Phase growth in diffusion couples under an low frequency alternating magnetic field

Scripta Materialia

Volumn 52, Issue 1, 2005, Pages 79-82

  Liu, Xiaotao ^a   Cui, Jianzhong ^a   Wu, Xiaoming ^a   Guo, Yanhui ^a   Zhang, Jun ^a  

^a NORTHEASTERN UNIVERSITY   (China)

Author keywords

Alternating magnetic field; Diffusion couple; Intermediate phase; Parabolic rate law; Thickness

Indexed keywords

ACTIVATION ENERGY; ALUMINUM COMPOUNDS; ANNEALING; CRYSTAL STRUCTURE; DATA REDUCTION; DIFFUSION; ELECTROMAGNETISM; PHASE DIAGRAMS; SOLIDIFICATION;

ALTERNATING MAGNETIC FIELD; DIFFUSION COUPLES; INTERMEDIATE PHASE; PARABOLIC RATE LAW;

MAGNETIC FIELDS;

EID: 5744251138     PISSN: 13596462     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.scriptamat.2004.05.025     Document Type: Article

References (10)

1. Furui M, Kojima Y, Matsuo M. ISIJ Int 1993;33(3):400.
2. Shimotomai M, Maruta K. Scripta Mater 2000;42:499.
3. Marty P, Alemany A. Metallurgical application of magnetohydrodynamics. In: Proceedings of a Symposium of the IUTAM, The Metal Society; 1984. p. 245.
4. Asai S. ISIJ Int 1989;29(12):981.
5. Ban CY. PhD Thesis, Northeastern University, Shenyang, 2002 [in Chinese].
6. Zhang BJ, Cui JZ, Lu GM. Mater Lett 2003;57:1707.
7. Hansen M, Auderko K. Constitution of binary alloys. New York: McGraw-Hill; 1958 p. 105.
8. Samson S. Acta Cryst 1965;19:401.
9. Laves F, Moeller K. Z Metall 1938;30:232.
10. Funamizu Y, Watamabe K. Trans JIM 1971;12(3):147.