Examination of fatigue crack driving force parameter

Fatigue and Fracture of Engineering Materials and Structures

Volumn 31, Issue 9, 2008, Pages 754-765

  Xiong, Y ^a   Katsuta, J ^b   Kawano, K ^b   Sakiyama, T ^b  

^a ZHEJIANG UNIVERSITY OF TECHNOLOGY   (China)

^b NAGASAKI UNIVERSITY   (Japan)

Author keywords

Crack closure; Crack driving force; Crack tip; Fatigue crack growth; Hysteresis loop; R ratio; Variable amplitude loads

Indexed keywords

ABS RESINS; BUILDING MATERIALS; CRACK CLOSURE; CRACK TIPS; CRACKING (CHEMICAL); FATIGUE CRACK PROPAGATION; FATIGUE OF MATERIALS; HYSTERESIS; MAGNETIC MATERIALS;

AMPLITUDE LOADINGS; COMPLIANCE CHANGES; CRACK DRIVING FORCE; CRACK DRIVING FORCES; DRIVING FORCES; EXPERIMENTAL DATUM; FATIGUE CRACK GROWTH; FATIGUE CRACK GROWTH RATES; FATIGUE CRACKS; PHYSICAL MEANINGS; R-RATIO; STRUCTURAL STEELS; TEST RESULTS; THEORETICAL CALCULATIONS; VARIABLE AMPLITUDE LOADS;

CRACKS;

EID: 54549096040     PISSN: 8756758X     EISSN: 14602695     Source Type: Journal    
DOI: 10.1111/j.1460-2695.2008.01261.x     Document Type: Article

References (36)

1. Elber, W. (1971) The significance of fatigue crack closure. In: Damage Tolerance in Aircraft Structures, ASTM STP 486. American Society for Testing and Materials, Philadelphia, pp. 230-242.
2. Stoychev, S. and Kujawki, D. (2003) Methods for crack opening load and crack tip shielding determination: A review. Fatigue Fract. Engng Mater. Struct. 26, 1053-1067.
3. Nisitani, H. and Chen, D. H. (1985) A consideration on the unloading elastic compliance method. Trans. Jpn. Soc. Mech. Engng. 51, 1436-1441.
4. Paris, P. C. and Tada, H. (2002) Near threshold fatigue crack growth versus long finite life. Fatigue Fract. Engng Mater. Struct. 25, 727-733.
5. Donald, J. K. (1997) Introducing the compliance ratio concept for determining effective stress intensity. Int. J. Fatigue. 19, S191-195.
6. Chen, D. L., Weiss, B. and Stickler, R. (1996) A model for crack closure. Engng. Fract. Mech. 53, 493-509.
7. Riemelmoser, F. and Pippan, R. (1997) Crack closure, a concept of fatigue crack growth under examination. Fatigue Fract. Engng Mater. Struct. 20, 1529-1540.
8. Chen, D. L., Weiss, B. and Stickler, R. (1996) Contribution of the cycle loading portion below the opening load to fatigue crack growth. Mater. Sci. Engng. A208, 181-187.
9. Paris, P. C., Tada, H. and Donald, J. K. (1999) Service load fatigue damage - a historical perspective. Int. J. Fatigue. 21 (Suppl), S35-S46.
10. Kujawski, D. (2002) Utilization of partial crack closure for fatigue crack growth modeling. Engng Fract. Mech. 69, 1315-1324.
11. Hertzberg, R. W., Newton, C. H. and Jaccard, R. (1998) Crack closure: correlation and confusion. Mechanics of fatigue crack closure, ASTM STP 982. American Society for Testing and Materials, Philadelphia, PA, pp. 139-148.
12. Lang, M. (2000) A model for fatigue crack growth, part I: Phenomenology. Fatigue Fract. Engng Mater. Struct. 23, 587-601.
13. Marci, G. (1979) Effect of the plastic wake zone on fatigue crack growth rates. ASTM STP 677, 168-186.
14. Toyosada, M. and Niwa, T. (1994) The significance of RPG load for fatigue crack growth and the development of a compliance measuring system. Int. J. Fract. 67, 217-230.
15. Toyosada, M., Niwa, T., Yamaguchi, K., Takenaka, H., Aramaki, N. and Masaki, H. (1992) Fatigue crack growth law for wide range from very slow crack growth rate region to stable crack growth rate region. Jpn. Soc. Naval Architect. 172, 589-599 [in Japanese].
16. Sadananda, K. and Vasudevan, A. K. (1993) Analysis of fatigue crack closure and threshold. ASTM STP 1220. American Society for Testing and Materials, Philadelphia, PA, pp. 484-501.
17. Vasudevan, A. K., Sadananda, K. and Louat, N. A. (1994) Review of crack closure, fatigue crack threshold and related phenomena. Mater. Sci. Engng. A. 188, 1-22.
18. eff estimation procedure on 6061-T6 and 2024-T3 aluminum alloys. Int. J. Fatigue. 21, S47-S57.
19. Walker, E. K. (1970) The effect of stress ratio during crack propagation and fatigue 2024-T3 and 7076-T6 aluminum. In: Effect of Environment and Complex Load History on Fatigue Life, ASTM STP 462. American Society for Testing and Materials, Philadelphia, pp. 1-14.
20. max dependent models of fatigue crack growth. Int. J. Fatigue. 21, S147-S155.
21. max) 0.5 driving force parameter for crack growth in aluminum alloys. Int. J. Fatigue. 23, 733-740.
22. Kujawski, D. (2001) A fatigue crack driving force parameter with load ratio effects. Int. J. Fatigue. 23, S239-S246.
23. + parameters. Engng Fract. Mech. 71, 1779-1790.
24. Noroozi, A. H., Glinka, G. and Lambert, S. (2005) A two parameter driving force for fatigue crack growth analysis. Int. J. Fatigue. 27, 1277-1296.
25. Xiong, Y., Katsuta, J., Sakiyama, T. and Kawano, K. (2006) Characteristics of fatigue crack growth behaviour as identified by hysteresis loop at the crack tip. Fatigue Fract. Engng Mater. Struct. 29, 454-463.
26. Kikukawa, M., Jono, M., Tanaka, K. and Takatani, M. (1976) Measurement of fatigue crack propagation and crack closure at low stress intensity level by unloading elastic compliance method. J Soc Mater Sci. 25, 899-903 [in Japanese].
27. Toyosada, M., Yamaguchi, K., Niwa, T., Takenaka, H., Kajimoto, K. and Yajima, H. (1991) Proposal of new parameter for fatigue crack growth rate based upon the compliance changing phenomena and the development of its measuring method. Jpn. Soc. Naval Architect. 169, 245-255 [in Japanese].
28. Xiong, Y., Hu, X. X., Katsuta, J., Sakiyama, T. and Kawano, K. (2008) Influence of compressive plastic zone at the crack tip upon fatigue crack propagation. Int. J. Fatigue. 30, 67-73.
29. Toyosada, M. (2002) A study of threshold phenomena by residual tensile layer close to the surface of a fatigue crack. West-Jpn. Soc. Naval Architect. 105, 223-235 [in Japanese].
30. eff-concept: A unique and complete description of fatigue crack growth. Engng Fract. Mech. 55, 95-114.
31. Lang, M. and Huang, X. (1998) The influence of compressive loads on fatigue crack growth in metals. Fatigue Fract. Engng Mater. Struct. 21, 65-83.
32. Dugdale, D. S. (1960) Yielding of steel sheets containing slits. J. Mech. Phys. Solids. 8, 100-108.
33. Zheng, J. and Powell, B. E. (1999) Effect of stress ratio and test methods on fatigue crack growth rate for nickel based superalloy Udimet 720. Int. J. Fatigue. 21, 507-513.
34. Schijve, J. (1981) Some formulas for crack opening stress level. Engng Fract. Mech. 14, 461-465.
35. Kumar, R. and Singh, K. (1995) Influence of stress ratio on fatigue crack growth in mild steel. Engng Fract. Mech. 50, 377-384.
36. Maddox, S. J. (1975) The effect of mean stress on fatigue crack propagation: A literature review. In. J. Fract. 11, 389-407.