Crack healing in polymeric materials via photochemical [2+2] cycloaddition

Chemistry of Materials

Volumn 16, Issue 21, 2004, Pages 3982-3984

  Chung, Chan Moon ^a   Roh, Young Suk ^a   Cho, Sung Youl ^a   Kim, Joong Gon ^b  

^a Yonsei University Wonju   (South Korea)

^b Hanwha Corporation   (South Korea)

Author keywords

[No Author keywords available]

Indexed keywords

BUTANE; CRACK INITIATION; CROSSLINKING; MONOMERS; PHOTOCHEMICAL REACTIONS;

CINNAMOYL GROUPS; CRACK HEALING; PHOTOCYCLOADDITION;

POLYMERS;

1,1,1 TRIS(CINNAMOYLOXYMETHYL)ETHANE; 1,6 BIS(2' METHACRYLOXYETHOXYCARBONYLAMINO) 2,4,4 TRIMETHYLHEXANE; CHLOROFORM; CINNAMIC ACID DERIVATIVE; CYCLOBUTANE; METHACRYLIC ACID DERIVATIVE; MONOMER; PLASTIC; POLYMER; TRIETHYLENE GLYCOL DIMETHYL ACRYLATE; UNCLASSIFIED DRUG;

ARTICLE; CATALYST; CHEMICAL STRUCTURE; CROSS LINKING; CYCLOADDITION; HEATING; INFRARED SPECTROSCOPY; PHOTOCHEMISTRY; PROTON NUCLEAR MAGNETIC RESONANCE; ULTRAVIOLET SPECTROSCOPY;

EID: 6044223548     PISSN: 08974756     EISSN: None     Source Type: Journal    
DOI: 10.1021/cm049394+     Document Type: Article

References (29)

1. Sauer, J. A.; Hara, M. Adv. Polym. Sci. 1990, 91/92, 69.
2. (a) Jud, K.; Kausch, H. H.; Williams, J. G. J. Mater. Sci. 1981, 16, 204.
3. (b) Kausch, H. H.; Jud, K. Plast. Rubber Proc. Appl. 1982, 2, 265.
4. (a) Lin, C. B.; Lee, S.; Liu, K. S. Polym. Eng. Sci. 1990, 30, 1399.
5. (b) Wang, P.; Lee, S.; Harmon, J. P. J. Polym. Sci. Part B: Polym. Phys. 1994, 32, 1217.
6. Dry, C. Composite Struct. 1996, 35, 263.
7. White, S. R.; Sottos, N. R.; Geubelle, P. H.; Moore, J. S.; Kessler, M. R.; Sriram, S. R.; Brown, E. N.; Viswanathan, S. Nature 2001, 409, 794.
8. Chen, X.; Dam, M. A.; Ono, K.; Mal, A.; Shen, H.; Nutt, S. R.; Sheran, K.; Wudl, F. Science 2002, 295, 1698.
9. (a) Arsu, N.; Bowser, R.; Davidson, R. S.; Kahn, N.; Moran, P. M.; Rhodes, C. J. In Photochemistry and Polymeric Systems; Kelly, J. M., McArdle, C. B., Maunder, M. J. F., Eds.; Royal Society of Chemistry. London, 1993; p 15.
10. (b) Decker, C. In Photochemistry and Polymeric Systems; Kelly, J. M., McArdle, C. B., Maunder, M. J. F., Eds.; Royal Society of Chemistry: London, 1993; p 32.
11. (a) Paczkowski, J. In Polymeric Materials Encyclopedia; Salamone, J. C., Ed.; CRC Press: Boca Raton, FL, 1996; p 5142.
12. (b) Ramamurthy, V.; Venkatesan, K. Chem. Rev. 1987, 87, 433.
13. (c) Egerton, P. L.; Hyde, E. M.; Trigg, J.; Payne, A.; Beynon, P.; Mijovic, M. V.; Reiser, A. J. Am. Chem. Soc. 1981, 103, 3859.
14. Hasegawa, M.; Katsumata, T.; Ito, Y.; Saigo, K.; Iitaka, Y. Macromolecules 1988, 21, 3134.
15. 3), 117.76, 128.32, 129.04, 134.41 (phenyl), 130.57 (phCH), 145.53 (phCH=CH), 166.79 (carbonyl).
16. Chung, C.-M.; Hasegawa, M. J. Am. Chem. Soc. 1991, 113, 7311.
17. 2).
18. Ali, A. H.; Srinivasan, K. S. V. Polym. Int. 1997, 43, 310.
19. Pretsch, E.; Buhlmann, P.; Affolter, C. Structure Determination of Organic Compounds; Springer: Berlin, 2000; p 292.
20. The ratios of the calculated areas of the two absorption bands (C=C and C=O as an internal standard) before and after exposure were compared to determine the degree of conversion of the cinnamoyl C=C bonds.
21. (a) Smith, M. B.; March, J. March's Advanced Organic Chemistry: Reactions, Mechanisms, and Structures', John Wiley and Sons: New York, 2001; p 24.
22. (b) Cremer, D.; Gauss, J. J. Am. Chem. Soc. 1986, 108, 7467.
23. Craig, R. G.; Powers, J. M. Restorative Dental Materials; Mosby: St. Louis, MO, 2002; pp 191 and 234.
24. The photocured samples had an average dimension of 25 × 2 × 2 mm. Twenty-five specimens were prepared for each formulation.
25. Free radical copolymerization of a cinnamate with some vinyl monomers such as methyl methacrylate has been reported to thermally occur in the presence of a peroxide initiator (see Esen, H.; Kusefoglu S. H. J. Appl. Polym. Sci. 2003, 89, 3882).
26. Billing, W. L.; Kroening R. D.; Little, J. C. J. Am. Chem. Soc. 1970, 92, 928.
27. Flexural strength was measured with a universal testing machine (Instron 6022) at a cross-head speed of 0.75 mm/min.
28. It was confirmed by differential scanning calorimetry and FT-IR spectroscopy that the cyclobutane structure is thermally stable up to 100 °C.
29. The time periods required for crack healing in the other systems are much longer than that in our system: several hours (refs 3b and 6), 48 h (ref 5), and 8 months (ref 4) compared to 10 min in this work.