Fatigue damage of low amplitude cycles under variable amplitude loading condition

VHCF-4 - 4th International Conference on Very High Cycle Fatigue

Volumn , Issue , 2007, Pages 333-340

  Mayer, Herwig ^a  

^a UNIVERSITY OF NATURAL RESOURCES AND LIFE SCIENCES   (Austria)

Author keywords

Damage accumulation; Fatigue limit; Threshold stress intensity; Ultrasonic fatigue; Variable amplitude loading

Indexed keywords

CRACK INITIATION; CRACK PROPAGATION; CRACKING (CHEMICAL); CRACKS; DURABILITY; FATIGUE CRACK PROPAGATION; FATIGUE OF MATERIALS; FATIGUE TESTING; LOADING; STRUCTURAL LOADS; THEOREM PROVING; ULTRASONICS;

DAMAGE ACCUMULATION; FATIGUE LIMIT; THRESHOLD STRESS INTENSITY; ULTRASONIC FATIGUE; VARIABLE AMPLITUDE LOADING;

FATIGUE DAMAGE;

EID: 58349093916     PISSN: None     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (19)

1. S.E. Stanzl-Tschegg, H. Mayer, and A. Stich, Variable amplitude loading in the very high-cycle fatigue regime. Fatigue Fract. Engng. Mater. Struct., 2002. 25: p. 887-896.
2. B. Zettl, H. Mayer, C. Ede, and S. Stanzl-Tschegg, Very high cycle fatigue of normalized carbon steels. Int. J. Fatigue, 2006. 28(11): p. 1583-1589.
3. E.R. De Los Rios, H.J. Mohamed, and K.J. Miller, A micro-mechanics analysis for short fatigue crack growth. Fatigue Fract. Engng. Mater. Struct., 1985. 8(1): p. 49-63.
4. M.D. Chapetti, N. Katsura, T. Tagawa, and T. Miyata, Static strengthening and fatigue lunt-notch sensitivity in low-carbon steels. Int. J. Fatigue, 2001. 23: p. 207-214.
5. A. Palmgren, Die Lebensdauer von Kugellagern. VDI-Zeitschr., 1924. 68(14): p. 339-341.
6. MA. Miner, Cumulative Damage in Fatigue. J. App. Mech. Trans. ASME, 1945. 12: p. 159-164.
7. P. Heuler and T. Seeger, A criterion for omission of variable amplitude loading histories. Int. J. Fatigue, 1986. 8(4): p. 225-230.
8. G. Marquis, Long life spectrum fatigue of carbon and stainless steel welds. Fatigue Fract. Engng. Mater. Struct., 1996. 19(6): p. 739-753.
9. X. Zheng, On some basic problems of fatigue research in engineering. Int. J. Fatigue, 2001. 23: p. 751-766.
10. J.H. Yan, X.L. Zheng, and K. Zhao, Experimental investigation on the small-loadomitting criterion. Int. J. Fatigue, 2001. 23: p. 403-415.
11. Y. Murakami and K. Matsuda, Cause of unsuccessful results of Miner's rule: Behavior of small fatigue crack growth under repeated two-step loadings, in Small fatigue cracks, K.S. Ravichandran, R.O. Ritchie, and Y. Murakami, Editors. 1999, Elsevier Sci. Ltd.: Amsterdam.
12. R. Koterzawa, Y. Mudjijana, Y. Quinsheng, W. Tian-Jian, and T. Nosho, Acceleration of fatigue crack growth under intermitted overstressing with different mean levels. Fatigue Fract. Engng. Mater. Struct., 1994. 17(9): p. 1033-1041.
13. H. Mayer, Ultrasonic Torsion and Tension-Compression Fatigue Testing: Measuring Principles and Investigations on 2024-T351 Aluminium Alloy. Int. J. Fatigue, 2006. 28(11): p. 1446-1455.
14. H. Mayer, C. Ede, and J.E. Allison, Influence of Cyclic Loads below Endurance Limit and Threshold Stress Intensity on Fatigue Damage in Cast Aluminium Alloy 319T7. Int. J. Fatigue, 2005. 27(2): p. 129-141.
15. H. Mayer, Fatigue crack growth and threshold measurements at very high frequencies. Int. Mater. Rev., 1999. 44(1): p. 1-36.
16. W.W. Maenning, Planning and evaluation of fatigue tests, in ASM Handbook Fatigue and Fracture, S.R. Lampman, et al., Editors. 1997, ASM International: Materials Park OH. p. 303-313.
17. N.M. James and E.R. De Los Rios, Variable amplitude loading of small fatigue cracks in 6261-T6 aluminium alloy. Fatigue Fract. Engng. Mater. Struct., 1996. 19(4): p. 413-426.
18. S. Suresh and R.O. Ritchie, On the influence of fatigue underloads on cyclic crack growth at low stress intensities. Mater. Sci. Engng., 1981. 51: p. 61-69.
19. S.E. Stanzl-Tschegg, H.R. Mayer, E.K. Tschegg, and A. Beste, In-service loading of AlSill aluminium cast alloy in the very high cycle regime. Int. J. Fatigue, 1993. 15(4): p. 311-316.