Volumn 72, Issue 2, 2005, Pages 195-208

Fracture mechanics and scale effects in the fatigue of railway axles

Author keywords

Crack growth model; Crack propagation; Full scale fatigue test; Railway axles; Short crack effect

Indexed keywords

AXLES; CRACK PROPAGATION; FATIGUE OF MATERIALS; RAILROAD ROLLING STOCK;

EID: 4644350617     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfracmech.2003.12.011     Document Type: Article
Times cited : (101)

References (19)
  • 1
    • 4644281557 scopus 로고    scopus 로고
    • European standard EN 13103-13104 CEN European Committee for Standardization. Brussels
    • European standard EN 13103-13104 (2001). CEN European Committee for Standardization. Brussels
    • (2001)
  • 4
    • 0000504982 scopus 로고
    • Effects of defects, inclusions and inhomogeneities on fatigue strength
    • Murakami Y. Endo M. Effects of defects, inclusions and inhomogeneities on fatigue strength Int. J. Fatigue 16 1994 163-182
    • (1994) Int. J. Fatigue , vol.16 , pp. 163-182
    • Murakami, Y.1    Endo, M.2
  • 5
    • 0000542063 scopus 로고
    • Fracture mechanics approach to very small crack growth and to the threshold condition
    • Kitagawa H. Takahashi S. Fracture mechanics approach to very small crack growth and to the threshold condition Trans. Jpn. Soc. Mech. Engng. A 45 399 1979 1289-1303
    • (1979) Trans. Jpn. Soc. Mech. Engng. A , vol.45 , Issue.399 , pp. 1289-1303
    • Kitagawa, H.1    Takahashi, S.2
  • 6
    • 0028464859 scopus 로고
    • Instructions for a new method of inclusion rating and correlations with the fatigue limit
    • Murakami Y. Toriyama T. Coudert E.M. Instructions for a new method of inclusion rating and correlations with the fatigue limit J. Test. Eval. 22 1994 318-326
    • (1994) J. Test. Eval. , vol.22 , pp. 318-326
    • Murakami, Y.1    Toriyama, T.2    Coudert, E.M.3
  • 7
    • 0000741103 scopus 로고    scopus 로고
    • Small defects and inhomogeneities in fatigue strength: Experiments, models and statistical implications
    • Murakami Y. Beretta S. Small defects and inhomogeneities in fatigue strength: experiments, models and statistical implications Extremes 2 1999 123-147
    • (1999) Extremes , vol.2 , pp. 123-147
    • Murakami, Y.1    Beretta, S.2
  • 8
    • 4644332057 scopus 로고    scopus 로고
    • ESIS P11-02: Technical Recommendations for the Extreme Value Analysis of Data on Large Nonmetallic Inclusions in Steels
    • ESIS Procedures and Documents
    • ESIS P11-02: Technical Recommendations for the Extreme Value Analysis of Data on Large Nonmetallic Inclusions in Steels. ESIS Procedures and Documents. 2002
    • (2002)
  • 9
    • 0001030370 scopus 로고
    • Materials science perspective of metal fatigue resistance
    • Miller K.J. Materials science perspective of metal fatigue resistance Mater. Sci. Technol. 9 1993 453-462
    • (1993) Mater. Sci. Technol. , vol.9 , pp. 453-462
    • Miller, K.J.1
  • 10
    • 4644326882 scopus 로고    scopus 로고
    • t in transition zone between body and wheel-seat for different axle shapes
    • Internal Lucchini Report
    • t in transition zone between body and wheel-seat for different axle shapes. Internal Lucchini Report. 2001
    • (2001)
    • Lombardo, F.1    Benigni, E.2
  • 11
    • 19544390143 scopus 로고    scopus 로고
    • Propagation of short cracks in a high strength steel for railway axles
    • Neimitz A, Rokach IV, Kocanda D, Golos K, editors. EMAS
    • Beretta S. Propagation of short cracks in a high strength steel for railway axles. In: Neimitz A, Rokach IV, Kocanda D, Golos K, editors. ECF14 fracture mechanics beyond 2000. EMAS. 2002. p. 217-24
    • (2002) ECF14 Fracture Mechanics Beyond 2000 , pp. 217-224
    • Beretta, S.1
  • 12
    • 0021869835 scopus 로고
    • Analysis of stress intensity factors of modes I, II and III for inclined surface cracks of arbitrary shape
    • Murakami Y. Analysis of stress intensity factors of modes I, II and III for inclined surface cracks of arbitrary shape Engng. Fract. Mech. 22 1985 101-114
    • (1985) Engng. Fract. Mech. , vol.22 , pp. 101-114
    • Murakami, Y.1
  • 14
    • 0032293895 scopus 로고    scopus 로고
    • Statistical analysis of defects for fatigue strength prediction and quality control of materials
    • Beretta S. Murakami Y. Statistical analysis of defects for fatigue strength prediction and quality control of materials Fatigue Fract. Engng. Mater. Struct. 21 1998 1049-1065
    • (1998) Fatigue Fract. Engng. Mater. Struct. , vol.21 , pp. 1049-1065
    • Beretta, S.1    Murakami, Y.2
  • 17
    • 85120355555 scopus 로고
    • Monitoring small-crack growth by the replication method
    • Larsen JM, Allison JE, editors. ASTM STP 1149, ASTM
    • Swain MH. Monitoring small-crack growth by the replication method. In: Larsen JM, Allison JE, editors. Small crack test methods. ASTM STP 1149, ASTM. 1992. p. 34-56
    • (1992) Small Crack Test Methods , pp. 34-56
    • Swain, M.H.1
  • 18
    • 0029736511 scopus 로고    scopus 로고
    • Part-through cracks in round bars under cyclic combined axial and bending loading
    • Carpinteri A. Brighenti R. Part-through cracks in round bars under cyclic combined axial and bending loading Int. J. Fatigue 18 1996 33-39
    • (1996) Int. J. Fatigue , vol.18 , pp. 33-39
    • Carpinteri, A.1    Brighenti, R.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.