On the degradation the endurance of silicon-rich TRIP800 steel after hot-dip galvanization

Engineering Failure Analysis

Volumn 16, Issue 7, 2009, Pages 2009-2019

  Aden Ali, S ^a   Chamat, A ^a   Gilgert, J ^a   Petit, E J ^b   Dominiak, S ^a   Schmitt, L ^c   Gilles, M ^d   Azari, Z ^a  

^a UNIVERSITÉ DE LORRAINE   (France)

^b UNIVERSITÉ PAUL VERLAINE METZ   (France)

^c UMICORE R and D ^*  (France)

^d UMICORE   (Belgium)

Author keywords

Fatigue properties; Heat treatment; Hot dip galvanization; TRIP steel

Indexed keywords

ADVANCED HIGH STRENGTH STEEL; CYCLIC LOADINGS; FATIGUE LIFETIME; FATIGUE PROPERTIES; HOT-DIP GALVANIZATION; INTERMETALLIC LAYER; MOLTEN ZINC; NEW RESULTS; STEEL SUBSTRATE; STRUCTURAL PARTS; TRIP STEEL; ZINC COATING;

AUTOMOBILE PARTS AND EQUIPMENT; CORROSION FATIGUE; CRACKS; DEGRADATION; DURABILITY; FUEL ECONOMY; MECHANICAL PROPERTIES; PROTECTIVE COATINGS; ZINC;

STEEL;

EID: 67649881322     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2009.04.001     Document Type: Review

References (19)

1. Gambrell J.W. Corrosion. ASM Handbook vol. 13 (1999), ASM, New York p. 436-45
2. Marder A.R. The metallurgy of zinc-coated steel. Prog Mater Sci 45 (2000) 191-271
3. Bicao P., Jianhua W., Xuping S., Zhi L., and Fucheng Y. Effects of zinc bath temperature on the coatings of hot-dip galvanizing. Surf Coat Technol 202 9 (2008) 1785-1788
4. De la Cruz P., and Ericsson T. Influence of hot dip galvanizing on fatigue and corrosion fatigue resistance of a B-Mn steel. Scand J Metall 26 4 (1997) 145-152
5. Reumont G., Vogt J.B., Iost A., and Foct J. The effects of a Fe-Zn intermetallic-containing coating on the stress corrosion cracking behavior of a hot-dip galvanized steel. Surf Coat Technol 139 (2001) 265-271
6. Vogt J.-B., Boussac O., and Foct J. Prediction of fatigue resistance of a hot-dip galvanized steel. Fatigue Fract Eng Mater Struct 24 1 (2001) 33-39
7. Bergengren Y., and Melander A. An experimental and theoretical study of the fatigue properties of hot-dip galvanized high strength sheet steel. Int J Fatigue 14 3 (1992) 154-162
8. Nillson T., Engberg G., and Trogen H. Fatigue properties of hot-dip galvanized steels. Scand J Metall 18 4 (1989) 166-175
9. Nieth F., and Wiegand H. The behaviour of high-strength structural steels after hot-dip galvanizing at dynamic stress. Arch Eisenhüttenwes 46 9 (1975) 589-593
10. Berchem K., and Hocking M.G. The influence of pre-straining on the high-cycle fatigue performance of two hot-dip galvanised car body steels. Mater Charact 58 (2007) 593-602
11. Camurri C.P., Benavente R.G., Roa I.S., and Carrasco C.C. Deformation and fatigue behavior of hot dip galvanized coatings. Mater Charact 55 3 (2005) 203-210
12. Tzimas E., and Papadimitriou G. Cracking mechanisms in high temperature hot-dip galvanized coatings. Surf Coat Technol 145 1-3 (2001) 176-185
13. Henry G., and Horstmann D. De Ferri metallographia, V (1979), Verlag Stahleisen m.b.H., Düsseldorf
14. Li Z., and Wu D. Effect of austempering on transformation induced plasticity of hot rolled multiphase steels. Act Metall Sin 20 1 (2007) 1-8
15. Carpio J., Casado J.A., Alvarez J.A., and Gutierrez-Solana F. Environmental factors in failure during structural steel hot-dip galvanizing. Eng Fail Anal 16 2 (2009) 585-595
16. Bablik H. In: Schubert A, editor. La galvanisation du fer. a chaud, électrolytique, shérardisation, par projection. Dunod;1927.
17. Balloy D., Dauphin J.Y., and Tissier J.C. Study of the comportment of fatty acids and mineral oils on the surface of steel pieces during galvanization. Surf Coat 202 3 (2007) 479-485
18. McCoy R.A., Gerberich W.W., and Zackay V.F. On the resistance of TRIP steel to hydrogen embrittlement. Metall Mater Trans 15 7 (1970) 2031-2034
19. Azari Z., Abbadi M., Moustabchir H., and Lebienvenu M. The influence of fatigue cycling on the oxidation kinetics and crack initiation of a Cr-Mo steel. Int J Fatigue 30 3 (2007) 517-527