Stop drilling procedure for fatigue life improvement

International Journal of Fatigue

Volumn 26, Issue 12, 2004, Pages 1333-1339

  Song, P S ^a   Shieh, Y L ^b  

^a DAHAN INSTITUTE OF TECHNOLOGY   (Taiwan)

^b NATIONAL DEFENSE UNIVERSITY   (Taiwan)

Author keywords

Crack initiation life; Fatigue notch factor; Stophole; Total fatigue life

Indexed keywords

ALUMINUM ALLOYS; COMPRESSIVE STRESS; CRACK INITIATION; FATIGUE OF MATERIALS; FINITE ELEMENT METHOD; RESIDUAL STRESSES; STAINLESS STEEL;

CRACK INITIATION LIFE; FATIGUE NOTCH FACTOR; STOPHOLE; TOTAL FATIGUE LIFE;

DRILLING;

EID: 6344221430     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2004.04.009     Document Type: Article

References (22)

1. Domazet Ž. Comparison of fatigue crack retardation methods. Engng Failure Analysis. 3:(2):1996;137-147.
2. Broek D. Elementary engineering fracture mechanics. 4th ed. 1986;445-449 Martinus Nijhoff, The Hague.
3. Song P.S., Hwang S., Shin C.S. Effect of artificial closure materials on crack growth retardation. Engng Fract Mech. 60:(1):1998;47-58.
4. Song P.S., Sheu B.C., Chou H.H. Deposition of plating metals to improve crack growth life. Int J Fatigue. 23:2001;259-270.
5. Shin C.S., Cai C.Q. A model for evaluating the effect of fatigue crack repair by the infiltration method. Fatigue Fract Engng Mater Struct. 23:2000;835-845.
6. Schubbe J.J., Mall S. Investigation of a cracked thick aluminum panel repaired with a bonded composite patch. Engng Fract Mech. 63:1999;305-323.
7. Baker A.A. Repair efficiency in fatigue-cracked aluminium components reinforced with boron/epoxy patches. Fatigue Fract Engng Mater Struct. 16:(7):1993;753-765.
8. Linnert G.E. Welding metallurgy. vol 2:1967;American Welding Society, New York.
9. Novotny L.G. Overstressing of pressure vessels to increase service life. Proc Inst Mech Engrs UK. C268/86:1986;249-256.
10. Vardar Ö. Effect of single overload in FCP. Engng Fract Mech. 30:(3):1988;329-335.
11. Miyagawa H., Nisitani H. Retardation of fatigue crack propagation due to additional holes or indentations in plate specimens. Bull JSME. 28:(244):1985;2219-2223.
12. Song P.S., Sheu G.L. Retardation of fatigue crack propagation by indentation technique. Int J Pressure Vessels Piping. 79:2002;725-733.
13. Buxbaum O., Huth H. Expansion of cracked fastener holes as a measure for extension of lifetime to repair. Engng Fract Mech. 28:(5/6)):1987;689-698.
14. Ball D.L., Lowry D.R. Experimental investigation on the effects of cold expansion of fastener holes. Fract Engng Mater Struct. 21:1998;17-34.
15. Goto M., Miyagawa H., Nisitani H. Crack growth arresting property of a hole and brinell-type dimple. Fatigue Fract Engng Mater Struct. 19:(1):1996;39-49.
16. Ghfiri R., Amrouche A., Imad A., Mesmacque G. Fatigue life estimation after crack repair in 6005 A-T6 aluminium alloy using the colding expansion hole technique. Fatigue Fract Engng Mater Struct. 23:2000;911-916.
17. Shin C.S., Wang C.M., Song P.S. Fatigue damage repair: a comparison of some possible methods. Int J Fatigue. 18:(8):1996;535-546.
18. Tanaka K., Nakai Y., Kawashima R. Fracture mechanics approach to fatigue crack initiation from deep notches. Engng Fract Mech. 18:(5):1983;1011-1023.
19. Peterson R.E. Notch sensitivity. Sines G., Waisman J.L. Metal fatigue. 1959;McGraw-Hill, New York.
20. Li Q.S., Cai Q.G., Chen X.X. J-integral analysis of notch fatigue crack initiation. Acta Mechanica. 5:1982;488-495. [in Chinese].
21. ASTM E647-88a Standard test method for measurement of fatigue crack growth rates. Annual book of ASTM standards, 1995, 03.01.
22. Dowling NE. Fatigue at notches and the local strain and fracture mechanics approaches. ASTM STP 677, 1979. p. 247-73.