Fabrication of Cu-Zr-Ag-Al glassy alloy samples with a diameter of 20 mm by water quenching

Journal of Materials Research

Volumn 23, Issue 5, 2008, Pages 1452-1456

  Zhang, Wei ^a   Zhang, Qingsheng ^a   Inoue, Akihisa ^a  

^a TOHOKU UNIVERSITY   (Japan)

Author keywords

[No Author keywords available]

Indexed keywords

EUTECTICS; GLASS TRANSITION; INJECTION MOLDING; QUENCHING; TEMPERATURE; THERMODYNAMIC STABILITY;

GLASS-FORMING ABILITY;

COPPER ALLOYS;

EID: 44649084360     PISSN: 08842914     EISSN: None     Source Type: Journal    
DOI: 10.1557/jmr.2008.0183     Document Type: Article

References (34)

1. 20 alloy prepared by water quenching. Mater. Trans., JIM 30, 722 (1989).
2. A. Inoue, A. Kato, T. Zhang, S.G. Kim, and T. Masurnoto: Mg-Cu-Y amorphous alloys with high mechanical strengths produced by a metallic mold casting method. Mater. Trans., JIM 32, 609 (1991).
3. T. Zhang, A. Inoue, and T. Masumoto: Amorphous Zr-Al-TM (TM = Co, Ni, Cu) alloys with significant supercooled liquid region of over 100 K. Mater. Trans., JIM 32, 1005 (1991).
4. 22.5. Appl. Phys. Lett. 63, 2342 (1993).
5. A. Inoue and S.G. Gook: Fe-based ferromagnetic glassy alloys with wide supercooled liquid region. Mater. Trans., JIM 36, 1180 (1995).
6. X.H. Lin and W.L. Johnson: Formation of Ti-Zr-Cu-Ni bulk metallic glasses. J. Appl. Phys. 78, 6514 (1995).
7. 20 alloy cylinder of 72 mm in diameter. Mater. Trans., JIM 38, 179 (1997).
8. T. Zhang and A. Inoue: Thermal and mechanical properties of Ti-Ni-Cu-Sn amorphous alloys with a wide supercooled liquid region before crystallization. Mater. Trans., JIM 39, 1001 (1998).
9. T. Itoi and A. Inoue: Thermal stability and soft magnetic properties of Co-Fe-M-B (M = Nb, Zr) amorphous alloys with large supercooled liquid region. Mater. Trans., JIM 41, 1256 (2000).
10. y (M = Cr, Mo) alloys with large supercooling and high strength. Mater. Trans., JIM 40, 1130 (1999).
11. S. Yi, T.G. Park, and D.H. Kim: Ni-based bulk amorphous alloys in the Ni-Ti-Zr-(Si,Sn) system. J. Mater. Res. 15, 2425 (2000).
12. T. Zhang and A. Inoue: New bulk glassy Ni-based alloys with high strength of 3000 MPa. Mater. Trans. 43, 708 (2002).
13. 5. J. Non-Cryst. Solids 311, 72 (2002).
14. A. Inoue, W. Zhang, T. Zhang, and K. Kurosaka: High-strength Cu-based bulk glassy alloys in Cu-Zr-Ti and Cu-Hf-Ti ternary systems. Acta Mater. 49, 2645 (2001).
15. A. Inoue and W. Zhang: Formation, thermal stability and mechanical properties of Cu-Zr-Al bulk glassy alloys. Mater. Trans. 43, 2921 (2002).
16. W. Zhang and A. Inoue: High glass-forming ability and good mechanical properties of new bulk glassy alloys in Cu-Zr-Ag ternary system. J. Mater. Res. 21, 234 (2006).
17. K. Amiya and A. Inoue: Formation, thermal stability and mechanical properties of Ca-based bulk glassy alloys. Mater. Trans. 43, 81 (2002).
18. J. Schroers and W.L. Johnson: Highly processable bulk metallic glass-forming alloys in the Pt-Co-Ni-Cu-P system. Appl. Phys. Lett. 84, 3666 (2004).
19. J. Schroers, B. Lohwongwatana, W.L. Johnson, and A. Peker: Gold based bulk metallic glass. Appl. Phys. Lett. 87, 061912 (2005).
20. 30 alloy of 30 mm in diameter by a suction casting method. Mater. Trans., JIM 37, 185 (1996).
21. W.L. Johnson: Fundamental aspects of bulk metallic glass formation in multicomponent alloys. Mater. Sci. Forum 225-227, 35 (1996).
22. 10 glassy alloy rod of 30 mm in diameter by a cap-cast technique. Mater. Trans. 48, 3190 (2007).
23. H. Ma, L.L. Shi, J. Xu, Y. Li, and E. Ma: Discovering inch-diameter metallic glasses in three-dimensional composition space. Appl. Phys. Lett. 87, 181915 (2005).
24. F. Guo, S.J. Poon, and G.J. Shiflet: Metallic glass ingots based on yttrium. Appl. Phys. Lett. 83, 1575 (2003).
25. Q.K. Jiang, G.Q. Zhang, L.Y. Chen, J.Z. Wu, H.G. Zhang, and J.Z. Jiang:, Glass formability, thermal stability and mechanical properties of La-based bulk metallic glasses. J. Alloy Compd. 424, 183 (2006).
26. R. Li, S.J. Pang, C.L. Ma, and T. Zhang: Influence of similar atom substitution on glass formation in (La-Ce)-Al-Co bulk metallic glasses. Acta Mater. 55, 3719 (2007).
27. D. Turnbull: Under what conditions can a glass be formed. Contemp. Phys. 10, 473 (1969).
28. Z.P. Lu and C.T. Liu: A new glass-forming ability criterion for bulk metallic glasses. Acta Mater. 50, 3501 (2002).
29. H. Tan, Y. Zhang, D. Ma, Y.P. Feng, and Y. Li: Optimum glass formation at off-eutectic composition and its relation to skewed eutectic coupled zone in the La based La-Al-(Cu,Ni) pseudo ternary system. Acta Mater. 51, 4551 (2603).
30. Y. Zhang, H. Tan, H.Z. Kong, B. Yao, and Y. Li: Glass-forming ability of Pr-(Cu,Ni)-Al alloys in eutectic system. J. Mater. Res. 18, 664 (2003).
31. Q.S. Zhang, W. Zhang, and A. Inoue: New Cu-Zr-based bulk metallic glasses with large diameters of up to 1.5 cm. Scripta Mater. 55, 711 (2006).
32. D.H. Xu, G. Duan, and W.L. Johnson: Unusual glass-forming ability of bulk amorphous alloys based on ordinary metal copper. Phys. Rew. Lett. 92, 245504 (2004).
33. A. Inoue: Stabilization of metallic supercooled liquid and bulk amorphous alloys. Acta Mater. 48, 279 (2000).
34. C.L. Qin, W. Zhang, Q.S. Zhang, K. Asam, and A. Inoue: Chemical characteristics of the passive surface films formed on newly developed Cu-Zr-Ag-Al bulk metallic glasses. J. Mater. Res. (in press).