Durability of concretes containing natural pozzolan

Proceedings of Institution of Civil Engineers: Construction Materials

Volumn 161, Issue 3, 2008, Pages 113-118

  Najimi, Meisam ^a   Jamshidi, Masoud ^a   Pourkhorshidi, Alireza ^a  

^a BUILDING AND HOUSING RESEARCH CENTER   (Iran)

Author keywords

Concrete technology manufacture

Indexed keywords

BONE CEMENT; CEMENT MANUFACTURE; CEMENTS; CONCRETE CONSTRUCTION; CONCRETES; DURABILITY; MECHANICAL PROPERTIES; PORTLAND CEMENT; SILICA;

ALKALI REACTIVITIES; CHLORIDE IONS; DURABILITY OF CONCRETES; EXPANSION TESTS; NATURAL POZZOLANS; WATER PENETRATIONS;

POZZOLAN;

EID: 55949117305     PISSN: 1747650X     EISSN: 17476518     Source Type: Journal    
DOI: 10.1680/coma.2008.161.3.113     Document Type: Article

References (27)

1. RAMEZANIANPOUR A. A. and MIYAMOTO A. Durability of concrete structures in the Persian Gulf. Concrete Journal, Japan Concrete Institute, 2000, 38, No. 3, 29-33.
2. OZER B. and HULUSI OZKUL M. The influence of initial water curing on the strength development of ordinary Portland and pozzolanic cement concretes. Cement and Concrete Research, 2004, 34, No. 1, 13-18.
3. RAMYAR K. and INAN G. Sodium sulfate attack on plain and blended cements. Building and Environment, 2007, 42, No. 3, 1368-1372.
4. EZZIANE K., BOUGARA A., KADRI A., KHELAFI H. and KADRI E. Compressive strength of mortar containing natural pozzolan under various curing temperature. Cement and Concrete Composites, 2007, 29, No. 8, 587-593.
5. FELEKOGLU B., RAMYAR K., TOSUN K. and MUSAL B. Sulfate resistance of different types of Turkish Portland cements by selecting the appropriate test methods. Construction and Building Materials, 2006, 20, No. 9, 819-823.
6. SHA W. and PEREIRA G. B. Differential scanning calorimetry study of ordinary Portland cement paste containing metakaolin and theoretical approach of metakaolin activity. Cement and Concrete Composites, 2001, 23, No. 6, 455-461.
7. COLAK A. The long-term durability performance of gypsum-Portland-cement-natural pozzolan blends. Cement and Concrete Research, 2002, 32, No. 1, 109-115.
8. COLAK A. Characteristics of pastes from a Portland cement containing different amounts of natural pozzolan. Cement and Concrete Research, 2003, 33, No. 4, 585-593.
9. BINICI H. and AKSOGAN O. Sulfate resistance of plain and blended cement. Cement and Concrete Composites, 2006, 28, No. 1, 39-46.
10. VU D. D., STROEVEN P. and BUI V. B. Strength and durability aspects of calcined kaolin-blended Portland cement mortar and concrete. Cement and Concrete Composites, 2001, 23, No. 6, 471-478.
11. TARGAN S., OLGUN A., ERDOGAN Y. and SEVINV V. Influence of natural pozzolan, colemanite ore waste, bottom ash, and fly ash on the properties of Portland cement. Cement and Concrete Research, 2003, 33, No. 8, 1175-1182.
12. SHANNAG M. J. High strength concrete containing natural pozzolan and silica fume. Cement and Concrete Composites, 2000, 22, No. 6, 399-406.
13. SHANNAG M. J. and YEGINOBALI A. Properties of pastes, mortars and concretes containing natural pozzolan. Cement and Concrete Research, 1995, 25, No. 3, 647-657.
14. AMERICAN SOCIETY FOR TESTING AND MATERIALS. Standard Specification for Blended Hydraulic Cement. ASTM International, West Conshohocken, PA, USA, C595-08.
15. AMERICAN SOCIETY FOR TESTING AND MATERIALS. Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete. ASTM. International, West Conshohocken, PA, USA, C618-08.
16. EUROPEAN COMMITTEE FOR STANDARDIZATION. Testing Hardened Concrete-Compressive Strength of Test Specimens. CEN, Brussels, 2001, EN 12390: Part 3.
17. GERMAN INSTITUTE FOR STANDARDIZATION. Testing Concrete, Testing of Hardened Concrete. DIN, Berlin, 1991, DIN 1048: Part 5.
18. EUROPEAN COMMITTEE FOR STANDARDIZATION. Testing Hardened Concrete-Depth of Penetration of Water under Pressure. CEN, Brussels, 2000, EN 12390: Part 8.
19. AMERICAN SOCIETY FOR TESTING AND MATERIALS. Standard Test Method for Electrical Indication of Concrete's Ability to Resist Chloride Ion Penetration. ASTM International, West Conshohocken, PA, USA, C1202-07.
20. AMERICAN SOCIETY FOR TESTING AND MATERIALS. Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing. ASTM International, West Conshohocken, PA, USA, C666-03.
21. AMERICAN SOCIETY FOR TESTING AND MATERIALS. Standard Test Method for Effectiveness of Mineral Admixtures or Ground Blast Furnace Slag in Preventing Excessive Expansion of Concrete due to the Alkali-silica Reaction. ASTM International, West Conshohocken, PA, USA, C441-05.
22. AMERICAN SOCIETY FOR TESTING AND MATERIALS. Standard Test Method for Potential Alkali Reactivity of Aggregates (Mortar-Bar Method). ASTM International, West Conshohocken, PA, USA, C1260-07.
23. AMERICAN SOCIETY FOR TESTING AND MATERIALS. Standard Test Method for Length of Hydraulic-cement Mortar Exposed to Sulfate Solution. ASTM International, West Conshohocken, PA, USA, C1012-04.
24. EUROPEAN COMMITTEE FOR STANDARDIZATION. Testing Fresh Concrete-Density. CEN, Brussels, 1999, EN 12350: Part 6.
25. EUROPEAN COMMITTEE FOR STANDARDIZATION. Testing Fresh Concrete-Slump Test. CEN, Brussels, 1999, EN 12350: Part 2.
26. EUROPEAN COMMITTEE FOR STANDARDIZATION. Testing Fresh Concrete-Pressure Methods. CEN, Brussels, 2000, EN 12350: Part 7.
27. EUROPEAN COMMITTEE FOR STANDARDIZATION. Testing Hardened Concrete-Making and Curing Specimens for Strength Tests. CEN, Brussels, 2000, EN 12390: Part 2.