Corrosion behaviour of several aluminium alloys in contact with a thermal storage phase change material based on Glauber's salt

Corrosion Science

Volumn 51, Issue 6, 2009, Pages 1263-1272

  Garcia Romero A ^a   Delgado, A ^a   Urresti, A ^a   Martin K ^a   Sala, J M ^a  

^a UNIVERSITY OF THE BASQUE COUNTRY UPV EHU   (Spain)

Author keywords

A. Aluminium; B. SEM; B. XRD; C. Alkaline corrosion; C. Pitting corrosion

Indexed keywords

A. ALUMINIUM; B. SEM; B. XRD; C. ALKALINE CORROSION; C. PITTING CORROSION;

ALUMINUM; ALUMINUM ALLOYS; CORROSIVE EFFECTS; HEAT STORAGE; PHASE CHANGE MATERIALS; PITTING; X RAY DIFFRACTION; X RAY DIFFRACTION ANALYSIS;

ALUMINUM CORROSION;

EID: 67349221749     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2009.03.006     Document Type: Article

References (17)

1. Abhat A. Low temperature latent heat thermal energy storage materials: heat storage materials. Solar Energy 30 (1983) 313-332
2. Porosini F.C. Salt hydrates used for latent heat storage: corrosion of metals and reliability of thermal performance. Solar Energy 41 (1988) 193-197
3. Groll M., Brost O., and Heine D. Corrosion of steels in contact with salt eutectics as latent heat storage materials: influence of water and other impurities. Heat Recov. Syst. CHP 10 (1990) 567-572
4. Cabeza L.F., Illa J., Roca J., Badia F., Mehling H., Hiebler S., and Ziegler F. Immersion corrosion tests on metal-salt hydrate pairs used for latent heat storage in the 32 to 36 Deg temperature range. Mater. Corros. 52 (2001) 140-146
5. Cabeza L.F., Illa J., Roca J., Badia F., Mehling H., Hiebler S., and Ziegler F. Middle term immersion corrosion tests on metal-salt hydrate pairs used for latent heat storage in the 32 to 36 Deg temperature range. Mater. Corros. 52 (2001) 748-754
6. Cabeza L.F., Roca J., Nogués M., Mehling H., and Hiebler S. Immersion corrosion tests on metal-salt hydrate pairs used for latent heat storage in the 48 to 58 DegC temperature range. Mater. Corros. 53 (2002) 902-907
7. Nagano K., Ogawa K., Mochida T., Hayashi K., and Ogoshi H. Performance of heat charge/discharge of magnesium nitrate hexahydrate and magnesium chloride hexahydrate mixture to a single vertical tube for a latent heat storage system. Appl. Therm. Eng. 24 (2004) 209-220
8. Cabeza L.F., Roca J., Nogueés M., Mehling H., and Hiebler S. Long term immersion corrosion tests on metal-PCM pairs used for latent heat storage in the 24 to 29 DegC temperature range. Mater. Corros. 56 (2005) 33-38
9. Farrell AJ., Norton B., and Kennedy D.M. Corrosive effects of salt hydrate phase change materials used with aluminium and copper. J. Mater. Process. Tech. 175 (2006) 198-205
10. Blanc C., Lavelle B., and Mankowski G. The role of precipitates enriched with copper on the susceptibility to pitting corrosion of the 2024 aluminium alloy. Corros. Sci. 39 (1997) 495-510
11. J. Moran, Effects of metallurgical variables on the corrosion of aluminum alloys in: ASM Handbook, vol. 13A, Corrosion: Fundamentals, Testing, and Protection, ASM International, 2003, pp. 275-278.
12. Bakos I., and Szabo S. Corrosion behaviour of aluminium in copper containing environment. Corros. Sci. 50 (2008) 200-205
13. J.G. Kaufman, Corrosion of aluminum and aluminum alloys, in: ASM Handbook, vol. 13B, Corrosion: Materials, ASM International, 2005, pp. 95-124.
14. G.S. Frankel, Pitting corrosion, in: ASM Handbook, vol. 13A, Corrosion: Fundamentals, Testing, and Protection, ASM International, 2003, pp. 236-241.
15. Szklarska-Smialowska Z. Pitting corrosion of aluminum. Corros. Sci. 41 (1999) 1743-1767
16. Zhang X., Wen Z., Gu Z., Xu X., and Lin Z. Hydrothermal synthesis and thermodynamic analysis of dawsonite-type compounds. J. Sol. State Chem. 177 (2004) 849-855
17. 4 and NaCl on the atmospheric corrosion of aluminum. Corros. Sci. 48 (2006) 1848-1866