Volumn 29, Issue 10, 2008, Pages 1893-1896
Tensile behaviours of some high performance filaments after NaOH treatment
Author keywords

Chemical reactions (F); Corrosion (E); Fibres and filaments (B)
Indexed keywords

EID: 45049088308     PISSN: 02641275     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.matdes.2008.04.025     Document Type: Article
Times cited : (20)
References (9)
  • 1
    • 0035021726 scopus 로고    scopus 로고
    • Environmental fatigue of unidirectional glass-carbon fiber reinforced hybrid composite
    • Shan Y., and Liao K. Environmental fatigue of unidirectional glass-carbon fiber reinforced hybrid composite. Composites Part B 32 (2001) 355-363
    • (2001) Composites Part B , vol.32 , pp. 355-363
    • Shan, Y.1    Liao, K.2
  • 2
    • 0034745720 scopus 로고    scopus 로고
    • Aging of polymeric composite specimens for 5000 h at elevated pressure and temperature
    • Thomas K., et al. Aging of polymeric composite specimens for 5000 h at elevated pressure and temperature. Compos Sci Technol 61 (2001) 75-86
    • (2001) Compos Sci Technol , vol.61 , pp. 75-86
    • Thomas, K.1
  • 3
    • 0019008880 scopus 로고
    • Effect on moisture experiments of failure to dry specimens prior to exposure
    • Edge E.C. Effect on moisture experiments of failure to dry specimens prior to exposure. Composites 11 (1980) 101-104
    • (1980) Composites , vol.11 , pp. 101-104
    • Edge, E.C.1
  • 4
    • 0021464211 scopus 로고
    • Stress rupture life time of a polyethylene terephthalate/glass composite under an alkaline solution environment
    • Shultz J.M., and Lhymn C. Stress rupture life time of a polyethylene terephthalate/glass composite under an alkaline solution environment. Polym Compos 7 (1984) 208-214
    • (1984) Polym Compos , vol.7 , pp. 208-214
    • Shultz, J.M.1    Lhymn, C.2
  • 5
    • 0023169264 scopus 로고
    • Effect of matrix toughness on crack propagation during stress corrosion of glass reinforced composites
    • Price J.N., and Hull D. Effect of matrix toughness on crack propagation during stress corrosion of glass reinforced composites. Compos Technol 28 (1987) 193-200
    • (1987) Compos Technol , vol.28 , pp. 193-200
    • Price, J.N.1    Hull, D.2
  • 6
    • 0035271689 scopus 로고    scopus 로고
    • An evaluation of the critical conditions for the initiation of stress corrosion cracking in unidirectional E-glass/polymer composites
    • Kumosa L., Armentrout D., and Kumosa M. An evaluation of the critical conditions for the initiation of stress corrosion cracking in unidirectional E-glass/polymer composites. Compos Sci Technol 61 (2001) 615-623
    • (2001) Compos Sci Technol , vol.61 , pp. 615-623
    • Kumosa, L.1    Armentrout, D.2    Kumosa, M.3
  • 7
    • 0035086168 scopus 로고    scopus 로고
    • Stress corrosion crack growth in glass polyester composites with surface crack
    • Akdemir A., et al. Stress corrosion crack growth in glass polyester composites with surface crack. Composites Part B 32 (2001) 123-129
    • (2001) Composites Part B , vol.32 , pp. 123-129
    • Akdemir, A.1
  • 8
    • 0023362634 scopus 로고
    • Corrosion of glass fibres
    • Rodriguez E.L. Corrosion of glass fibres. J Mater Sci Lett 6 (1987) 718-720
    • (1987) J Mater Sci Lett , vol.6 , pp. 718-720
    • Rodriguez, E.L.1
  • 9
    • 0020543257 scopus 로고
    • Accelerating ageing of a glass fiber reinforced epoxy resin in water
    • Dewimille B., and Bunsell A.R. Accelerating ageing of a glass fiber reinforced epoxy resin in water. Composites 14 (1983) 35-40
    • (1983) Composites , vol.14 , pp. 35-40
    • Dewimille, B.1    Bunsell, A.R.2

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.