Compatibility of chlorinated polyolefin with the components of thermoplastic polyolefin: A study by laser scanning confocal fluorescence microscopy

Macromolecules

Volumn 37, Issue 17, 2004, Pages 6544-6552

  Ma, Yuechun ^a   Farinha, J P S ^a,d   Winnik, Mitchell A ^a   Yaneff, Phillip V ^b   Ryntz, Rose A ^c  

^a UNIVERSITY OF TORONTO   (Canada)

^b E I du Pont Canada Company   (Canada)

^c VISTEON CORPORATION   (United States)

^d INSTITUTO SUPERIOR TÉCNICO   (Portugal)

Author keywords

[No Author keywords available]

Indexed keywords

FILM SURFACE; LASER SCANNING; THERMOPLASTIC POLYOLEFINS (TPO); VOLUME FRACTIONS;

ANNEALING; FLUORESCENCE; LASER APPLICATIONS; MICROSCOPIC EXAMINATION; SCANNING; SOLUBILITY; SYNTHESIS (CHEMICAL); THERMOPLASTICS; THICKNESS CONTROL;

POLYOLEFINS;

EID: 4444375577     PISSN: 00249297     EISSN: None     Source Type: Journal    
DOI: 10.1021/ma030381b     Document Type: Article

References (23)

1. Ryntz, R. A.; Prater, T. J.; Holubka, J. W. J. Coat. Technol. 1998, 68 (857), 83.
2. Ryntz, R. A.; Xie, Q.; Ramamurthy, A. C. J. Coat. Technol. 1995, 67 (843), 45.
3. Schmitz, P. J.; Holubka, J. W. J. Adhes. 1995, 48, 137.
4. Tomasetti, E.; Legras, R.; Henri-Mazeaud, B.; Nysten, B. Polymer 2000, 41, 6597.
5. Tomasetti, E.; Daoust, D.; Legras, R.; Bertrand, P.; Rouxhet, P. G. J. Adhes. Sci. Technol. 2001, 15, 13, 1589.
6. Tomasetti, E.; Vandorpe, S.; Daoust, D.; Boxus, T.; Marchand-Brynaert, J.; Poleunis, C.; Bertrand, P.; Legras, R.; Rouxhet, P. G. J. Adhes. Sci. Technol. 2001, 15, 1589.
7. Ryntz, R. A. J. Coat. Technol. 1991, 63 (799), 63.
8. Ryntz, R. A. Prog. Org. Coat. 1996, 27, 241.
9. Ryntz, R. A.; Buzdon, B. Prog. Org. Coat. 1997, 32, 167.
10. Ellis, T. S. Polym. Eng. Sci. 2001, 41, 2065.
11. Morris, H. R.; Munroe, B.; Ryntz, R. A.; Treado, P. J. Langmuir 1998, 14, 2426.
12. Morris, H. R.; Turner, J. F.; Munro, B.; Ryntz, R. A.; Treado, P. J. Langmuir 1999, 15, 2961.
13. Raphael, E.; de Gennes, P. G. J. Phys. Chem. 1992, 96, 4002.
14. Li, L.; Chen, L.; Bruin, P.; Winnik, M. A. J. Polym. Sci., Part B: Polym. Phys. 1997, 35, 979.
15. Tong, J.; Moffitt, M.; Huang, X.; Winnik, M. A.; Ryntz, R. A. J. Polym. Sci., Part A: Polym. Chem. 2001, 39, 239.
16. Li, L.; Sosnowski, S.; Kumacheva, E.; Winnik, M. A.; Rajaram, S.; Balke, S. T.; Chaffey, C. E. Langmuir 1996, 12, 2141.
17. Li, L.; Sosnowski, S.; Chaffey, C. E.; Balke, S. T.; Winnik, M. A. Langmuir 1994, 10, 2495.
18. (a) Moffitt, M.; Winnik, M. A. J. Polym. Sci. Technol. 2000, 11, 779.
19. (b) Moffitt, M.; Rharbi, Y.; Li, H.; Chen, W.; Tong, J.; Winnik, M. A.; Thurman, D. K.; Oberhauser, J. P.; Kornfield, J. A.; Ryntz, R. A. J. Polym. Sci., Part B: Polym. Phys. 2002, 40, 2842.
20. Sclavons, M.; Carlier, V.; De Roover, B.; Franquinet, P.; Devaux, J.; Legras, R. J. Appl. Polym. Sci. 1996, 62, 1205.
21. Our CPO sample is stable to heating at 180 °C. GPC measurements on the original CPO sample and on the 95/5 CPO/CPO-HY blend baked at 180 °C in a vacuum oven for 300 min show no significant difference in molecular weight and molecular weight distribution. There is ca. 8% weight loss, which appears to be accompanied by interchain anhydride formation. Annealed CPO samples have poor solubility in THF but become completely soluble when a few drops of water are added to the THF.
22. Moffitt, M.; Rharbi, Y.; Li, H.; Winnik, M. A. Macromolecules 2002, 35, 3321.
23. Russ, J. C. Practical Stereology; Plenum Press: New York, 1986.