fatigue Eng Mater Struct 1 (1979) 203-215
30. Vasudevan A.K., and Bretz P.E. Near-threshold fatigue crack growth behavior in 7XXX and 2XXX alloys: a brief review. In: Davidson D.L., and Suresh S. (Eds). Fatigue crack growth threshold concepts (1984), The Metallurgical Society of AIME, Warrendale, PA 25-42
31. Ritchie R.O., Suresh S., and Moss C.M. Near-threshold fatigue crack growth in 2 1/4 Cr-1Mo pressure vessel steel in air and hydrogen. J Eng Mater Technol, ASME Trans 102 (1980) 293-299
32. Stewart A.T. The influence of environment and stress ratio on fatigue crack growth at near threshold stress intensities in low-alloy steels. Eng Fract Mech 13 (1980) 463-478
33. Nakai Y., Tanaka K., and Nakanishi T. The effects of stress ratio and grain size on near-threshold fatigue crack propagation in low-carbon steel. Eng Fract Mech 15 3-4 (1981) 291-302
34. Liaw P.K., Saxena A., Swaminathan V.P., and Shih T.T. Influence of temperature and load ratio on near-threshold fatigue crack growth behavior. In: Davidson D.L., and Suresh S. (Eds). Fatigue crack growth threshold concepts (1984), The Metallurgical Society of AIME, Warrendale (PA) 205-223
35. Liaw P.K., Leax T.R., and Donald J.K. Fatigue crack growth behavior of 4340 steels. Acta Metall 35 7 (1987) 1415-1432
36. th and subsequent crack growth of a low-alloy steel. In: Davidson D.L., and Suresh S. (Eds). Fatigue crack growth threshold concepts (1984), The Metallurgical Society of AIME, Warrendale (PA) 281-298
37. Ritchie R.O. Near-threshold fatigue crack propagation in ultra-high strength steel: influence of load ratio and cyclic strength. J Eng Mater Technol, ASME Trans (1977) 195-204
38. Suresh S., Vasudevan A.K., and Bretz P.E. Mechanisms of slow fatigue crack growth in high strength aluminum alloys: role of microstructure and environment. Metall Trans A 15A (1984) 369-379
39. Lee E.U., Vasudevan A.K., and Sadananda K. Effects of various environments on fatigue crack growth in Laser formed and IM Ti-6Al-4V alloys. Int J Fatigue 27 (2005) 1597-1607
40. Van der Velden R., Ewalds H.L., and Schultze W.A. Anomalous fatigue crack growth retardation in steels for offshore applications. In: Crooker T.W., and Leis B.N. (Eds). Corrosion fatigue, mechanics, metallurgy, electrochemistry, and engineering. ASTM STP 801 (1983), American Society for Testing and Materials 64-80
41. Vasudevan A.K., and Suresh S. Influence of corrosion deposits on near-threshold fatigue crack growth behavior in 2XXX and 7XXX series aluminum alloys. Metall Trans A 13A (1982) 2271-2280
42. Skorupa M. Load interaction effects during fatigue crack growth under variable amplitude loading - a literature review, part I: empirical trends. Fatigue Fract Eng Mater Struct 21 (1998) 987-1006
43. Sadananda K., Vasudevan A.K., Holtz R.L., and Lee E.U. Analysis of overload effects and related phenomena. Int J Fatigue 21 (1999) S233-S246
44. Willenborg S, Eagle RM, Wood HA. A crack growth retardation model using an effective stress concept. AFFDL-TM-FBR-81-1, Air Force Flight Dynamics Laboratory; 1971.
45. Bathias C., and Vancorn M. Mechanisms of overload effect on fatigue crack propagation in aluminum alloys. Eng Fract Mech 10 (1978) 409-424
46. Bretz P.E., Vasudevan A.K., Bucci R.J., and Malcolm R.C. Fatigue crack growth behaviour of 7XXX aluminum alloys under simple variable amplitude loading. Fracture mechanics, fifteenth symposium, ASTM STP 833 (1984), American Society for Testing and Materials 242-265