Tarnishing film-induced brittle cracking of brass

Journal of Materials Research

Volumn 24, Issue 7, 2009, Pages 2409-2415

  Zhang, Cheng ^a   Su, Yan Jing ^a   Qiao, Li Jie ^a   Chu, Wu Yang ^a  

^a UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

Author keywords

[No Author keywords available]

Indexed keywords

APPLIED LOADS; BRASS SUBSTRATES; DEPOSITED FILMS; DUCTILE-MODE; FILM RUPTURE; GALVANIC CURRENT; INTERGRANULAR; LOADING SPEED; MATRIX; MATTSON'S SOLUTION; PERIODIC CURRENT; PLATINUM WIRE; ROOM TEMPERATURE; SLOW STRAIN RATES;

BRASS; PLATINUM; STRAIN RATE; STRESS CORROSION CRACKING;

CRACKS;

EID: 68149131506     PISSN: 08842914     EISSN: None     Source Type: Journal    
DOI: 10.1557/jmr.2009.0289     Document Type: Article

References (14)

1. K. Sieradzki and R.C. Newman: Brittle behavior of ductile metals during stress-corrosion cracking. Philos. Mag. A 51, 95 (1985).
2. K. Sieradzki and R.C. Newman: Stress-corrosion cracking. J. Phys. Chem. Solids 48, 1101 (1987).
3. R.C. Newman, T. Shahrabi, and K. Sieradzki: Film-induced cleavage of alpha-brass. Scr. Metall. 23, 71 (1989).
4. R.G. Kelly, A.J. Frost, J. Shahrabi, and R.C. Newman: Brittle fracture of an Au/Ag alloy induced by a surface film. Metall. Trans. A 22, 531 (1991).
5. J.S. Chen, M. Salmeron, and T.M. Devine: Intergranular vs transgranular stress-corrosion cracking of Cu 30-Au. Scr. Metall. Mater. 26, 739 (1992).
6. A. Devasenapathi, R.C. Prasad, and V.S. Raja: Change in fracture mode and selective dissolution of austenitic stainless steels. Scr. Metall. Mater. 33, 233 (1995).
7. M. Saito, G.S. Smith, and R.C. Newman: Testing the filminduced cleavage model of stress-corrosion cracking. Corros. Sci. 35, 411 (1993).
8. 3Au single crystals. Metall. Trans. A 17, 703 (1986).
9. W.C. Oliver and G.M. Pharr: An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 7, 1564 (1992).
10. R. Nishimura and T. Yoshida: Stress-corrosion cracking of Cu-30% Zn alloy in Mattsson's solutions at pH 7.0 and 10.0 using constant load method-A proposal of SCC mechanism. Corros. Sci. 50, 1205 (2008).
11. J.C. Nelson and R.A. Oriani: Stress generation during anodic oxidation of titanium and aluminum. Corros. Sci. 34, 307 (1993).
12. K. Sieradzki and R.C. Newman: Brittle behaviour of ductile metals during stress-corrosion cracking. Philos. Mag. A 51, 95 (1985).
13. R. Nishimura: Characterization and perspective of stress-corrosion cracking of austenitic stainless steels (type 304 and type 316) in acid solutions using constant load method. Corros. Sci. 49, 81 (2007).
14. J.C. Scully: Stress corrosion crack propagation: A constant charge criterion. Corros. Sci. 15, 207 (1975).