Crack initiation and propagation in a stainless duplex steel during HCF and VHCF loading

VHCF-4 - 4th International Conference on Very High Cycle Fatigue

Volumn , Issue , 2007, Pages 143-149

  Knobbe, Helge ^a   Köster, Philipp ^a   Krupp, Ulrich ^b   Christ, Hans Jürgen ^a   Fritzen, Claus Peter ^a   Cherif, Mohamed Anis ^c   Altenberger, Igor ^c  

^a UNIVERSITY OF SIEGEN   (Germany)

^b UNIVERSITY OF APPLIED SCIENCES OSNABRÜCK   (Germany)

^c UNIVERSITY OF KASSEL   (Germany)

Author keywords

Crack initiation; Duplex steel; Slip bands; Very high cycle fatigue

Indexed keywords

CRACK INITIATION; FATIGUE CRACK PROPAGATION; FATIGUE DAMAGE; FATIGUE OF MATERIALS; FERRITIC STEEL; FINITE ELEMENT METHOD; SCANNING ELECTRON MICROSCOPY; STAINLESS STEEL; STEEL; STRESS CORROSION CRACKING;

AUSTENITIC; CRACK INITIATION AND PROPAGATIONS; DUPLEX STEEL; ELASTIC ANISOTROPIES; ELECTRON BACK SCATTERED DIFFRACTIONS; FATIGUE EXPERIMENTS; FATIGUE LIMITS; FERRITIC STAINLESS STEELS; FINITE ELEMENT MODELS; GRAIN ORIENTATIONS; MICROSTRUCTURAL CONDITIONS; SLIP BANDS; VERY HIGH CYCLE FATIGUE; VERY HIGH CYCLE FATIGUES;

CRACKS;

EID: 58349098969     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (10)

1. S. Stanzl-Tschegg, H. Mayer, ed., Proceedings of International Conference on Fatigue in the Very High Cycle Regime (Vienna: University of Agriculture Science Press, 2001).
2. T. Sakai, Y. Ochi, ed., Proceedings of the Third International Conference on Very High Cycle Fatigue (Kusatsu: Ritsumeikan University, 2004).
3. C. Bathias, "There is no Infinite Fatigue Life in Metallic Materials," Fatigue and Fracture of Engineering Materials and Structures, 22 (1999), 559-565.
4. th International Fatigue Congress, ed. W. Steven Johnson (Atlanta: Georiga Institute of Technology, 2006).
5. H. Mughrabi, "Specific Features and Mechanisms of Fatigue in the Ultrahigh Cycle Regime," Proceedings of the Third International Conference on Very High Cycle Fatigue, ed. T. Sakai, Y. Ochi (Kusatsu: Ritsumeikan University, 2004).
6. th International Fatigue Congress, ed. W. Steven Johnson (Atlanta: Georiga Institute of Technology, 2006).
7. E. Notkina, G. Lütjering, A. Gysler, "Surface vs. subsurface crack nucleation in the HCF regime of titanium alloys," Proceedings of International Conference on Fatigue in the Very High Cycle Regime, ed. S. Stanzl-Tschegg, H. Mayer (Vienna: University of Agriculture Science Press, 2001).
8. G. Chai, "Fatigue Behaviour of Duplex Stainless Steels in the Very High Cycle Regime," International Journal of Fatigue, 28 (2006), 1611-1617.
9. G. Chai, "The Formation of Subsurface Non-Defect Fatigue Crack Origins," International Journal of Fatigue, 28 (2006), 1533-1539.
10. A. Heinz, P. Neumann, "Crack initiation during high cycle fatigue of an austenitic steel," Acta Metallurgica et Materialia, 38 (1990), 1933-1940. Fourth International Conference on Very High Cycle Fatigue Advanced Apparatus (Poster Session)