Studies of new YDy-based R2Fe14B magnets for high temperature performance (R = Y + Dy + Nd)

IEEE Transactions on Magnetics

Volumn 40, Issue 4 II, 2004, Pages 2907-2909

  Tang, W ^a   Dennis, K W ^a   Wu, Y Q ^a   Kramer, M J ^a   Anderson, I E ^a   McCallum, R W ^a  

^a IOWA STATE UNIVERSITY   (United States)

Author keywords

Magnetocrystalline anisotropy; Melting spinning; Permanent magnets; Rare earth materials and compounds

Indexed keywords

ANNEALING; COERCIVE FORCE; DIFFERENTIAL THERMAL ANALYSIS; GRAIN BOUNDARIES; GRAIN SIZE AND SHAPE; HIGH TEMPERATURE PROPERTIES; MAGNETIC PROPERTIES; MAGNETIZATION; MAGNETOMETERS; MICROSTRUCTURE; NEODYMIUM; PERMANENT MAGNETS; TRANSMISSION ELECTRON MICROSCOPY; X RAY ANALYSIS; X RAY DIFFRACTION; YTTRIUM COMPOUNDS;

MAGNETOCRYSTALLINE ANISOTROPY; MELTING SPINNING; RARE EARTH MATERIALS AND COMPOUNDS; VIBRATING SAMPLE MAGNETOMETER (VSM);

MAGNETS;

EID: 4444301950     PISSN: 00189464     EISSN: None     Source Type: Journal    
DOI: 10.1109/TMAG.2004.829014     Document Type: Article

References (6)

1. 14B materials: Intrinsic properties and technological aspects," Rev. Mod. Phys., vol. 63, pp. 819-897, 1991.
2. xB compounds," J. Less-Common Met., vol. 124, pp. 165-172, 1986.
3. 14B measured on single crystals," J. Appl. Phys., vol. 59, pp. 873-879, 1986.
4. 14B systems prepared with high purity rare earths," J. Appl. Phys., vol. 57, pp. 4106-4108, 1985.
5. 14B," Solid State Commun., vol. 50, pp. 497-499, 1984.
6. 14B," Solid State Commun., vol. 55, pp. 295-298, 1985.