Development of adhesive bonds with reduced fracture strength as NDE benchmarks

International Journal of Adhesion and Adhesives

Volumn 29, Issue 4, 2009, Pages 372-379

  Jastrzebski, M U ^a   Sinclair, A N ^a   Raizenne, D D ^b   Spelt, J K ^a  

^a UNIVERSITY OF TORONTO   (Canada)

^b NATIONAL RESEARCH COUNCIL CANADA   (Canada)

Author keywords

A. Epoxy epoxides; P. Durability non destructive testing; S. Aluminum and alloys

Indexed keywords

ACOUSTIC IMAGING; ADHESION; ADHESIVE JOINTS; ALUMINA; ALUMINUM; DEGRADATION; DURABILITY; IMAGING SYSTEMS; IMAGING TECHNIQUES; LIGHT METALS; METALLIC COMPOUNDS; NONDESTRUCTIVE EXAMINATION; QUALITY ASSURANCE; ULTRASONIC APPLICATIONS; ULTRASONIC IMAGING; ULTRASONIC TESTING; ULTRASONICS;

A. EPOXY/EPOXIDES; ACCELERATED AGING; ACCELERATED DEGRADATIONS; ADHESIVE BONDS; BONDED ALUMINUMS; EDX ANALYSES; ENVIRONMENTAL ATTACKS; ENVIRONMENTAL DEGRADATIONS; FRACTURE STRENGTHS; FRACTURE SURFACES; HIGH TEMPERATURES; P. DURABILITY NON-DESTRUCTIVE TESTING; RESIDUAL ALUMINUMS; S. ALUMINUM AND ALLOYS; SPECIMEN GEOMETRIES; SURFACE CONCENTRATIONS; ULTRASONIC METHODS; WET AGING;

FRACTURE;

EID: 58349118694     PISSN: 01437496     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijadhadh.2008.07.004     Document Type: Article

References (10)

1. Kinloch A.J. Adhesion and adhesives (1990), Chapman and Hall, New York
2. Wylde J.W., and Spelt J.K. Measurement of adhesive joint fracture properties as a function of environmental degradation. Int J Adhes Adhes 18 (1998) 237-246
3. Tu Y., and Spelt J.K. Blistering as a form of degradation in adhesive joints. J Adhesion 72 (2000) 359-372
4. Moidu A., Sinclair A.N., and Spelt J.K. Adhesive joint durability assessed using open-faced peel specimens. J Adhesion 65 (1998) 239-257
5. Mirkhani K. Characterization of interfacial degradation in adhesive joints using EMAT's, PhD thesis, University of Toronto, 2004.
6. Wegman R. Surface preparation techniques for adhesive bonding (1989), William Andrew Publishing, New York
7. Rushforth M.W., Bowen P., McAlpine E., Zhou X., and Thomson G.E. The effect of surface pretreatment and moisture on the fatigue performance of adhesively-bonded aluminium. J Mater Process Technol 153-154 (2004) 359-365
8. Kinloch A.J., Little M.S.G., and Watts J.F. The role of the interphase in the environmental failure of adhesive joints. Acta Mater 44 (2000) 4543-4553
9. Underhill P.R., and DuQuensnay D.L. The role of corrosion/oxidation in the failure of aluminum adhesive joints under hot, wet conditions. Int J Adhes Adhes 26 (2006) 88-93
10. Nordlien J., Nisancioglu K., Ono S., and Masuko N. Morphology of oxide films formed on MgAl alloys by exposure to air and water. J Electrochem Soc 143 8 (1996) 2564-2572