A comparative study of V2O5/AC and V2O5/Al2O3 catalysts for the selective catalytic reduction of NO by NH3

Chemical Engineering Journal

Volumn 149, Issue 1-3, 2009, Pages 173-182

  Boyano, A ^a   Lazaro M J ^a   Cristiani, C ^b   Maldonado Hodar, F J ^c   Forzatti, P ^b   Moliner, R ^a  

^a INSTITUTO DE CARBOQUÍMICA   (Spain)

^b POLITECNICO DI MILANO   (Italy)

^c UNIVERSITY OF GRANADA   (Spain)

Author keywords

Alumina; Carbon coated catalysis; SCR NH3 of NO; Washcoat

Indexed keywords

ALUMINA COATINGS; CARBON-COATED MONOLITHS; CERAMIC HONEYCOMBS; CERAMIC MONOLITHS; COATED SAMPLES; COMPARATIVE STUDIES; DIP-COATING METHODS; KEY PARAMETERS; LOW TEMPERATURES; MECHANICAL STRENGTHS; NO CONVERSIONS; NO REDUCTIONS; SCR-NH3 OF NO; SELECTIVE CATALYTIC REDUCTION OF NO; SLURRY VISCOSITIES; TEMPERATURE RESISTANCES; WASHCOAT; WASHCOATS;

CATALYSTS; CERAMIC COATINGS; CERAMIC MATERIALS; MECHANICAL PROPERTIES; MONOLITHIC INTEGRATED CIRCUITS; REDUCTION;

SELECTIVE CATALYTIC REDUCTION;

EID: 63349105802     PISSN: 13858947     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.cej.2008.10.022     Document Type: Article

References (41)

1. Iwamoto M., and Hamada H. Removal of nitrogen monoxide from exhaust gases through novel catalytic processes. Catal. Today 10 (1991) 57-71
2. Hamada H., Kintaichi Y., Yoshinari T., Tabata M., Sasaki M., and Ito T. Performance of solid acid type catalysts for the selective reduction of nitrogen oxides by hydrocarbons and alcohols. Catal. Today 17 (1993) 111-119
3. Bosch H., and Janssen F. Catalytic reduction of nitrogen oxides-a review on the fundamentals and technology. Catal. Today 2 (1988) 369-529
4. x emissions from automotive diesel engines. Catal. Today 59 (2000) 335-345
5. A. Cybulski, J.A. Moulijn, Structured Catalysts and Reactors. Ed. Taylor, 2006.
6. Meille V. Review on methods to deposit catalysts on structured surfaces. Appl. Catal. A: Gen. 315 (2006) 1-17
7. Weckhuysen B.M., and Keller D.E. Chemistry, spectroscopy and the role of supported vanadium oxides in heterogeneous catalysis. Catal. Today 78 (2003) 25-46
8. 3 catalysts: IR and TPD studies. J. Mol. Catal. A: Chem. 104 (1995) 87-94
9. 3. Appl. Catal. B: Environ. 7 (1996) 337-357
10. 5 catalysts. J. Catal. 221 (2004) 93-101
11. Avila P., Montes M., and Miró E.E. Monolithic reactors for environmental applications: a review on preparation technologies. Chem. Eng. J. 109 (2005) 11-36
12. 3 over an activated carbon-supported copper oxide catalyst at low temperatures. Appl. Catal. B: Environ. 26 (2000) 25-35
13. x removal in nitric-acid plant gaseous effluents. Atmos. Environ. Part A: Gen. Topics 27 (1993) 443-447
14. 3 washcoat deposited on a ceramic honeycomb. Surf. Coat. Technol. 19 (2005) 314-320
15. Jia L., Shen M., and Wang J. Preparation and characterization of dip-coated γ-alumina based ceramic materials on FeCrAl foils. Surf. Coat. Technol. 201 (2007) 7159-7165
16. Collic M., and Morse D. Effects of amplitude of the radiofrequency electromagnetic radiation on aqueous suspensions and solutions. J. Colloid Interface Sci. 200 (1998) 265-272
17. Collic M., and Fisher M.L. Effect of the size and affinity for water of excluded ions on interparticle forces. Chem. Phys. Lett. 291 (1998) 24-30
18. 2 over vanadium supported on mesoporous carbon-coated monoliths for the SCR of NO at low temperature. Catal. Today 102 (2005) 177-182
19. Garcia-Bordeje E., Kapteijn F., and Moulijn J.A. Preparation and characterization of carbon-coated monoliths for catalyst support. Carbon 40 (2002) 1079-1088
20. García-Bordejé E., Calvillo L., Lázaro M.J., and Moliner R. Vanadium supported on carbon-coated monoliths for the SCR of NO at low temperature: effect of pore structure. Appl. Catal. B: Environ. 50 (2004) 235-242
21. 3 over NomexTM rejects-based activated carbon fibre composite-supported manganese oxides. Part II. Effect of 242 procedures for impregnation and active phase formation. Appl. Catal. B. Environ. 34 (2001) 55-71
22. 3 at low temperatures. Appl. Catal. B: Environ. 23 (1999) L229-L233
23. x reduction exposed to flue gas from 100 MW-scale biofuel and peat fired boilers: influence of flue gas composition. Appl. Catal. B: Environ. 69 (2007) 240-251
24. 3 over activated carbon-supported vanadium oxide catalyst. J. Catal. 197 (2001) 6-16
25. C. Cristiani, A. Grossale, Forzatti, Study of the physico-chemical characteristics Q6 and rheological behaviuor of boehmite dispersions for dip-coating applications, submitted for publication.
26. Boehm H.P. Surface oxides on carbon and their analysis: a critical assessment. Carbon 40 (2002) 145-149
27. Szymański G.S., Karpiński Z., Biniak S., and Świa{ogonek}tkowski A. The effect of the gradual thermal decomposition of surface oxygen species on the chemical and catalytic properties of oxidized activated carbon. Carbon 40 (2002) 2627-2639
28. Figueiredo J.L., Pereira M.F.R., Freitas M.M.A., and Orfão J.J.M. Modification of the surface chemistry of activated carbons. Carbon 37 (1999) 1379-1389
29. Jia J., Zhou J., Zhang J., Yuan Z., and Wang S. The influence of preparative parameters on the adhesion of alumina washcoats deposited on metallic supports. Appl. Surf. Sci. 253 (2007) 9099-9104
30. Boyano A., Malpartida I., Larrubia M.A., Alemany J.L., and Lazaro M.J. Vanadium-loaded carbon-based monoliths for on-board NO reduction: Influence of nature and concentration of the oxidation agent on activity. Catal. Today 137 (2008) 222-227
31. Wu B., Xu B., Zhang B., and Dong S. The effects of parameters on the mechanical properties of Ni-based coatings prepared by automatic brush plating technology. Surf. Coat. Technol. 201 (2007) 5758-5765
32. Heck R.M., and Farrauto R.J. Automobile exhaust catalysts. Appl. Catal. A: Gen. 221 (2001) 443-457
33. Boyano A., Lombardo N., Gálvez M.E., Lázaro M.J., and Moliner R. Vanadium-loaded carbon-based monoliths for the on-board NO reduction: Experimental study of operating conditions. Chem. Eng. J. 144 (2008) 343-351
34. 3 layers on ceramic and metallic supports for the preparation of structured catalysts. Catal. Today 69 (2001) 307-314
35. Zamaro J.M., Ulla M.A., and Miro E.E. Zeolite washcoating onto cordierite honeycomb reactors for environmental applications. Chem. Eng. J. 106 (2005) 25-33
36. 4. Appl. Catal. B: Environ. 49 (2003) 121-132
37. ASTM E 1269-05, Test Method for Determining Specific Heat Capacity by Differential Scanning Calorimetry.
38. Jordan M.M., Montero M.A., Meseguer S., and Sanfeliu T. Influence of firing temperature and mineralogical composition on bending strength and porosity of ceramic tile bodies. Applied Clay Science 42 (2008) 266-271
39. Colombo P. Engineering porosity in polymer-derived ceramics. Journal of the European Ceramic Society 28 (2008) 1389-1395
40. 2 removal from flue gas: preparation and evaluation. Catal. Today 93-95 (2004) 833-837
41. Zamaro J.M., Ulla M.A., and Miró E.E. The effect of different slurry compositions and solvents upon the properties of ZSM5-washcoated cordierite honeycombs for the SCR of NOx with methane. Catal. Today 107-108 (2005) 86-93