PSB threshold and fatigue limit of polycrystalline copper in the VHCF-regime

VHCF-4 - 4th International Conference on Very High Cycle Fatigue

Volumn , Issue , 2007, Pages 15-22

  Stanzl Tschegg, Stefanie ^a   Schonbauer, Bernd ^a  

^a UNIVERSITY OF NATURAL RESOURCES AND LIFE SCIENCES   (Austria)

Author keywords

Fatigue limit; Persistent slip bands (PSBs); PSB threshold; Ultrasonic fatigue; Very high cycle fatigue (VHCF)

Indexed keywords

COPPER; CRACK INITIATION; FATIGUE CRACK PROPAGATION; FATIGUE OF MATERIALS; PLASTIC DEFORMATION; STRAIN; STRAIN RATE; TESTING; ULTRASONIC APPLICATIONS; ULTRASONIC TESTING; ULTRASONICS;

FATIGUE LIMIT; PERSISTENT SLIP BANDS (PSBS); PSB THRESHOLD; ULTRASONIC FATIGUE; VERY HIGH CYCLE FATIGUE (VHCF);

FATIGUE TESTING;

EID: 58349098334     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (15)

1. H. Mughrabi, On the life-controlling microstructural fatigue mechanisms in ductile metals and alloys in the gigacycle regime, Fatigue & Fract Engng Mater Struct, 22 (1999) 633-641.
2. H. Mughrabi, "On multi-stage fatigue life diagrams and the relevant life-controlling mechanisms in ultrahighcycle fatigue", Fatigue & Fract Engng Mater Struct, 25 (2002) 755-764.
3. th European Conference of Fracture (ECF 16) - Failure Analysis of Nano and Engineering Materials and Structures, Alexandropoulis, Greece, ed. E.E. Gdoutos (Springer, 2006) CD, ISBN-10 1-4020-4971-4.
4. S. Stanzl-Tschegg, H. Mughrabi, and B. Schoenbauer, Life time and cyclic slip of copper in the VHCF regime, Proceedings of International Conference on Fatigue Damage of Structural Materials, Hyanrris, MA, USA, Sept. 2006, eds. MR. Bache et al. Updated version in press: Int. J. Fatigue (2007), doi: 10.1016/j.ijfatigue.2007.03.010
5. N. Thompson, N. Wadsworth, and N. Louat, The origin of fatigue fracture in copper, Philos Mag. Vol. 1, no. 2 (1956)113-126
6. H. Mughrabi and R. Wang, Cyclic deformation of face-centred cubic polycrystals: a comparison with observations on single crystals, in: Deformation of Polycrystals: Mechanisms and Microstructures, Proceedings of 2nd Rise International Symposium on Metallurgy and Materials Science, eds. N. Hansen et al. (Roskilde: Risø National Laboratory, 1981) 87-98.
7. M. Klesnil and P. Lukáš, Fatigue of Metallic Materials (Prague: Academia, and Amsterdam: Elsevier, 1980).
8. P. Lukáš, M. Klesnil, and Polák, "High cycle fatigue life of metals", Mater Sci., Eng 15 (1974) 239-245
9. H. Mughrabi, R. Wang, K. Differt, and U. Essmann, "Fatigue crack initiation by cyclic slip irreversibilities in high-cycle fatigue", Fatigue mechanisms: Advances in Quantitative Measurement of Physical Damage, eds. J. Lankford et al. (Philadelphia: American Society for Testing and Materials, ASTM STP 811, 1983) 5-45.
10. J.C. Figueroa, and C. Laird, "Crack initiation mechanisms in copper polycrystals cycled under constant strain amplitudes and in step test", Mater Sci., Eng 60 (1983) 45-58.
11. L. Llanes and C. Laird, Effect of loading mode on the cyclic response and the associated substructure of polycrystalline copper in the high-cycle regime, Fatigue & Fract Engng Mater Struct, 16 (1993) 165-179.
12. H. Mayer and C. Laird, Frequency effects on cyclic plastic strain of polycrystalline copper under variable loading, Mater Sci and Eng A194 (1995) 137-145.
13. H Mughrabi, "Cyclic deformation and fatigue - some current problems", Proc. ICSMA 7. Montreal, Vol. 3, 1985, 1017-1942.
14. L. Buchinger, S. Stanzl, and C. Laird, Dislocation structure in copper single crystals at low amplitudes, Philos Mag. A, 2 (1984) 275-298.
15. H. Mughrabi, and S. Stanzl-Tschegg, Fatigue damage evolution in ductile single-phase face-centred cubic metals in the UHCF-regime, to be presented at VHCF-4