Damage characterisation of fibre metal laminates under interlaminar shear load

Composites Part A: Applied Science and Manufacturing

Volumn 40, Issue 6-7, 2009, Pages 925-931

  Hinz, Stephan ^a   Omoori, Toshihiro ^b   Hojo, Masaki ^b   Schulte, Karl ^a  

^a HAMBURG UNIVERSITY OF TECHNOLOGY   (Germany)

^b KYOTO UNIVERSITY   (Japan)

Author keywords

A. Layered structures; B. Fibre matrix bond; D. Mechanical testing; Interlaminar shear properties

Indexed keywords

A. LAYERED STRUCTURES; B. FIBRE/MATRIX BOND; CHARACTERISATION; CROSS-PLY; D. MECHANICAL TESTING; DAMAGE AND FAILURE; FIBRE METAL LAMINATES; HIGH STRESS CONCENTRATION; IN-SITU; INTERLAMINAR SHEAR; INTERLAMINAR SHEAR PROPERTIES; INTERLAMINAR SHEAR STRENGTH; SEM; SINGLE EVENT; STRESS VALUES;

DEBONDING; FIBERS; FUSELAGES; LAMINATES; MECHANICAL ENGINEERING; MECHANICAL TESTING; SCANNING ELECTRON MICROSCOPY; SHEAR STRAIN; STRESS CONCENTRATION;

SHEAR STRENGTH;

EID: 67349109708     PISSN: 1359835X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compositesa.2009.04.020     Document Type: Article

References (18)

1. Vogelesang L.B., and Vlot A. Development of fibre metal laminates for advanced aerospace structures. J Mater Process Technol 103 1 (2000) 1-5
2. Marissen R. Fatigue crack growth in ARALL - a hybrid aluminium-aramid composite material. Deutsche Forschungs- und Versuchsanstalt für Luft- und Raumfahrt e.V. (DFVLR); 1989.
3. Roebroeks GHJJ. Towards GLARE - the development of a fatigue insensitive and damage tolerant aircraft material. PhD thesis, Delft University of Technology; 1991.
4. De Vries TJ. Blunt and sharp notch behaviour of Glare laminates. PhD thesis, Delft University of Technology; 2001.
5. Verolme K. The development of a design tool for fibre metal laminate compression panels. PhD thesis, Delft University of Technology; 1995.
6. Wittenberg T.C., and Jansen E.L. Stability. Fibre metal laminates - an introduction (2001), Kluwer Academic Publishers 133-153
7. Wittenberg T.C., van Baten T.J., and de Boer A. Design of fibre metal laminate shear panels for ultra-high capacity aircraft. Aircraft Des 4 (2001) 99-113
8. Botelho E.C., Silva R.A., Pardini L.C., and Rezende M.C. Evaluation of adhesion of continuous fiber-epoxy composite/aluminum laminates. J Adhes Sci Technol 18 15 (2004) 1799-1813
9. De Jong TW, Sinke J. Interlaminar shear failure in fiber metal laminates. In: Processing and fabrication of advanced materials, vol. X; 2001. p. 493-501.
10. ®4B under interlaminar shear loading at different temperature conditions. Adv Compos Lett 14 2 (2005) 47-55
11. Fiedler B., Hojo M., Ochiai S., Schulte K., and Ochi M. Finite-element modelling of initial matrix failure in CFRP under static transverse load. Compos Sci Technol 61 (2001) 95-105
12. Hobbiebrunken T., Hojo M., Adachi T., DeJong C., and Fiedler B. Evaluation of interfacial strength in CF/epoxies using FEM and in-situ experiments. Composites Part A 54 (2006) 90 [online available]
13. ® at elevated temperatures. Comp Mater Sci 39 (2007) 142-148
14. Corletto C.R., Bradley W.L., and Brinson H.F. An experimental micromechanics measurement technique for submicrometre domains. J Mater Sci 31 (1996) 1803-1808
15. Castrodeza E.M., Bastian F.L., Yawny A., and Perez Ipiña J.E. Fracture micromechanisms of fibre-metal laminates: in-situ SEM observations. J Compos Mater 36 04 (2002) 387-400
16. Hobbiebrunken T., Fiedler B., Hojo M., and Tanaka M. Experimental determination of the true epoxy resin strength using micro-scaled specimens. Composites Part A 38 3 (2007) 814-818
17. Fiedler B., Hojo M., Ochiai S., Schulte K., and Ando M. Failure behavior of an epoxy matrix under different kinds of static load. Compos Sci Technol 61 (2001) 1615-1624
18. Hobbiebrunken T. Microscopic transverse failure initiation in composite materials. Diss., Kyoto University, Japan; 2005.