Fatigue life of rubber components: 3D damage evolution from X-ray computed microtomography

Proceedings of the 5th European Conference on Constitutive Models for Rubber, ECCMR 2007

Volumn , Issue , 2008, Pages 173-177

  Le Gorju Jago, K ^a  

^a Chalette sur Loing ^*  (France)

Author keywords

[No Author keywords available]

Indexed keywords

COALESCENCE; CONSTITUTIVE MODELS; FATIGUE DAMAGE; FATIGUE TESTING; IMAGE ANALYSIS; INCLUSIONS; RUBBER;

CLOSE PROXIMITIES; DAMAGE EVOLUTIONS; DIFFERENT DAMAGES; FATIGUE CYCLES; FATIGUE LIVES; HIGH SPATIAL RESOLUTIONS; IMAGE ANALYSIS TOOLS; LOADING DIRECTIONS; MACROSCOPIC SCALE; MECHANICAL TESTS; MICROSCOPIC SCALE; MULTI-AXIAL FATIGUES; NUMBER AND SIZES; THREE DIMENSIONS; X-RAY COMPUTED MICROTOMOGRAPHY;

THREE DIMENSIONAL;

EID: 60749096112     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (8)

1. Choi, I.S. & Roland, CM. 1996. Intrinsic defects and the failure properties of cis-1.4-polyisoprenes. Rubber Chemistry and Technology 69, 591-599.
2. Fukahori, Y. & Seki, W. 1993. Stress analysis of elastomeric materials at large extensions using the finite elements methods. II: Stress and strain distribution around rigid spherical particles. Journal of Materials Science 28, 4471-482.
3. Gent, A.N. & Byoungyeu Park. 1984. Failure processes in elastomers at or near a rigid spherical inclusion. Journal of Materials Science 19, 1947-1956.
4. Gent, A.N. 1992. Engineering with rubber. Munich. Hanser Publishers.
5. Le Cam, J.B., Verron, E., Huneau, B., Gornet, L. & Perocheau, F. 2005. Micro-mechanism of fatigue crack growth : Comparison between carbon black filled NR and SBR.In Constitutive Models for rubber IV-Austrell & Kari (eds), 115-120.
6. Le Gorju-Jago, K. & Bathias, C. 2002. Fatigue initiation and propagation in natural and synthetic rubbers. International Journal of Fatigue 24, 85-92.
7. Mars, W.V 2001. Multiaxial fatigue of rubber. Ph-D Dissertation of the University of Toledo.
8. Trabelsi, S., Albouy, P.A. & Rault, J. 2002. Stress induced crystallisation around a crack tip in natural rubber. Macromolecules 35, 10054-10060.