Ageing behavior of acrylic polyurethane varnish coating in artificial weathering environments

Progress in Organic Coatings

Volumn 65, Issue 4, 2009, Pages 504-509

  Hu, Jianwen ^a,b   Li, Xiaogang ^b   Gao, Jin ^b   Zhao, Quanlin ^b,c  

^a HEBEI UNIVERSITY OF SCIENCE AND TECHNOLOGY   (China)

^b UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING   (China)

^c PEKING UNIVERSITY   (China)

Author keywords

Acrylic polyurethane varnish; Artificial weathering environments; FTIR; Low frequency impedance

Indexed keywords

AGEING BEHAVIOR; AGEING TIME; ARTIFICIAL WEATHERING ENVIRONMENT; ARTIFICIAL WEATHERING ENVIRONMENTS; FTIR; FTIR ANALYSIS; LOW FREQUENCY IMPEDANCE; SCANNING ELECTRON MICROSCOPES; THICKNESS GAUGE; THICKNESS LOSS; TIME PERIODS; UV EXPOSURE; VARNISH COATING; WEATHERING EQUIPMENT; XENON LAMPS;

COATINGS; ELECTRIC LAMPS; ELECTROCHEMICAL CORROSION; ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY; EROSION; FOURIER TRANSFORM INFRARED SPECTROSCOPY; SCANNING ELECTRON MICROSCOPY; SPECTROSCOPIC ANALYSIS; VARNISH; XENON;

WEATHERING;

EID: 67349200315     PISSN: 03009440     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.porgcoat.2009.05.002     Document Type: Article

References (19)

1. In: Hamid S.H., Amin M.B., and Maddhah A.G. (Eds). Handbook of Polymer Degradation (1992), Marcel Dekker, New York
2. He Y., Yuan J.P., Cao H., et al. Characterization of photo-degradation of a polyurethane coating system by electron spin resonance. Prog. Org. Coat. 42 1-2 (2001) 75-81
3. Perrin F.X., Irigoyen M., Aragon E., et al. Artificial aging of acrylurethane and alkyd paints: a micro-ATR spectroscopic study. Polym. Degrad. Stab. 70 3 (2000) 469-475
4. Perrin F.X., Irigoyen M., Aragon E., et al. Evaluation of accelerated weathering tests for three paint systems: a comparative study of their aging behavior. Polym. Degrad. Stab. 72 1 (2001) 115-124
5. Jacques L.F.E. Accelerated and outdoor/natural exposure testing of coatings. Prog. Polym. Sci. 25 9 (2000) 1337-1362
6. Yang X.F., Tallman D.E., Bierwagen G.P., et al. Blistering and degradation of polyurethane coatings under different accelerated weathering tests. Polym. Degrad. Stab. 77 1 (2002) 103-109
7. Wernstihl K.M. Service life prediction of automotive coatings, correlating infrared measurements and gloss retention. Polym. Degrad. Stab. 54 1 (1996) 57-65
8. Irigoyen M., Aragon E., Perrin F.X., et al. Effect of UV aging on electrochemical behavior of an anticorrosion paint. Prog. Org. Coat. 59 3 (2007) 259-264
9. Johnson B.W., and McIntyre R. Analysis of test methods for UV durability predictions of polymer coatings. Prog. Org. Coat. 27 1 (1996) 95-106
10. Wood K.A. Optimizing the exterior durability of new fluoropolymer coatings. Prog. Org. Coat. 43 1 (2001) 207-213
11. Singh R.P., Namrata S.T., and Bhadraiah S.V. Photo-oxidation studies on polyurethane coating: effect of additives on yellowing of polyurethane. Polym. Degrad. Stab. 73 3 (2001) 443-446
12. Halt A., and Ranby B. Photo-stability of photo-cured organic coating part-1: secondary reaction in thioxanthane/amine photo-cured organic coating. Polym. Degrad. Stab. 8 1 (1984) 75-87
13. Halt A., and Ranby B. Photo-stability of photo-cured organic coating part-IV: interaction between photo-initiator and photo-stabilizers in photo-curing reaction. Polym. Degrad. Stab. 9 1 (1984) 1-13
14. Yang X.F., Vangb C., Tallmana D.E., et al. Weathering degradation of a polyurethane coating. Polym. Degrad. Stab. 74 2 (2001) 341-351
15. 2O multidimensional spectroscopic studies. Langmuir 16 12 (2000) 5382-5390
16. Armsteron R.D., Jenkins A.T.A., and Johnson B.W. An investigation into the UV breakdown of thermoset polyester coatings using impedance spectroscopy. Corros. Sci. 37 10 (1995) 1615-1625
17. Nichols M.E., Gerlock J.L., and Smith C.A. Rates of photooxidation induced crosslinking and chain scission in thermoset polymer coatings-I. Polym. Degrad. Stab. 56 1 (1997) 81-91
18. Bierwagen G.P., Tallman G.P., Li G.P.D.J., et al. EIS studies of coated metals in accelerated exposure. Prog. Org. Coat. 46 2 (2003) 148-157
19. Vogelsang J., and Strunz W. New interpretation of electrochemical data obtained from organic barrier coatings. Electrochim. Acta 46 24-25 (2001) 3817-3826