Fretting-fatigue behaviour of bridge engineering cables in a solution of sodium chloride

Wear

Volumn 267, Issue 1-4, 2009, Pages 308-314

  Perier V ^a   Dieng, L ^a   Gaillet, L ^a   Tessier, C ^a   Fouvry, S ^b  

^a UNIVERSITÉ GUSTAVE EIFFEL   (France)

^b LABORATOIRE DE TRIBOLOGIE ET DYNAMIQUE DES SYSTÈMES   (France)

Author keywords

Cable; Corrosion; Fatigue; Fretting; Steel wires

Indexed keywords

BRIDGE ENGINEERING; CONTACT CONDITIONS; CORROSION PRODUCTS; EXPERIMENTAL TEST; FATIGUE; FATIGUE BEHAVIOUR; FATIGUE TESTS; FRACTURE SURFACES; FREE-BENDING; FRETTING; LIFE SPAN; NACL SOLUTION; PARTIAL SLIP; SPIRAL STRANDS; STEEL WIRE; STEEL WIRES; TANGENTIAL FORCE; ZINC COATING;

BENDING TESTS; BRIDGE CABLES; CORROSION; FATIGUE DAMAGE; FATIGUE TESTING; PROTECTIVE COATINGS; RAILROAD BRIDGES; SODIUM; SODIUM CHLORIDE; STEEL; TESTING; WIRE; ZINC;

CORROSION FATIGUE;

EID: 65749091877     PISSN: 00431648     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.wear.2008.12.107     Document Type: Article

References (15)

1. Walton J.M. Developments in steel cables. Journal of Constructional Steel Research 39 1 (1996) 3-29
2. Raoof M. Wire recovery length in a helical strand under axial-fatigue load. International Journal of Fatigue 13 2 (1991) 127-132
3. Fouvry S., Kapsa Ph., Vincent L., and Dang Van K. Theoretical analysis of fatigue cracking under dry friction for fretting loading conditions. Wear 195 (1996) 21-34
4. Siegert D., Royer J., and Brevet P. Fretting fatigue in steel stay cables. International Symposium on Fretting. China (1997)
5. Zhou Z.R., Nakazawa K., Zhu M.H., Maruyama N., Kapsa Ph., and Viencent L. Progress in fretting maps. Tribology International 39 (2006) 1068-1073
6. Siegert D. Initiation of fretting fatigue cracks in spiral multilayer strands. OIPEEC Bulletin 78 (1999) 27-44
7. Dieng L., Périer V., and Tessier C. Degradation mechanisms and protective methods of civil engineering cables - Example of stay cables. Journées AUM : Activités Universitaires en Mécanique/AFM : Association Française de Mécanique, National Congress Proceedings (2008)
8. Brevet P., and Siegert D. Comportement à la fatigue de torons de précontrainte soumis à la flexion. Bulletin de Liaison des Laboratoires des Ponts et Chaussées 187 (1993) 45-50 ISSN 0458-5860
9. ASTM, Standard practice for laboratory immersion corrosion testing of metals, G 31-72 (reapproved 2004).
10. ASTM, Standard practice for exposure of metals and alloys by alternate immersion in neutral 3.5% sodium chloride solution, G 44-99 (reapproved 2005).
11. AFNOR, Corrosion des métaux et alliages - Essai en immersions alternées en solution saline, NF EN ISO 11130, 1999.
12. ASTM, Standard practice for modified salt spray (fog) testing, G 85-02.
13. J.R. Urvoy, D. Siegert, L. Dieng, P. Brevet, Influence des revêtements métalliques et des lubrifiants sur la fatigue des contacts interfilaires de câbles, Congrès Français de Mécanique, 2005.
14. Dieng L., Urvoy J.R., Siegert D., Brevet P., Périer V., and Tessier C. Assessment of lubrication and zinc coating on the high cycle fretting fatigue behaviour of high strength steel wires. OIPEEC Conference. Johannesburg (2007) 85-97
15. D. Siegert, Mécanismes de fatigue de contact dans les câbles de haubanage du Génie Civil, Ph.D. Thesis, 1997.