Correlation between average melting temperature and glass transition temperature in metallic glasses

Applied Physics Letters

Volumn 94, Issue 6, 2009, Pages

  Lu, Zhibin ^a   Li, Jiangong ^a  

^a LANZHOU UNIVERSITY   (China)

Author keywords

[No Author keywords available]

Indexed keywords

GLASS; LIQUID METALS; MELTING POINT; METAL MELTING; METALLIC GLASS; SUPERCONDUCTING TRANSITION TEMPERATURE;

EXPERIMENTAL DATUM; GLASS TRANSITION TEMPERATURES; LINEAR RELATIONSHIPS; MELTING TEMPERATURES;

GLASS TRANSITION;

EID: 60349103426     PISSN: 00036951     EISSN: None     Source Type: Journal    
DOI: 10.1063/1.3081028     Document Type: Article

References (26)

1. W. L. Johnson, Mater. Sci. Forum 225-227, 35 (1996).
2. P. G. Debenedetti and F. H. Stillinger, Nature (London) 0028-0836 10.1038/35065704 410, 259 (2001).
3. W. H. Wang, P. Wen, D. Q. Zhao, M. X. Pan, and R. J. Wang, J. Mater. Res. 0884-2914 10.1557/JMR.2003.0382 18, 2747 (2003).
4. B. Yang, C. T. Liu, and T. G. Nieh, Appl. Phys. Lett. 0003-6951 10.1063/1.2206099 88, 221911 (2006).
5. T. Egami, Mater. Sci. Eng., A 226-228, 261 (1997). 0921-5093
6. W. H. Wang, J. Appl. Phys. 0021-8979 10.1063/1.2193060 99, 093506 (2006).
7. T. Egami, S. J. Poon, Z. Zhang, and V. Keppens, Phys. Rev. B 0163-1829 10.1103/PhysRevB.76.024203 76, 024203 (2007).
8. W. H. Wang, J. Non-Cryst. Solids 0022-3093 10.1016/j.jnoncrysol.2005.03. 024 351, 1481 (2005).
9. B. Zhang, D. Q. Zhao, W. H. Wang, and A. L. Greer, Phys. Rev. Lett. 0031-9007 10.1103/PhysRevLett.94.205502 94, 205502 (2005).
10. P. W. Anderson, Science 0036-8075 10.1126/science.267.5204.1615-e 267, 1615 (1995).
11. X. L. Li, X. F. Bian, L. N. Hu, Y. Q. Wu, J. Guo, and J. Y. Zhang, J. Appl. Phys. 101, 103540 (2007).
12. Z. Lu, J. Li, H. Shao, H. Gleiter, and X. Ni, " The correlation between shear elastic modulus and glass transition temperature of bulk metallic glasses.," Appl. Phys. Lett. (submitted). 0003-6951
13. http://www.webelements.com.
14. H. Kato, H. -S. Chen, and A. Inoue, Scr. Mater. 58, 1106 (2008). 1359-6462
15. J. Schroers, A. Masuhr, W. L. Johnson, and R. Busch, Phys. Rev. B 0163-1829 10.1103/PhysRevB.60.11855 60, 11855 (1999).
16. Th. Carnelley, Ber. Deut. Chem. Ges. 12, 439 (1879).
17. F. A. Lindemann, Phys. Z. 11, 609 (1910).
18. J. C. Dyre, Rev. Mod. Phys. 0034-6861 10.1103/RevModPhys.78.953 78, 953 (2006).
19. T. Egami, Rep. Prog. Phys. 0034-4885 10.1088/0034-4885/47/12/002 47, 1601 (1984).
20. M. Q. Jiang and L. H. Dai, Phys. Rev. B 0163-1829 10.1103/PhysRevB.76. 054204 76, 054204 (2007).
21. V. N. Novikov and A. P. Sokolov, Phys. Rev. B 0163-1829 10.1103/PhysRevB.74.064203 74, 064203 (2006).
22. S. Li, R. J. Wang, M. X. Pan, D. Q. Zhao, and W. H. Wang, Scr. Mater. 1359-6462 10.1016/j.scriptamat.2005.07.036 53, 1489 (2005).
23. L. Zhang, E. Ma, and J. Xu, Intermetallics 16, 584 (2008). 0966-9795
24. L. Y. Chen, Z. D. Fu, W. Zeng, G. Q. Zhang, Y. W. Zeng, G. L. Xu, S. L. Zhang, and J. Z. Jiang, J. Alloys Compd. 443, 105 (2007). 0966-9795
25. Z. -Z. Yuan, S. -L. Bao, Y. Lu, D. -P. Zhang, and L. Yao, J. Alloys Compd. 0925-8388 10.1016/j.jallcom.2007.05.037 459, 251 (2008).
26. J. F. Li, D. Q. Zhao, M. L. Zhang, and W. H. Wang, Appl. Phys. Lett. 0003-6951 10.1063/1.2998262 93, 171907 (2008).