Ultrasonic detection of fretting fatigue damage at bolt joints of aluminum alloy plates

International Journal of Fatigue

Volumn 31, Issue 8-9, 2009, Pages 1378-1385

  Wagle, Sanat ^a   Kato, Hiroshi ^a  

^a SAITAMA UNIVERSITY   (Japan)

Author keywords

Aluminum alloy; Bolt joint; Fretting fatigue; Non destructive testing; Ultrasonic measurement

Indexed keywords

2024-T3; BOLT HOLES; FATIGUE FAILURES; FATIGUE LIFE; FATIGUE LIFE DIAGRAM; FRETTING FATIGUE; FRETTING FATIGUE CRACKS; FRETTING FATIGUE DAMAGE; FRETTING FATIGUES; FRETTING WEAR; MECHANICAL FATIGUE; NON-DESTRUCTIVE TESTING; SPECIMEN SURFACES; STRESS AMPLITUDES; SURFACE ACOUSTIC WAVES; TIGHTENING TORQUE; ULTRASONIC DETECTION;

ACOUSTIC SURFACE WAVE DEVICES; ACOUSTIC WAVES; ALUMINA; ALUMINUM; ALUMINUM ALLOYS; ALUMINUM METALLURGY; BOLT TIGHTENING; BOLTED JOINTS; CRACK DETECTION; CRACKS; DAMAGE DETECTION; FAILURE ANALYSIS; FATIGUE DAMAGE; FRETTING CORROSION; NONDESTRUCTIVE EXAMINATION; STRESSES; SURFACE TESTING; TORQUE; ULTRASONIC MEASUREMENT; ULTRASONIC TESTING; ULTRASONICS;

FATIGUE TESTING;

EID: 67349264441     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2009.03.017     Document Type: Article

References (36)

1. Steadman D, Ramakrishnan R. Simulation of multiple site damage growth. In: 9th joint FAA/DoD/NASA aging aircraft conf, Atlanta GA; March 2006.
2. A report of the Airworthiness Assurance Working Groups. Widespread fatigue damage bridging tasks. Multiple element damage, July 23; 2003. p. 15-57.
3. Terada H. Structural fatigue and joint degradation. Int J Fatigue 23 (2001) S21-S30
4. Szolwinski M.P., and Farris T.N. Observation, analysis and prediction of fretting fatigue in 2024-T351 aluminum alloy. Wear 221 (1998) 24-36
5. Shinde S.R., and Hoeppner D.W. Fretting fatigue behaviour in 7075-T6 aluminum alloy. Wear 261 (2006) 426-434
6. Elliott III C.B., and Hoeppner D.W. The importance of wear and corrosion on the fretting fatigue behavior of two aluminum alloys. Wear 236 (1999) 128-133
7. Chen Y.K., Han L., Chrysanthou A., and O'Sullivan J.M. Fretting wear in Self piercing riveted aluminum alloy sheet. Wear 255 (2003) 1463-1470
8. Munoz S., Proudhon H., Dominguez J., and Fouvry S. Prediction of the crack extension under fretting wear loading conditions. Int J Fatigue 28 (2006) 1769-1779
9. Mi{dotless}nguez J.M., and Vogwell J. Effect of torque tightening on the fatigue strength of bolted joints. Eng Fail Anal 13 (2006) 1410-1421
10. Dominguez J. Cyclic variations in friction forces and contact stress during fretting fatigue. Wear 218 (1998) 43-53
11. Alderliesten R.C., Hagenbeek M., Homan J.J., Hooijmeijer P.A., De Vries T.J., and Vermeeren C.A.J.R. Fatigue and damage tolerence of glare. Appl Compos Mater 10 (2003) 223-242
12. Nakazawa K., Maruyama N., and Hanawa T. Effect of contact pressure on fretting fatigue of austenitic stainless steel. Tribol Int 36 (2003) 79-85
13. Naidu N.K.R., and Raman S.G.S. Effect of contact pressure on fretting fatigue behavior of Al-Mg-Si alloy AA6061. Int J Fatigue 27 (2005) 283-291
14. Arora P.R., Jacob M.S.D., Salit M.S., Ahmed E.M., Saleem M., and Edi P. Experimental evaluation of fretting fatigue test apparatus. Int J Fatigue 29 (2007) 941-952
15. Cortez R., Mall S., and Calcaterra J.R. Investigation of variable amplitude loading on fretting fatigue behavior of Ti-6Al-V. Int J Fatigue 21 (1999) 709-717
16. Nishioka K., and Hirakawa K. Fundamental investigation of fretting fatigue. Bull Jpn Soc Mech Eng 15 (1972) 135-144
17. Adibnazari S., and Hoeppner D.W. A fretting fatigue normal pressure threshold concept. Wear 160 (1993) 33-35
18. Osegueda R, Kreinovich V, Nazarian S, Roldan E. Detection of cracks at rivet hole in thin plates using lamb wave scanning. El Paso, Texas: The University of Texas; 79968.
19. Chang Z., and Mal A. Scattering of Lamb waves from a rivet hole with edge cracks. Mech Mater 31 (1999) 197-204
20. Mi B., Micheals J.E., and Michaels T.E. An ultrasonic method for dynamic monitoring of Fatigue crack initiation and growth. J Acoust Soc Am 119 (2006) 74-85
21. Micheals J.E., Michaels T.E., and Mi B. An ultrasonic Angle beam method for in situ sizing of fastener hole. J Nondestruct Eval 25 1 (2006) 3-16
22. Chiou C.P., Martegetan F.J., and Bose J.H. Ultrasonic detection of cracks below bolts in aircraft skin. QNDE 10B (1991) 1891-1897
23. Akanda M.A.S., and Saka M. Ultrasonic shear wave technique for sensitive detection and sizing of small closed cracks. JSME Int J, Ser A 45 2 (2002) 252-261
24. Saka M., and Akanda M.A.S. Ultrasonic measurement of crack depth crack opening stress intensity factor under a no load condition. J Nondestruct Eval 23 2 (2004) 49-63
25. Akanda M.A.S., and Saka M. Relation between closure stress of small fatigue crack and ultrasonic response. J Nondestruct Eval 23 2 (2004) 37-47
26. Ahmed S.R., and Saka M. Influence of wall thickness on the ultrasonic evaluation of small closed surface cracks and quantitative NDE. J Nondestruct Eval 21 1 (2002) 37-47
27. Kim J.-Y., and Rokhlin S.I. Surface acoustic wave measurements of small fatigue cracks initiated from a surface cavity. Int J Solids Struct 39 (2002) 1487-1504
28. Kim Y.H., Song S.-J., Bae D.H., and Kwon S.-D. Assessment of material degradation due to corrosion-fatigue using a backscattered Rayleigh surface wave. Ultrasonics 42 (2004) 545-550
29. Cook D.A., and Berthelot Y.H. Detection of small surface breaking crack in steel using scattering of Rayleigh waves. NDT&E Int 34 (2001) 483-492
30. Lawlor V.P., McCarthy M.A., and Stanley W.F. An experimental study of bolt hole clearance effects in the double-lap, multi-bolt composite joints. Compos Struct 71 (2005) 176-190
31. McCarthy M.A., Lawlor V.P., Stanley W.F., and McCarthy C.T. Bolt hole clearance effects and strength criteria in single-bolt, single-lap, composite bolted joints. Compos Sci Technol 62 (2002) 1415-1431
32. Min X., and Kato H. Change in ultrasonic parameters with loading/unloading process in cyclic loading of aluminum alloy. Mater Sci Eng A 372 1-2 (2004) 269-277
33. Suresh S. Fatigue of materials. 2nd ed. (1998), Cambridge University Press, UK p. 466-73
34. Shigley J.E., and Mischke C.R. Mechanical engineering design. 5th ed. (1989), McGraw-Hill, Singapore p. 345-346
35. Szolwinski M.P., and Farris T.N. Mechanics of fretting fatigue crack formation. Wear 221 (1998) 24-36
36. Lykins C.D., Mall S., and Jain V. An evaluation parameter for predicting fretting fatigue crack initiation. Int J Fatigue 22 (2000) 706-716